Wire drawing belt, method for manufacturing metallic glass plate by using wire drawing belt and metallic glass plate

A metal color and glass plate technology, applied in the direction of coating, etc., can solve the problems of easy separation of surface layer and base glass, difficulty in meeting market demand, dark or bright, etc., to solve the problem of light pollution, avoid resin cracking, weaken high The effect of brightness

Inactive Publication Date: 2019-03-22
JIANGSU XIUQIANG GLASSWORK CO LTD
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, surface treatment is generally carried out by physical methods such as wire drawing, sanding, and sanding. However, the above-mentioned conventional methods are often difficult to meet the market demand, and the color is dark or bright, and the surface texture after physical treatment cannot be fully displayed. Light pollution, Problems such as easy separation of surface layer and base glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Select non-woven fabric, use glue to bond aluminum oxide or silicon carbide on its surface, dry to obtain the wire drawing tape with abrasive grain size ranging from 50-600 mesh for use.

[0039] Select transparent glass with a thickness of 2mm as the glass substrate; use the abrasive as alumina and a particle size of 400 mesh drawing tape to draw filaments on the surface of the glass substrate, and the length of the filament is controlled to be greater than 5mm; then use the abrasive as alumina, particle size For the 300-mesh drawing tape, the side of the drawn filament is shredded, and the length of the shredded wire is controlled to be less than or equal to 5mm to obtain a wire-drawing layer; in the process of drawing, a frequency conversion device is used to control the drawing belt to ensure the length of the filament and shredded wire Be diverse.

[0040] The large glass plate obtained above is cut and edged, and then screen-printed on the surface of the wire-draw...

Embodiment 2

[0044] Select non-woven fabric, glue aluminum oxide or silicon carbide on its surface, dry it to obtain wire drawing tape with abrasive particle size ranging from 50-600 mesh, and make the wire drawing ring belt into a wire drawing ring for later use.

[0045] Select transparent glass with a thickness of 6mm as the glass substrate; use the abrasive material as silicon carbide and a wire drawing ring belt with a particle size of 50 mesh to draw filaments on the surface of the glass substrate, and the length of the filaments is controlled to be greater than 5mm; then use the abrasives as silicon carbide, particle size The wire-drawing ring belt with a diameter of 600 meshes is used to pull and shred the side that has passed through the long wire. The length of the shredded wire is controlled to be less than or equal to 5mm to obtain the wire-drawing layer; The length of the wire is diversified.

[0046] The large glass plate obtained above is cut and edged, and then screen-print...

Embodiment 3

[0048] Select non-woven fabric, glue aluminum oxide or silicon carbide on its surface, dry it to obtain wire drawing tape with abrasive particle size ranging from 50-600 mesh, and make the wire drawing ring belt into a wire drawing ring for later use.

[0049] Select a transparent glass with a thickness of 4.5mm as the glass substrate; use the abrasive as silicon carbide and the wire drawing ring belt with a particle size of 200 mesh to draw filaments on the surface of the glass substrate, and the length of the filaments is controlled to be greater than 5mm; then use the abrasives to be alumina, The wire-drawing ring belt with a particle size of 450 mesh is used to pull and shred the side of the drawn filament. The length of the shredded wire is controlled to be less than or equal to 5mm to obtain a wire-drawing layer; during the wire-drawing process, a frequency conversion device is used to control the wire-drawing ring belt to ensure that the filament and The length of shredd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a wire drawing belt, a method for manufacturing a metallic glass plate by using the wire drawing belt and the metallic glass plate. The wire drawing belt comprises a substrate material and an abrasive material; the substrate material is a non-woven fabric, the abrasive material is aluminium oxide or silicon carbide, and the grain size of the abrasive material is 50-600 meshes; and the abrasive material adheres to the substrate material. The method for manufacturing the metallic glass plate by using the wire drawing belt comprises the following steps: selecting transparent glass as a glass substrate; successively drawing long wires and broken wires on the surface of the glass substrate by using the wire drawing belt to obtain a wire drawing layer; printing brighteninggloss oil resin on the surface of the precisely treated wire drawing layer, and then sintering to obtain a wire drawing brightening layer; and printing protecting coloring resin on the surface of thewire drawing brightening layer, and then sintering to obtain the metallic glass plate. The metallic glass plate is manufactured by the method. The wire drawing belt and the metallic glass plate obtained by the method for manufacturing the metallic glass plate are suitable in color and good in surface wire drawing effect, and are attractive.

Description

technical field [0001] The invention relates to the field of glass processing, in particular to a drawing ribbon and a method for manufacturing a metallic glass plate using the same, as well as the metallic glass plate. Background technique [0002] Due to its advantages of easy cleaning, aging resistance, and high metal-like appearance, metallic glass is more and more widely used in various industries, especially in the field of home appliances. For a long time, people often pay attention to the improvement of the physical properties of metallic glass, such as strength, hardness, adhesion between surface materials and base glass, etc., but with the improvement of people's living standards, the requirements for the appearance of metallic glass Also getting higher and higher. [0003] In the prior art, surface treatment is generally carried out by physical methods such as wire drawing, sanding, and sanding. However, the above-mentioned conventional methods are often difficul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C19/00C03C17/42
CPCC03C17/42C03C19/00C03C2217/72C03C2218/32
Inventor 张新利赵庆忠陆瑾刘红利侍孝飞
Owner JIANGSU XIUQIANG GLASSWORK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com