Soft magnetic ferrite material for charging pile

A technology of soft magnetic ferrite and charging piles, applied in the direction of magnetic materials, magnetic objects, inorganic materials, etc., can solve the problems of poor formability and stability, and achieve improved dielectric coefficient, good resistivity, and low core loss Effect

Active Publication Date: 2019-03-22
ANHUI HUALIN MAGNETIC TECH
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of the electronics industry and the expansion of application fields, the requirements for magnetic materials are getting higher and higher, and the classification requirements for material properties are more detailed and specialized. The formability and stability are poor, and the resistivity and dielectric coefficient need to be improved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of soft magnetic ferrite material for charging pile, its raw material comprises main material and auxiliary material; The molecular formula of described main material material is Mn x Zn y Fe z o 4 ; The auxiliary material includes Nb 2 o 5 , V 2 o 5 、Co 3 o 4 , CaCO 3 、Cr 2 o 3 ,P 2 o 5 ;

[0024] Wherein, in the molecular formula of the main material, x=0.9, y=0.6, z=2.5; based on the total mass of raw materials, the auxiliary materials include: 0.1wt% Nb 2 o 5 , 0.01wt% V 2 o 5 , 1.5wt% Co 3 o 4 , 0.02wt% CaCO 3 , 0.1wt% Cr 2 o 3 , 0.05wt% P 2 o 5 ;

[0025] The preparation method of the soft ferrite material for the charging pile comprises the following steps:

[0026] S1. Mix the main ingredients, add grinding balls and water, and mill for 4 hours. The weight ratio of main ingredients: grinding balls: water is 1:2.6:1, and prefabricated material A is obtained;

[0027] S2. Dry the prefabricated material A at 105°C for 2 hours, and t...

Embodiment 2

[0030] A kind of soft magnetic ferrite material for charging pile, its raw material comprises main material and auxiliary material; The molecular formula of described main material material is Mn x Zn y Fe z o 4 ; The auxiliary material includes Nb 2 o 5 , V 2 o 5 、Co 3 o 4 , CaCO 3 、Cr 2 o 3 ,P 2 o 5 ;

[0031] Wherein, in the molecular formula of the main material, x=0.6, y=0.9, z=2.5; based on the total mass of raw materials, the auxiliary materials include: 0.01wt% Nb 2 o 5 , 0.1wt% V 2 o 5 , 0.1wt% Co 3 o 4 , 0.2wt% CaCO 3 , 0.01wt% Cr 2 o 3 , 0.15wt% P 2 o 5 ;

[0032] The preparation method of the soft ferrite material for the charging pile comprises the following steps:

[0033] S1. Mix the main ingredients, add grinding balls and water, and mill for 2 hours. The weight ratio of main ingredients: grinding balls: water is 1:3.5:0.5 to obtain prefabricated material A;

[0034] S2. Dry the prefabricated material A at 120°C for 1 hour, and then pr...

Embodiment 3

[0037] A kind of soft magnetic ferrite material for charging pile, its raw material comprises main material and auxiliary material; The molecular formula of described main material material is Mn x Zn y Fe z o 4 ; The auxiliary material includes Nb 2 o 5 , V 2 o 5 、Co 3 o 4 , CaCO 3 、Cr 2 o 3 ,P 2 o 5 ;

[0038] Wherein, in the molecular formula of the main material, x=0.6, y=0.6, z=2.8; based on the total mass of raw materials, the auxiliary materials include: 0.07wt% Nb 2 o 5 , 0.02wt% V 2 o 5 , 1.2wt% Co 3 o 4 , 0.08wt% CaCO 3 , 0.06wt% Cr 2 o 3 , 0.08wt% P 2 o 5 ;

[0039] The preparation method of the soft ferrite material for the charging pile comprises the following steps:

[0040] S1. Mix the main ingredients, add grinding balls and water, and mill for 3 hours. The weight ratio of main ingredients: grinding balls: water is 1:3.5:1 to obtain prefabricated material A;

[0041] S2. Dry the prefabricated material A at 115°C for 1 hour, and then pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a soft magnetic ferrite material for a charging pile. The raw materials comprise a main material and auxiliary materials; the molecular formula of the main material is MnxZnyFezO4; and the auxiliary materials comprise Nb2O5, V2O5, Co3O4, CaCO3, Cr2O3, P2O5. The resistivity and the dielectric coefficient of the manganese zinc ferrite material are significantly improved, so that the soft magnetic ferrite material has high electromagnetic characteristic.

Description

technical field [0001] The invention relates to the technical field of magnetic materials, in particular to a soft ferrite material for charging piles. Background technique [0002] The application of soft magnetic materials in industry began at the end of the 19th century, with the rise of electric power and telecommunication technology, and its application range is extremely wide. Soft magnetic materials are not only used in the fields of home appliances, information technology, automobiles and other supporting fields, but more importantly, soft magnetic materials, as the main raw materials for the production of electronic components, have brought a steady stream of demand for them. With the development of the electronics industry and the expansion of application fields, the requirements for magnetic materials are getting higher and higher, and the classification requirements for material properties are more detailed and specialized. The formability and stability are poor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/38C04B35/622H01F1/34
CPCC04B35/265C04B35/622C04B2235/3208C04B2235/3239C04B2235/3241C04B2235/3251C04B2235/3262C04B2235/3277C04B2235/3284C04B2235/34H01F1/342
Inventor 沈宏江蔡忠贤张学舟牟大兵
Owner ANHUI HUALIN MAGNETIC TECH