Low-cost high-CTI high-GWIT flame-retardant reinforced PBT composite material and preparation method thereof

A composite material and low-cost technology, applied in the field of PBT plastic modification, can solve the problems of difficult processing technology, high cost of halogen-free flame retardants, poor mechanical properties of materials, etc., achieve environmental pollution, improve CTI and GWIT, mold little corrosion effect

Inactive Publication Date: 2019-03-29
JINYOUNG XIAMEN ADVANCED MATERIALS TECH CO LTD
View PDF14 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] To sum up, the main problems of the current halogen-free flame retardant reinforced PBT materials are: (1) the cost of halogen-free flame retardants is expensive; (2) it is difficult to meet the two harsh conditions of high CTI and high GWIT at the same time, and the material Poor mechanical properties; (3) difficult processing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-cost high-CTI high-GWIT flame-retardant reinforced PBT composite material and preparation method thereof
  • Low-cost high-CTI high-GWIT flame-retardant reinforced PBT composite material and preparation method thereof
  • Low-cost high-CTI high-GWIT flame-retardant reinforced PBT composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention more clear, the following will be clearly and completely described in conjunction with the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are part of the embodiments of the present invention, rather than Full examples. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0035] The present invention also provides the embodiment shown in the following table:

[0036] Table 1

[0037]

[0038]

[0039] Specifically, according to the formulas of examples and comparative examples in the above table, the present invention also provides the following schemes for preparing examples:

[0040] Step a, bake the PBT resin at 120°C for 2-4 hours, and contr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of PBT plastic modification, in particular to a low-cost high-CTI high-GWIT flame-retardant reinforced PBT composite material and a preparation method thereof. The composite material includes, by weight, 40-52 parts of PBT resin, 14-25 parts of a halogen-free composite flame retardant, 25-30 parts of glass fibers, 1-5 parts of a toughening agent, 0.1-0.5 part of an antioxidant and 0.5-1 part of other processing aids. The halogen-free composite flame retardant is prepared by compounding a metal phosphate flame retardant, an organic phosphate flame retardant and an inorganic flame retardant. The halogen-free flame-retardant reinforced PBT engineering material has good mechanical properties and flame-retardant properties, high CTI (600V) and high GWIT (with the initiation temperature of glowing filament being 800 DEG C, without combustion during the whole process), and is environmentally friendly, and good in processing performance. In particular, the halogen-free composite flame retardant is low in cost, has a price 40-50% lower than the price of similar imported flame retardants, and has great market competitiveness.

Description

technical field [0001] The invention relates to the technical field of PBT plastic modification, in particular to a low-cost, high-CTI, high-GWIT flame-retardant reinforced PBT composite material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) is a crystalline thermoplastic polyester. It has the advantages of high temperature resistance, weather resistance, chemical resistance, good electrical insulation, low water absorption, high dimensional stability, and good processability. It is an engineering plastic with excellent comprehensive properties and is widely used in electronics, electrical, Automotive, household appliances and other industries. [0003] With the development of science and technology and the gradual improvement of people's living standards, home intelligence will gradually be realized, and unattended electrical equipment will gradually become popular. put forward higher requirements. The traditional PBT en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L23/08C08K13/04C08K7/14C08K5/3492C08K3/22C08K3/32C08J5/04
CPCC08J5/043C08J2367/02C08J2423/08C08K3/32C08K5/34928C08K7/14C08K13/04C08K2003/2224
Inventor 黄志洪
Owner JINYOUNG XIAMEN ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap