Seat polyurethane foam material with high flame retardation, low volatility and small compressive residual variable, and preparation method and application thereof

A residual variable and foaming material technology, applied in the field of polyurethane foaming materials, can solve problems such as inability to manufacture satisfactory products, and achieve the effects of high loop repeat consistency, consistent and stable production products, and accurate delivery ratios

Inactive Publication Date: 2019-03-29
沈阳金杯李尔汽车座椅有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] High-speed rail has high requirements on flame retardancy, VOC and physical properties at the same time, and many manufacturers cannot manufacture products that meet the requirements of this standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seat polyurethane foam material with high flame retardation, low volatility and small compressive residual variable, and preparation method and application thereof
  • Seat polyurethane foam material with high flame retardation, low volatility and small compressive residual variable, and preparation method and application thereof
  • Seat polyurethane foam material with high flame retardation, low volatility and small compressive residual variable, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Example 1 Seat polyurethane foam material with high flame retardancy, low volatility and small compression residual variable

[0050] (1) comprising the following components by weight:

[0051] 50 parts of polyether polyol PPG, 50 parts of polymer polyol POP, 3 parts of distilled water, 1 part of crosslinking agent, 0.5 parts of gel catalyst, 0.17 parts of foaming catalyst, and 0.75 parts of surface stabilizer.

[0052] The above materials are specifically:

[0053] The model of polyether polyol PPG is: purchased from Juyuan Chemical (full name: Jilin Juyuan Chemical Co., Ltd.), the model is F-3531; its specific parameters are that the hydroxyl value is 33.5~36.5mgKOH / g, and the viscosity is 800~ 1000mPa·s.

[0054] The model of the polymer polyol POP is: purchased from Jiangyin Youbang (full name: Jiangyin Youbang Chemical Co., Ltd.), the model is 8033; its specific parameters are the hydroxyl value of 27.5-30.5mgKOH / g, and the viscosity of 2000-1000mPa·s.

[0055] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
viscosityaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a seat polyurethane foam material with high flame retardation, low volatility and small compressive residual variable. The seat polyurethane foam material comprises, by weight,40-60 parts of polyether polyol (PPG), 40-60 parts of polymer polyol (POP), 2.5-3.5 parts of distilled water, 0.8-1.2 parts of a cross-linking agent, 0.4-0.6 part of a gel catalyst, 0.15-0.19 part ofa foaming catalyst and 0.65-0.85 part of a surface stabilizer. The seat polyurethane foam material has the advantages of high flame retardation performance, high safety, low volatile matter content,environmental protection, high rebound rate, comfortableness, small compressive residual variable, good durability, short production cycle and high yield.

Description

technical field [0001] The invention relates to the field of polyurethane foam materials, in particular to a seat polyurethane foam material with high flame retardancy, low volatility and small compression residual variable, its preparation method and application. Background technique [0002] At present, China's high flame-retardant seat foam raw materials are made of ordinary flame-retardant polyether polyols, plus ordinary halogen flame retardants, or phosphorus-containing flame retardants, or melamine, or antimony trioxide. No matter what kind of flame retardant additives will cause other physical properties to be reduced, the effect of environmental protection, comfort and durability cannot be achieved, and the oxygen index can reach 28.5% at most. At present, the performance requirements of the seat foaming of the northern high-speed rail are as shown in Table 1: [0003] Table 1. Physical property requirements of polyurethane foam [0004] [0005] 2. The combust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L83/04C08J9/08C08G18/48C08G18/32C08G18/66C08G18/79C08G18/76
CPCC08G18/3275C08G18/48C08G18/6688C08G18/7607C08G18/7614C08G18/7671C08G18/794C08J9/0061C08J9/08C08J2203/02C08J2375/08C08J2483/04C08G2110/005C08G2110/0083
Inventor 王淞民陈芷逍曹鹏
Owner 沈阳金杯李尔汽车座椅有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com