Simulation ceramic tile and preparation method thereof

A ceramic tile and simulation technology, which is applied in the production of clay products, other household utensils, ceramic materials, etc., can solve the problems of low fidelity, achieve high texture matching, improve three-dimensionality and simulation, and increase fidelity.

Active Publication Date: 2019-04-16
FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Based on the problem of low fidelity existing in ceramics, the present invention intends to provide a simulated ceramic tile and its preparation method, aiming at improving the fidelity and three-dimensional effect of ceramic tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Simulation ceramic tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A simulation ceramic tile, wherein the ceramic tile is composed of a clay layer, a powder layer, a bottom glaze layer, and a top glaze layer in order from bottom to top, the bottom glaze layer includes penetrating ink, and the maximum depth of penetration of the ink is the bottom glaze The layer thickness and penetration width are consistent with the cross-sectional texture boundary of the blank. The mud includes the following components by weight: basic powder + 0.3% zirconia, wherein the basic powder is proportioned according to the following components: black Mud 20%, high alumina particles 3%, Longchuan stone powder 17%, Qingyuan stone particles 8%, raw talc 5%, bentonite 14%, potassium sodium sandstone 22%, water reducing agent 0.4%; It includes the following components by weight: base powder + 4% copper oxide; the primer includes 8% acrylic resin, 60% SiO2, Al3O2 10%, Fe2O3 0.05%, K2O1.5%, Na2O 2%, MgO 2 %;

[0039] The preparation method of the ceramic tile include...

Embodiment 2

[0053] A simulation ceramic tile, which is composed of a clay layer, a powder layer, a bottom glaze layer, and a top glaze layer in order from bottom to top, the bottom glaze layer includes penetrating ink, and the maximum depth of penetration of the ink is the bottom glaze The layer thickness and penetration width are consistent with the cross-sectional texture boundary of the blank. The mud includes the following components by weight: basic powder + 0.5% zirconia, wherein the basic powder is proportioned according to the following components: black 22% mud, 3% high alumina particles, 21% Longchuan stone powder, 9% Qingyuan stone particles, 5% raw talc, 14% bentonite, 18% potassium sodium sandstone, 0.6% water reducing agent; The weight includes the following components: base powder + 5% iron oxide; the thickness of the primer is 1.5mm, and the primer includes polyvinyl acetal 10%, SiO262%, Al3O215%, Fe2O30.07%, K2O 3.5%, Na2O3%, MgO 4%;

[0054] The preparation method of the c...

Embodiment 3

[0071] A simulation ceramic tile, which is composed of a clay layer, a powder layer, a bottom glaze layer, and a top glaze layer in order from bottom to top, the bottom glaze layer includes penetrating ink, and the maximum depth of penetration of the ink is the bottom glaze The layer thickness and penetration width coincide with the texture boundary of the blank cross section. The mud includes the following components by weight: basic powder + 0.4% zirconia, wherein the basic powder is proportioned according to the following components: black Mud 19.2%, high alumina particles 2.6%, Longchuan stone powder 18%, Qingyuan stone particles 7%, raw talc 3%, bentonite 16%, potassium sodium sand stone 29%, water reducing agent 0.4%; It includes the following components by weight: basic powder + 4.3% zinc oxide; the primer includes epoxy resin 14%, SiO2 65%, Al3O2 15%, Fe2O3 0.1%, K2O 1.5%, Na2O 2%, MgO 2 %;

[0072] The preparation method of the ceramic tile includes the following steps:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
porosityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a simulation ceramic tile and a preparation method thereof. The ceramic tile comprises a blank layer, a bottom glaze layer and a surface glaze layer, wherein the bottom glaze layer comprises penetrating ink; the maximum penetrating depth of the ink is the thickness of the bottom glaze layer; the penetrating width is fit with a grain boundary of a cross section, the blank layer comprises at least one pug layer and at least one powder layer, the most bottom layer of the ceramic tile is the pug layer, and at least one surface of the powder layer is in contact with the pug layer. Meanwhile, the preparation process of the ceramic tile is also provided, the penetrating depth and width of the ink pigment can be effectively controlled by optimizing and adjusting the ingredients, the process steps and the parameters, the grain fit degree between the bland body and the longitudinal section of the bottom glaze is high, the stereoscopic impression and simulation degree of the ceramic tile are greatly improved, meanwhile, due to the unique sintering process control, the bland body layer does not have a mutual penetration layer, thereby further improving the stereoscopic impression and simulation degree of the ceramic tile.

Description

Technical field [0001] The invention relates to a ceramic tile and a preparation method thereof, in particular to an artificial ceramic tile and a preparation method thereof. Background technique [0002] Natural marble has always been a popular stone decoration material because of its noble and elegant appearance. However, as a non-renewable resource, the cost of mining and production of natural marble is getting higher and higher. In order to meet people's increasing demand for natural marble, the production cost is reasonably controlled. At present, there are more and more artificial marbles on the market. However, due to poor technology, the artificial marble prepared by the artificial marble is not ideal in simulation and three-dimensional effect, which greatly affects the fidelity of the marble. [0003] The Chinese invention patent with the patent application number CN201810587557.8 is a method for manufacturing ceramic tiles with three-dimensional decorative effect, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/132C04B33/13C04B33/04C03C8/00C04B41/89
CPCC03C8/00C04B33/04C04B33/13C04B33/1321C04B33/16C04B41/5022C04B41/89C04B2235/6567Y02P40/60
Inventor 林伟范新晖廖花妹吴则昌林金宏
Owner FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com