A kind of simulation ceramic tile and preparation method thereof

A ceramic tile and simulation technology, which is applied in the production of clay products, other household utensils, ceramic materials, etc., can solve the problems of low fidelity, achieve high texture matching, easier control of texture path and width, and improve three-dimensionality and simulation degree of effect

Active Publication Date: 2022-03-15
FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Based on the problem of low fidelity existing in ceramics, the present invention intends to provide a simulated ceramic tile and its preparation method, aiming at improving the fidelity and three-dimensional effect of ceramic tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of simulation ceramic tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038]A simulated ceramic tile, the ceramic tile is a mud layer, a powder layer, a bottom glaze layer, and a surface glaze layer from bottom to top, and the bottom glaze layer includes penetrating ink, and the maximum depth of the ink penetration is the bottom glaze layer. The thickness of the layer and the width of penetration coincide with the texture boundary of the cross section of the billet. The mud material includes the following components by weight: base powder + 0.3% zirconia, wherein the base powder is proportioned according to the following components: black 20% clay, 3% high alumina stone, 17% Longchuan stone powder, 8% Qingyuan stone, 5% raw talc, 14% bentonite, 22% potassium sodium sandstone, 0.4% water reducing agent; It includes the following components by weight: basic powder + 4% copper oxide; the primer includes acrylic resin 8%, SiO2 60%, Al2O3 10%, Fe2O3 0.05%, K2O 1.5%, Na2O 2%, MgO 2 %;

[0039] The preparation method of described ceramic tile comprise...

Embodiment 2

[0053] A simulated ceramic tile, the ceramic tile is a mud layer, a powder layer, a bottom glaze layer, and a surface glaze layer from bottom to top, and the bottom glaze layer includes penetrating ink, and the maximum depth of the ink penetration is the bottom glaze layer. The thickness of the layer and the width of penetration coincide with the texture boundary of the cross section of the billet. The mud material includes the following components by weight: base powder + 0.5% zirconia, wherein the base powder is proportioned according to the following components: black 22% clay, 3% high alumina stone, 21% Longchuan stone powder, 9% Qingyuan stone, 5% raw talc, 14% bentonite, 18% potassium sodium sandstone, 0.6% water reducing agent; It includes the following components by weight: basic powder + 5% iron oxide; the thickness of the bottom glaze is 1.5mm, and the bottom glaze includes polyvinyl acetal 10%, SiO262%, Al2O315%, Fe2O30.07%, K2O 3.5%, Na2O3%, MgO 4%;

[0054] The p...

Embodiment 3

[0071] A simulated ceramic tile, the ceramic tile is a mud layer, a powder layer, a bottom glaze layer, and a surface glaze layer from bottom to top, and the bottom glaze layer includes penetrating ink, and the maximum depth of the ink penetration is the bottom glaze layer. The thickness of the layer and the width of penetration coincide with the texture boundary of the cross section of the billet. The mud material includes the following components by weight: base powder + 0.4% zirconia, wherein the base powder is proportioned according to the following components: black 19.2% clay, 2.6% high alumina stone, 18% Longchuan stone powder, 7% Qingyuan stone, 3% raw talc, 16% bentonite, 29% potassium sodium sandstone, 0.4% water reducing agent; It includes the following components by weight: basic powder + 4.3% zinc oxide; the primer includes epoxy resin 14%, SiO2 65%, Al2O3 15%, Fe2O3 0.1%, K2O 1.5%, Na2O 2%, MgO 2 %;

[0072] The preparation method of described ceramic tile compr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
porosityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a simulated tile and a preparation method thereof. The tile includes a blank layer, an underglaze layer and a surface glaze layer, the underglaze layer includes penetrating ink, and the maximum depth of ink penetration is the thickness of the underglaze layer , the penetration width coincides with the grain boundary of the blank cross section, the blank layer includes at least one mud layer and at least one powder layer, the bottom layer of the ceramic tile is a mud layer, at least one side of the powder layer is connected with the mud layer touch. At the same time, it also provides the preparation process of the ceramic tile. Through the optimization and adjustment of ingredients, process steps and parameters, the depth and width of ink pigment penetration can be effectively controlled, so that the texture of the green body and the bottom glaze on the longitudinal section is highly consistent, which greatly improves the ceramic tile. At the same time, due to the unique sintering process control, there is no interpenetration layer in the green body layer, which further improves the three-dimensional effect and simulation degree of the tiles.

Description

technical field [0001] The invention relates to a tile and a preparation method thereof, in particular to a simulated tile and a preparation method thereof. Background technique [0002] Natural marble has always been sought after by people as a stone decoration material because of its noble and elegant appearance. However, as a non-renewable resource, natural marble has higher and higher mining and production costs. In order to meet people's growing demand for natural marble and reasonably control production costs , There are more and more artificial marbles on the market. However, due to poor technology, the imitation degree and three-dimensional effect of the prepared artificial marble are not ideal, which greatly affects the fidelity of the marble. [0003] The Chinese invention patent with the patent application number CN201810587557.8 is a method for manufacturing ceramic tiles with a three-dimensional decorative effect, which includes the following steps: A. Burning ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/16C04B33/132C04B33/13C04B33/04C03C8/00C04B41/89
CPCC03C8/00C04B33/04C04B33/13C04B33/1321C04B33/16C04B41/5022C04B41/89C04B2235/6567Y02P40/60
Inventor 林伟范新晖廖花妹吴则昌林金宏
Owner FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products