Amorphous alloy with favorable toughness and preparation method thereof

An amorphous alloy and toughness technology, applied in the field of amorphous alloy and its preparation, can solve the problems of brittle fracture, transformer breakdown, high brittleness, and achieve high saturation magnetic induction intensity, optimized annealing process, and good toughness.

Active Publication Date: 2019-05-21
安徽智磁新材料科技有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, iron-based amorphous alloys lack the ability to deform macroscopically at room temperature, are highly brittle, and are prone to brittle fracture, which affects their engineering applications as structural materials. Lead to unfavorable phenomena such as incomplete magnetic circuit and transformer breakdown

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amorphous alloy with favorable toughness and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0019] (1) Put the raw materials into the smelting furnace according to the mass ratio shown in Table 1, add the purifying agent after melting, stand still for several times to remove slag, and finally make the components in the alloy mother liquor evenly distributed, and the respective contents of Al, O, and N are between Below 10ppm; the purifying agent is composed of 55% silicon dioxide, 35% calcium oxide, and 10% iron scale;

[0020] (2) Import the alloy mother liquid in the smelting furnace into the tundish, seal the nozzle with a stopper rod, and let it stand for about 30 minutes to make the temperature of the mother liquid even;

[0021] (3) Then lift the plug rod, the mother liquor enters the nozzle bag, and shoots through the nozzle onto the high-speed rotating cooling roller (using water-cooled copper roller), so that the alloy mother liquor 6 ~10 7 Cooling and forming at a speed of ℃ / sec to obtain an amorphous alloy strip, in which the spray casting pressure is abo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fracture strainaaaaaaaaaa
Login to View More

Abstract

The invention provides an amorphous alloy with favorable toughness and a preparation method thereof, and belongs to the technical field of magnetic material preparation. The amorphous alloy is prepared from the following element components in percentage by mass: 2.5 to 7.5 percent of Ni, 8.2 to 10.5 percent of Si, 1.5 to 3.8 percent of B, 1.0 to 1.7 percent of Mn, 1.3 to 2.0 percent of Sn, and thebalance Fe. Through optimizing the alloy element components and the matching ratio and adopting an annealing process, the amorphous alloy product with an excellent soft magnetic performance and favorable toughness is obtained.

Description

technical field [0001] The invention relates to the technical field of magnetic material preparation, in particular to an amorphous alloy with good toughness and a preparation method thereof. Background technique [0002] Iron-based amorphous alloy is a new type of material developed in the 1960s. Compared with traditional steel, it has an atomic structure with long-range disorder and short-range order in structure, without defects such as grain boundaries and dislocations; in terms of chemical composition, element distribution Uniform, no segregation and other phenomena; with high saturation magnetic induction, low coercive force, low loss and other excellent properties, it is widely used in transformers, motors, reactors, transformers, mutual induction coils and other fields. However, iron-based amorphous alloys lack the ability to deform macroscopically at room temperature, are highly brittle, and are prone to brittle fracture, which affects their engineering applications...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C45/02C21D1/26C21D6/00C22C33/04H01F1/153
Inventor 邓毕力罗顶飞冯英杰晋立丛
Owner 安徽智磁新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com