Amorphous alloy with good toughness and preparation method thereof

A technology of amorphous alloy and toughness, applied in the field of amorphous alloy and its preparation, can solve problems such as brittle fracture, lack of macroscopic room temperature plastic deformation ability of iron-based amorphous alloy, and transformer breakdown

Active Publication Date: 2020-04-17
安徽智磁新材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, iron-based amorphous alloys lack the ability to deform macroscopically at room temperature, are highly brittle, and are prone to brittle fracture, which affects their engineering applications as structural materials. Lead to unfavorable phenomena such as incomplete magnetic circuit and transformer breakdown

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amorphous alloy with good toughness and preparation method thereof
  • Amorphous alloy with good toughness and preparation method thereof
  • Amorphous alloy with good toughness and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0017] (1) Put the raw materials into the smelting furnace according to the mass ratio shown in Table 1, add the purifying agent after melting, stand still for several times to remove slag, and finally make the components in the alloy mother liquor evenly distributed, and the respective contents of Al, O, and N are between Below 10ppm; the purifying agent is composed of 55% silicon dioxide, 35% calcium oxide, and 10% iron scale;

[0018] (2) Import the alloy mother liquid in the smelting furnace into the tundish, seal the nozzle with a stopper rod, and let it stand for about 30 minutes to make the temperature of the mother liquid even;

[0019] (3) Then lift the plug rod, the mother liquor enters the nozzle bag, and shoots through the nozzle onto the high-speed rotating cooling roller (using water-cooled copper roller), so that the alloy mother liquor 6 ~10 7 Cooling and forming at a speed of ℃ / sec to obtain an amorphous alloy strip, in which the spray casting pressure is abo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fracture strainaaaaaaaaaa
Login to View More

Abstract

The invention provides an amorphous alloy with good toughness and a preparation method thereof, belonging to the technical field of magnetic material preparation. The amorphous alloy is composed of the following elements by mass percentage: Ni: 2.5-7.5%; Si: 8.2-10.5%; B: 1.5-3.8%; Mn: 1.0-1.7%; Sn: 1.3-2.0%; The amount is Fe. The present invention is an amorphous alloy product with excellent soft magnetic properties and good toughness by optimizing alloy element composition and proportion and annealing process.

Description

technical field [0001] The invention relates to the technical field of magnetic material preparation, in particular to an amorphous alloy with good toughness and a preparation method thereof. Background technique [0002] Iron-based amorphous alloy is a new type of material developed in the 1960s. Compared with traditional steel, it has an atomic structure with long-range disorder and short-range order in structure, without defects such as grain boundaries and dislocations; in terms of chemical composition, element distribution Uniform, no segregation and other phenomena; with high saturation magnetic induction, low coercive force, low loss and other excellent properties, it is widely used in transformers, motors, reactors, transformers, mutual induction coils and other fields. However, iron-based amorphous alloys lack the ability to deform macroscopically at room temperature, are highly brittle, and are prone to brittle fracture, which affects their engineering applications...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information