Environmentally-friendly plastic cement

A plastic and environmentally friendly technology, applied in the field of plastic materials, can solve the problems of easy fading, plastic odor, easy aging, etc., and achieve the effect of not easy aging, smooth surface and high compressive strength

Inactive Publication Date: 2019-06-04
TIANJIN KANG ENVIRONMENTAL PROTECTION EQUIP CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Traditional plastic has peculiar smell, is easy to age, and is easy to fade after long-term use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An environmentally friendly plastic, epoxy soybean oil: 28kg, polyol benzoate: 13kg, polyethylene resin: 8kg, polyepichlorohydrin: 11kg, white carbon black: 4kg, calcium oxide: 3kg, amide: 2kg , barium stearate: 5kg, and 26kg of rubber particles are mixed to make 100kg of the material. The product made by the present invention has excellent corrosion resistance and is not easy to rust during long-term use. The product made by the invention is environmentally friendly, harmless, odorless, smooth in surface, high in compressive strength, good in elasticity, long in service life and not prone to aging. It is suitable for public environment rubber facilities, such as plastic track and so on.

Embodiment 2

[0015] An environmentally friendly plastic, epoxy soybean oil: 31kg, polyol benzoate: 14kg, polyethylene resin: 9kg, polyepichlorohydrin: 13kg, white carbon black: 5kg, calcium oxide: 5kg, amide: 4kg , barium stearate: 5kg, and 14kg rubber granules are mixed to make 100kg of the material. The product made by the present invention is environmentally friendly, harmless and odorless, has a smooth surface, high compressive strength, good elasticity, long service life and is not easy to age. It is suitable for public environment rubber facilities, such as plastic track and so on.

Embodiment 3

[0017] An environmentally friendly plastic, epoxy soybean oil: 30kg, polyol benzoate: 15kg, polyethylene resin: 11kg, polyepichlorohydrin: 12kg, white carbon black: 6kg, calcium oxide: 4kg, amide: 3kg , barium stearate: 4kg, and 15kg rubber granules are mixed to make 100kg of the material. The product made by the present invention has excellent corrosion resistance and is not easy to rust during long-term use. The product made by the invention is environmentally friendly, harmless, odorless, smooth in surface, high in compressive strength, good in elasticity, long in service life and not prone to aging. It is suitable for public environment rubber facilities, such as plastic track and so on.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Environmentally-friendly plastic cement is disclosed. The plastic cement is composed of the following ingredients (by weight): 28-32% of epoxidized soybean oil, 13-15% of polyol benzoate, 7-13% of polyethylene resin, 11-14% of polyepichlorohydrin, 2-7% of white carbon black, 3-5% of calcium oxide, 1-4% of amide, 3-6% of barium stearate and the balance rubber particles. The invention has the following beneficial effects: the prepared product is environmentally-friendly, harmless, odorless, has flat surface, high compressive strength, good elasticity and long service life, and is not easy to age.

Description

1. Technical field [0001] The invention relates to a plastic material, in particular to an environment-friendly plastic. 2. Background technology [0002] Plastics are widely used and are indispensable components in home appliances, automobiles, mobile phones, PCs, medical devices, and lighting appliances. As my country's economy has achieved sustained and stable growth, industries such as home appliances, automobiles, mobile phones, PCs, and medical devices have benefited from a favorable external environment and have also achieved rapid development. The development of downstream industries has further stimulated the demand for plastics. [0003] During the 12th Five-Year Plan period, my country's downstream industries such as automobiles, home appliances, consumer electronics, and medical equipment will continue to maintain rapid development. The demand for plastic parts in these industries will continue to expand, and the demand will also show a trend of high-end and prec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L91/00C08L21/00C08L23/06C08L71/02C08K13/02C08K3/36C08K3/22C08K5/20C08K5/098C08K5/103
Inventor 王维海王胜柏
Owner TIANJIN KANG ENVIRONMENTAL PROTECTION EQUIP CO LTD