Wound dressing capable of stopping bleeding and resisting infection and preparation method of wound dressing
An anti-infection and wound surface technology, which is applied in the fields of pharmaceutical formula, coating, medical science, etc., can solve the problems of weak effect on large-scale bacterial infection, inconvenient and widely popularized use, and ineffective inhibitory effect. Significant blood coagulation effect and the effect of preventing wound infection
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] The invention provides a method for preparing a hemostatic and anti-infective wound dressing, which comprises the following steps:
[0030] (1) Dissolve N-hexylated chitosan in an acetic acid solution to obtain an acetic acid solution of N-hexylated chitosan; the degree of substitution of the N-hexylated chitosan is 8%~ 39%;
[0031] (2) Mixing the N-hexanesylated chitosan acetic acid solution, glycerin and Manuka honey to obtain a mixed solution;
[0032] (3) Coating the mixed solution on the dressing substrate and drying to obtain a hemostatic and anti-infective wound dressing.
[0033] In the present invention, N-hexylated chitosan is dissolved in acetic acid solution to obtain N-hexylated chitosan acetic acid solution. In the present invention, the degree of substitution of the N-hexylated chitosan is 8 to 39%, preferably 8 to 20%, and more preferably 19%.
[0034] In the present invention, the preparation method of the N-hexylated chitosan preferably includes the following...
Example Embodiment
[0064] Example 1
[0065] Preparation of N-Hexylated chitosan: Weigh 2.0g of chitosan and dissolve it in 200mL of 2% acetic acid solution, stir magnetically for 4 hours at room temperature until the chitosan is completely dissolved; add 75mL of absolute ethanol and continue to stir for about 1 hour; The molar mass ratio of chitosan monomer unit to hexanal is 1:0.9. Add hexanal, and then add 10% HCl solution dropwise to adjust the pH to 5.1. Continue stirring at room temperature for Schiff base reaction. The reaction time is 4 hours. Obtain the Schiff base reaction solution;
[0066] According to chitosan monomer unit and NaBH 4 Add NaBH to the Schiff base reaction solution at a mass ratio of 1:3 4 The reduction reaction is carried out under stirring, and the reduction reaction time is 12 hours; after the reduction reaction is completed, 10% NaOH solution is added dropwise to the reduction reaction solution to adjust the pH of the reaction solution to 10, and the precipitated produc...
Example Embodiment
[0068] Example 2
[0069] Other conditions are the same as in Example 1, except that the molar ratio of chitosan monomer unit and hexanal is changed to 1:0.49.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap