Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Composition for antireflection film, antireflection film formed therefrom, polarizing plate containing same, and optical display device containing same

A technology of anti-reflection film and composition, applied in optics, optical elements, nonlinear optics, etc., can solve the problems of hardness and impact resistance deterioration, complexity of anti-reflection film, reduction of reflectivity of anti-reflection film, etc.

Active Publication Date: 2021-02-19
SAMSUNG SDI CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antireflection film manufactured using this method is composed of three coating layers, leading to complexity in the manufacture of the antireflection film
In the anti-reflection film, the absence of the surface hardening layer leads to deterioration of hardness and impact resistance, and the absence of the high-refractive index layer limits the decrease in the reflectivity of the anti-reflection film
Increasing the proportion of inorganic hollow particles in the low-refractive index layer to reduce the reflectivity of the anti-reflection film, although the reflectivity is reduced, it is still difficult to apply due to the deterioration of mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for antireflection film, antireflection film formed therefrom, polarizing plate containing same, and optical display device containing same
  • Composition for antireflection film, antireflection film formed therefrom, polarizing plate containing same, and optical display device containing same
  • Composition for antireflection film, antireflection film formed therefrom, polarizing plate containing same, and optical display device containing same

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0117] Preparation Example 1: Preparation of Formula 1a

[0118] (1) Prepare a solution by diluting 2.11g (10mmol) phenylenephosphonothiodichloride in 30mL tetrahydrofuran (THF), cool the solution to 0°C with an ice bath, and then add 1.14g (11mmol) triethyl Amine solution. Next, a solution was prepared by diluting 1.1 g (10 mmol) of thiophenol in 10 mL of THF, and this solution was slowly added to the resulting solution using a dropping funnel. Keep the resulting solution at 0°C, add 1.14 g (11 mmol) triethylamine to the resulting solution, and slowly add 1.25 g (10 mmol) of 4-aminobenzenethiol in 6 mL of THF using a dropping funnel Solutions prepared by dilution. After the addition was complete, the ice bath was removed and the resulting solution was stirred for about 2 hours. After the reaction was completed, the resulting solution was filtered to remove the amine salt, and then the excess solvent was distilled off under reduced pressure. Then, 100 mL of ethyl acetate (...

preparation Embodiment 2

[0124] Preparation Example 2: Preparation of Formula 1b

[0125] (1) A compound represented by formula B was prepared by the same method as in Preparation Example 1 except that 1.26 g (10 mmol) of 4-hydroxybenzenethiol was used instead of 4-aminobenzenethiol. by column chromatography (SiO 2 , ethyl acetate:hexane=1:4) isolated the final compound {colorless oil, yield: 72%, refractive index: 1.69, 1 H-NMR (300MHz, CDCl 3 ): δ7.99-7.91 (m, 2H), 7.52-7.35 (m, 6H), 7.31-7.23 (m, 5H), 6.74 (dd, J=1.5, 6.6Hz, 2H)}.

[0126] [Formula B]

[0127]

[0128] (2) The compound represented by Formula 1b was prepared by the same method as in Preparation Example 1 except that 2.19 g (5.8 mmol) of the compound represented by Formula B was used instead of the compound represented by Formula A. by column chromatography (SiO 2 , ethyl acetate: hexane = 1:5) isolated the final compound {colorless oil, yield: 78%, refractive index: 1.685, 1 H-NMR (300MHz, CDCl 3 ):δ8.00-7.92(m,2H),7.53-7....

preparation Embodiment 3

[0131] Preparation Example 3: Preparation of Formula 1c

[0132] A solution prepared by diluting 25.04 g (200 mmol) of 4-aminobenzenethiol in 400 mL of THF was cooled to 0° C. using an ice bath, and then 21.3 g (210 mmol) of triethylamine was added. The resulting solution was kept at 0° C., and 21.1 g (100 mmol) of phenylenephosphonothiodichloride was diluted in 200 mL of THF to prepare a solution, which was slowly added to the resulting solution using a dropping funnel. After the addition was complete, the ice bath was removed and the resulting solution was stirred for about 2 hours. After the reaction was completed, the resulting solution was filtered to remove the amine salt, and cooled to 0° C., then 21.3 g (210 mmol) of triethylamine was added to the resulting solution. Then, a solution prepared by diluting 18.6 g (205 mmol) of acryloyl chloride in 100 mL of THF was slowly added to the resulting solution, followed by stirring at 0° C. for 1 hour. After the reaction was ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a composition for an antireflection film, an antireflection film formed therefrom, a polarizing plate comprising the same, and an optical display device comprising the same, the composition containing a compound of Chemical Formula 1, a UV curable compound , antistatic agent and initiator.

Description

technical field [0001] The present invention relates to a composition for an antireflection film, an antireflection film formed from the composition, a polarizing plate comprising the same, and an optical display device comprising the same. Background technique [0002] Optical display devices are typically exposed to external light in use. The external light incident on the optical display device will cause the display quality of the screen of the optical display device to degrade. Therefore, optical display devices generally use anti-reflection films. [0003] Typically, an antireflection film has a structure in which low-refractive-index layers and high-refractive-index layers are alternately stacked on a base layer. Anti-reflection films generally reduce reflectance by lowering the refractive index of the low-refractive index layer. [0004] Since the antireflection film is placed on the outer edge of the optical display device, it is desired that the antireflection f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/5398C08F290/06C08F20/34C08F2/44C08J5/18G02F1/1335G02B1/111G02B5/30
CPCC08F2/44C08F20/34C08F290/06C08J5/18C08K5/5398G02B1/11G02B5/30G02F1/1335C08F290/067C08K2201/017G02B5/305
Inventor 朴世铉林亨泰赵成昕闵庆晙吴釜根
Owner SAMSUNG SDI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com