Modified color masterbatch and preparation method thereof

A technology of modified color masterbatch and functional additives, which is applied in the field of plastic technology, can solve the problems of general tinting power and poor performance such as UV resistance, and achieve the effect of improving tinting power and facilitating production and processing

Inactive Publication Date: 2019-06-25
山东诺森塑胶有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing masterbatch products can already meet the general needs, but the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] A modified masterbatch composed of raw materials in the following weight ratios: 40 parts carrier, 5 parts functional additives, 7 parts pigment, 5 parts dispersant; 15 parts turpentine, 12 parts nucleating agent, 2 parts dispersant, 2 parts of magnesium stearate.

[0023] Further, the functional additive is an anti-ultraviolet additive, and the anti-ultraviolet additive is 2-hydroxy-4-n-octyloxybenzophenone.

[0024] Further, the functional additive is an anti-wear agent, and the anti-wear agent is A-186 anti-wear agent.

[0025] Further, the functional additive is an inorganic flame retardant, and the inorganic flame retardant is antimony trioxide.

[0026] Further, the carrier is a mixture of polyethylene terephthalate and polymer resin, and the ratio is 2:5.

[0027] Further, the pigment is Oil-soluble Yellow 93.

[0028] Further, the dispersant is polyethylene wax.

[0029] Further, the nucleating agent is a rosin nucleating agent.

[0030] A preparation meth...

Example Embodiment

[0036] Example 2

[0037] A modified masterbatch composed of raw materials in the following weight ratios: 80 parts of carrier, 20 parts of functional additives, 21 parts of pigments, 10 parts of dispersant; 25 parts of turpentine, 20 parts of nucleating agent, 5 parts of dispersant, 5 parts of magnesium stearate. Turpentine oil can make the pigment and the carrier very compatible. Magnesium stearate prevents the finely ground pigment particles from causing flocculation and protects a certain degree of fineness.

[0038] Further, the functional additive is an anti-ultraviolet additive, and the anti-ultraviolet additive is 3,5-di-tert-butyl-4-hydroxybenzoic acid n-hexadecyl ester.

[0039] Further, the functional additive is an anti-wear agent, and the anti-wear agent is A-186 anti-wear agent.

[0040] Further, the functional additive is an inorganic flame retardant, and the inorganic flame retardant is magnesium hydroxide.

[0041] Further, the carrier is a mixture of polyethylene te...

Example Embodiment

[0051] Example 3

[0052] A modified masterbatch consisting of raw materials in the following weight ratios: 55 parts of carrier, 15 parts of functional additives, 15 parts of pigments, 7 parts of dispersant; 21 parts of turpentine, 17 parts of nucleating agent, 3 parts of dispersant, 4 parts of magnesium stearate. Turpentine oil can make the pigment and the carrier very compatible. Magnesium stearate prevents the finely ground pigment particles from causing flocculation and protects a certain degree of fineness.

[0053] Further, the functional additive is an anti-ultraviolet additive, and the anti-ultraviolet additive is 2-hydroxy-4-n-octyloxybenzophenone.

[0054] Further, the functional additive is an anti-wear agent, and the anti-wear agent is A-186 anti-wear agent.

[0055] Further, the functional additive is an inorganic flame retardant, and the inorganic flame retardant is aluminum hydroxide.

[0056] Further, the carrier is a mixture of polyethylene terephthalate and polymer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modified color masterbatch and a preparation method thereof. The modified color masterbatch is composed of the following raw materials by weight: 40-80 parts of a carrier, 5-20 parts of functional additives, 7-21 parts of a pigment, 5-10 parts of a dispersant, 15-25 parts of turpentine, 12-20 parts of a nucleating agent, 2-5 parts of a dispersant and 2-5 parts of magnesium stearate. Through reasonable formula and proportion, the pigment and the carrier have good compatibility, pigment particles do not cause flocculation phenomenon, and protection of certain fineness facilitates production and processing. Also due to the setting of multiple functional additives, the finally modified color masterbatch has wear resistance, ultraviolet resistance, flame retardance andother characteristics. The production process adopted by the invention limits the pigment fineness, and sets special technological conditions. The lipophilic characteristic of pigment is utilized, the pigment enters turpentine from water flushing by kneading, and at the same time, the oily carrier coats the surface of the pigment, so that the pigment can be dispersed stably. Through the steps ofplasticization and then granulation, the tinting strength of the modified color masterbatch product is effectively improved.

Description

technical field [0001] The invention relates to the technical field of plastic technology, in particular to a modified color masterbatch and a preparation method thereof. Background technique [0002] Color masterbatch is a new plastic and fiber coloring product developed in the 1960s. It is a polymer compound prepared by uniformly loading pigments in resins. The masterbatch is mainly composed of three parts: colorant, carrier and dispersant. Masterbatch is a new type of polymer material colorant. It is a plastic colorant that is well dispersed with a high proportion of pigments or additives and thermoplastic resins. The selected resin has a good wetting and dispersing effect on the colorant. And it has good compatibility with the material to be colored. The existing masterbatch products can already meet the general needs, but there are still problems such as poor UV resistance and general tinting strength. Contents of the invention [0003] The technical problem to be ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L101/00C08L67/02C08L91/00C08L23/06C08L93/04C08K3/22C08K5/098C08K5/132C08K5/134C08K13/06C08K9/10C08J3/22
Inventor 赵俊超张金福
Owner 山东诺森塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap