Magnetic ring core raw material and preparation method of magnetic ring core

A technology of raw materials and magnetic rings, which is applied in the field of magnetic ring core raw materials and magnetic ring core preparation, can solve the problems of increasing costs, and achieve the effects of reducing raw material costs, increasing magnetic permeability, and reducing losses

Inactive Publication Date: 2019-08-06
SICHUAN DONGGE TECH
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At the same time, in the production process of the magnetic ring core, due to the loss of the mold, a lot of scrap products will be produced, which increases the cost of the product for the production of the factory.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The preparation method of the magnetic ring core is characterized in that it comprises the following process:

[0024] Step 1: Evenly mix 50% FeSi, 35% Sendust and 15% crushed powder to form a mixed powder, the FeSi is 100 mesh, the Sendust is 150 mesh; the crushed powder is 100 mesh, The iron-silicon content in the crushed powder is 58%, and the iron-silicon-aluminum content is 42%;

[0025] Step 2: dilute phosphoric acid with alcohol, the weight ratio of alcohol and phosphoric acid is 1:15, obtains diluted alcohol;

[0026] Step 3: After heating and melting the phenolic resin into a liquid, mix the liquid phenolic resin with the above-mentioned mixed powder, diluted alcohol and lubricating powder, stir for 40 minutes under the condition of 30r / min, and then dry it at 110°C; the mixed powder The weight ratio of the mixed powder to the lubricating powder is 100:0.3, the weight ratio of the mixed powder to the diluted alcohol is 100:0.16, and the weight ratio of the mix...

Embodiment 2

[0030] The preparation method of the magnetic ring core is characterized in that it comprises the following process:

[0031] Step 1: Evenly mix 50% FeSi, 35% Senust and 15% crushed powder to form a mixed powder. FeSi is 100 mesh, Senust is 150 mesh; crushed powder is 150 mesh, The iron-silicon content in the crushed powder is 60%, and the iron-silicon-aluminum content is 40%;

[0032] Step 2: dilute phosphoric acid with alcohol, the weight ratio of alcohol and phosphoric acid is 1:15, obtains diluted alcohol;

[0033] Step 3: After heating and melting the phenolic resin into a liquid, mix the liquid phenolic resin with the above-mentioned mixed powder, diluted alcohol and lubricating powder, stir for 40 minutes under the condition of 30r / min, and then dry it at 110°C; the mixed powder The weight ratio of the mixed powder to the lubricating powder is 100:0.3, the weight ratio of the mixed powder to the diluted alcohol is 100:0.16, and the weight ratio of the mixed powder to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A magnetic ring core raw material includes a raw material A and a raw material B. The raw material A is composed of 50% of ferrosilicon, 35% of sendust and 15% of crushed powder, and the total amountof the raw material A is 100%. The raw material B is composed of phosphoric acid, resin, lubricating powder and alcohol. The weight ratio of the raw material A to the phosphoric acid is 100:(0.1-0.3).The weight ratio of the raw material A to the resin is 100:(0.3-0.8). The weight ratio of the raw material A to the lubricating powder is 100:(0.1-0.5). The weight ratio of the raw material A to thealcohol is 100:(1-4.5).

Description

technical field [0001] The invention relates to the technical field of magnetic cores, in particular to a raw material for a magnetic ring core and a preparation method for the magnetic ring core. Background technique [0002] The magnetic ring core refers to the composite soft magnetic material made by mixing and pressing ferromagnetic powder and insulating binder. According to different materials, it mainly includes permalloy magnetic powder core, magnetic core and sendust magnetic powder core. [0003] With the development of technology, many devices have miniaturization requirements for electronic components, which requires the magnetic ring core to have high magnetic permeability, and sendust magnetic powder core and permalloy magnetic powder core have high magnetic permeability And the characteristics of low loss, because the price of sendust magnetic powder core is lower than permalloy, so it has replaced permalloy magnetic core in many occasions. [0004] At the sam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/00H01F41/00H01F41/02
CPCH01F1/00H01F41/00H01F41/0246
Inventor 罗建桥应俊李水超
Owner SICHUAN DONGGE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com