A kind of high performance concrete and preparation method thereof

A high-performance concrete and recycled aggregate technology, applied in the field of concrete, can solve the problems of large porosity, high water absorption rate, and increased performance degradation of recycled aggregate, and achieve the effect of excellent impermeability.

Active Publication Date: 2021-08-06
温州市三箭混凝土有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the waste concrete is crushed by external force, different degrees of fine cracks will appear inside the recycled aggregate, which will make the recycled aggregate have a large porosity and a high water absorption rate. Therefore, after the recycled aggregate replaces part of the natural aggregate, recycled concrete Workability, impermeability, strength and other aspects of performance have declined, and the performance reduction range increases with the increase of the replacement rate, which needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high performance concrete and preparation method thereof
  • A kind of high performance concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A high-performance concrete, comprising the following components by weight:

[0042] 350 parts of cement, the variety is P.O42.5;

[0043] 900 parts of coarse aggregate, the coarse aggregate includes 50% recycled aggregate and 50% crushed stone, the crushed stone is produced in Lishui Qingtian and has a continuous gradation of 5-31.5mm, the coarse aggregate of recycled aggregate primary concrete is crushed stone, The recycled aggregate is 5-31.5mm continuous gradation;

[0044] 540 parts of fine aggregate, the fine aggregate is medium sand, produced in Qingtian, Lishui;

[0045] 160 parts of water;

[0046] 190 parts of admixture, the admixture is compounded by mineral powder and fly ash with a mass ratio of 4:3;

[0047] 10 parts of admixture, the admixture is composed of expansion agent and water reducer with a mass ratio of 4:1, the model of the expansion agent is TD-AEA, and the water reducer is TD-5-3, both purchased from Shanghai Tongtai Concrete Admixtures Li...

Embodiment 2

[0059] A high-performance concrete, comprising the following components by weight:

[0060] 390 parts of cement, the variety is P.O42.5;

[0061] 1020 parts of coarse aggregate, the coarse aggregate includes 50% recycled aggregate and 50% crushed stone, the crushed stone is produced in Lishui Qingtian and has a continuous gradation of 5-31.5mm, the coarse aggregate of the recycled aggregate primary concrete is crushed stone, The recycled aggregate is 5-31.5mm continuous gradation;

[0062] 600 parts of fine aggregate, the fine aggregate is medium sand, produced in Qingtian, Lishui;

[0063] 180 parts of water;

[0064] 230 parts of admixture, the admixture is compounded by mineral powder and fly ash with a mass ratio of 4:3;

[0065] 14 parts of admixture, the admixture is composed of expansion agent and water reducer with a mass ratio of 4:1, the model of the expansion agent is TD-AEA, and the water reducer is TD-5-3, both purchased from Shanghai Tongtai Concrete Admixtur...

Embodiment 3

[0077] A high-performance concrete, comprising the following components by weight:

[0078] 370 parts of cement, the variety is P.O42.5;

[0079] 960 parts of coarse aggregate, the coarse aggregate includes 50% recycled aggregate and 50% crushed stone, the crushed stone is produced in Lishui Qingtian and has a continuous gradation of 5-31.5mm, the coarse aggregate of the recycled aggregate primary concrete is crushed stone, The recycled aggregate is 5-31.5mm continuous gradation;

[0080] 570 parts of fine aggregate, the fine aggregate is medium sand, produced in Qingtian, Lishui;

[0081] 170 parts of water;

[0082] 210 parts of admixture, the admixture is compounded by mineral powder and fly ash with a mass ratio of 4:3;

[0083] 12 parts of admixture, the admixture is composed of expansion agent and water reducer with a mass ratio of 4:1, the model of the expansion agent is TD-AEA, and the water reducer is TD-5-3, both purchased from Shanghai Tongtai Concrete Admixture...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
quality scoreaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance concrete and a preparation method thereof. The high-performance concrete comprises the following components in parts by weight: 350-390 parts of cement; 900-1020 parts of coarse aggregate; 540-600 parts of fine aggregate; 160-600 parts of water 180 parts; 190-230 parts of admixture; 10-14 parts of admixture; the coarse aggregate includes 50-70% recycled aggregate and 30-50% gravel, and the recycled aggregate is sequentially treated with S1 acid, S2 mortar treatment, S3 emulsion treatment. After the recycled aggregate is treated with S1 acid, S2 mortar, and S3 emulsion in sequence, the cracks are better repaired, so the performance of the concrete such as compressive strength is close to that of natural aggregate, and the impermeability is even better than that without regeneration. Aggregate concrete.

Description

technical field [0001] The invention relates to concrete, in particular to a high-performance concrete and a preparation method thereof. Background technique [0002] Concrete refers to the collective name of engineering composite materials that are cemented together by cementitious materials and aggregates. It is often used in house construction and road construction. Generally, cement is used as the cementitious material and sand and gravel are used as aggregates. At present, when natural aggregate resources are in short supply and waste concrete is seriously polluting the urban environment, people use waste concrete to make recycled aggregate only after cracking, crushing, and screening to partially or completely replace natural aggregate to make recycled aggregate. concrete. [0003] The production of recycled concrete undoubtedly plays a beneficial role in the treatment of construction waste and the protection of the ecological environment, which is in line with the na...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B20/10C08G18/12C08G18/66C08G18/48C08G18/34C08G18/40C08G18/61
CPCC04B20/1037C04B20/107C04B28/04C04B2111/00293C04B2201/50C08G18/12C08G18/348C08G18/4009C08G18/4825C08G18/6692C04B18/08C04B18/16C04B14/02C04B14/06C04B18/12C04B2103/0068C04B2103/302C04B16/0633C08G18/61
Inventor 黄炎孝
Owner 温州市三箭混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com