Multilayer film with metallic brushed effect layer
A multi-layer film, silk-colored technology, applied in the direction of coating, lamination, layered products, etc., can solve the problems of insufficient durability, limited surface protection, can not meet the car interior decoration, etc., to improve transferability, reduce Smoothing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0049] Preparation of anchor ink-absorbing layer coating solution:
[0050]
[0051] In the container, first add ethyl acetate and butyl acetate, and then add the above-mentioned other components in sequence, and stir at high speed to fully dissolve and disperse to obtain printing paste, which is ready for use.
[0052] Prepare the brushed color layer ink, lining color layer ink, silver layer ink and black background layer ink required for printing and set it aside.
[0053] On a 60-micron thick acrylic resin film, a 0.5-micron anchor ink-absorbing layer, a 0.8-micron brushed color layer, a 0.8-micron lining color layer, a 3-micron silver layer, and a 3-micron black background are sequentially printed by a multi-color gravure printing machine layer, the gravure printing drying temperature is 75°C, the printing speed is 30m / min, and the acrylic resin film with metal wire drawing effect is printed, and then the adhesive layer is coated on the coating laminating machine with a...
Embodiment 2
[0056] Preparation of anchor ink-absorbing layer coating solution:
[0057]
[0058] In the container, first add ethyl acetate and butyl acetate, and then add the above-mentioned other components in sequence, and stir at high speed to fully dissolve and disperse to obtain printing paste, which is ready for use.
[0059] Prepare the brushed color layer ink, lining color layer ink, silver layer ink and black background layer ink required for printing and set it aside.
[0060] On a 75-micron thick acrylic resin film, a 2-micron anchor ink-absorbing layer, a 2-micron brushed color layer, a 2-micron lining color layer, a 5-micron silver layer, and a 3-micron black background are sequentially printed by a multi-color gravure printing machine layer, the gravure printing drying temperature is 75°C, the printing speed is 30m / min, and the acrylic resin film with metal wire drawing effect is printed, and then the adhesive layer is coated on the coating laminating machine with a thick...
Embodiment 3
[0063] Preparation of anchor ink-absorbing layer coating solution:
[0064]
[0065] In the container, first add ethyl acetate and butyl acetate, and then add the above-mentioned other components in sequence, and stir at high speed to fully dissolve and disperse to obtain printing paste, which is ready for use.
[0066] Prepare the brushed color layer ink, lining color layer ink, silver layer ink and black background layer ink required for printing and set it aside.
[0067] On a 75-micron thick acrylic resin film, a 1-micron anchor ink-absorbing layer, a 0.5-micron brushed color layer, a 0.5-micron lining color layer, a 3-micron silver layer, and a 4-micron black background are sequentially printed by a multi-color gravure printing machine Layer, the gravure printing drying temperature is 75 ℃, the printing speed is 30m / min, and the acrylic resin film with metal wire drawing effect is printed, and then the adhesive layer is coated on the coating laminating machine with a t...
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| glass transition temperature | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More