Production method of fluorine-containing cyanate ester resin

Abstract

The invention discloses a production method of fluorine-containing cyanate ester resin. A specific production process comprises the following steps of firstly, producing a dicarbonyl unsaturated monomer, then making the dicarbonyl unsaturated monomer reacted with a Grignard reagent to produce unsaturated alkylene trimethoxy phenyl ether, then introducing silicon and fluorine onto a monomer, and conducting cross-linking by means of boric acid to produce the fluorine-containing cyanate ester resin. The fluorine-containing cyanate ester resin produced through the method contains multiple cyanateester groups, and has multiple acting sites, moreover, the multiple cyanate ester groups are distributed in different directions, the steric hindrance of a single monomer resin molecule is large, generation of a triazine ring in a curing process is limited, thus the tenacity of the resin is greatly improved, moreover, the cyanate ester groups in the different directions can be reacted at the sametime in the multiple directions, in a polymerization process, hyperbranched structures can be formed in the different directions, and the rigidity of a polymer is further reduced, so that compared with bisphenol A cyanate ester resin, a produced resin monomer has high tenacity.

Description

technical field [0001] The invention belongs to the field of cyanate resin preparation and relates to a preparation method of fluorine-containing cyanate resin. Background technique [0002] Bisphenol A cyanate resin has the equivalent modulus and mechanical strength of bisphenol A epoxy resin, and has excellent dielectric properties, and through the modification of the bisphenol A matrix, a large amount of fluorine is introduced into the matrix , prepared into bis(phenyl cyanate) hexafluoropropane, the resin has high flame retardancy due to the effect of fluorine element, but the bisphenol A cyanate resin is a linear structure, resulting in the rigidity of the prepared resin after curing Larger and less resilient. [0003] In the curing process of the existing cyanate resin, the trimerization ring formation reaction forms a triazine ring structure, which makes the cured product stronger in rigidity, brittle in texture and poor in toughness. In order to improve the toughnes...

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of preparation method of fluorine-containing cyanate resin, the prepared fluorine-containing cyanate resin contains a plurality of cyanate groups, has more action sites, and a plurality of cyanate The groups are distributed in different directions, and the steric hindrance of a single monomer resin molecule is relatively large, which limits the formation of triazine rings during the curing process, thereby greatly improving the toughness of the resin, and the cyanate groups in different directions can be simultaneously Reaction in multiple directions, hyperbranched structure can be formed in different directions during the polymerization process, further reducing the rigidity of the polymer, and the hyperbranched structure forms a huge network structure, so that a large amount of fluorine and silicon are evenly distributed in the network structure Elements, because the introduction of a large number of Si-O bonds improves the flexibility of the polymer and further reduces its rigidity, so that the prepared resin monomer has higher toughness compared with bisphenol A cyanate resin, And compared with the resin modified by miscibility with rubber elastomer, its thermal property is higher, and then solves the problem that the existing bisphenol A cyanate resin is a straight chain structure, resulting in greater rigidity of the prepared resin after curing , the toughness is low, and when the existing bisphenol A type cyanate resin is modified, it is directly mixed with the rubber elastomer for modification, but the flame retardancy and thermal stability of the modified cyanate resin are both Reducing, and adding reinforcement additives during the melting process, because it is difficult to achieve complete blending of the reinforcement additives and the two, resulting in the problem of uneven thermal stability, flame retardancy and toughness of the modified resin

Images