Roll system preparation method and rolling method for rolling ultra-thin ultra-wide stainless steel products

A stainless steel, ultra-thin technology, applied in the direction of rolls, metal rolling, metal rolling, etc., can solve problems such as unsatisfactory use requirements, thickness tolerance, poor plate shape, etc., achieve small thickness tolerance fluctuations, product quality improvement, steel The effect of high coil yield

Active Publication Date: 2019-09-06
SHANXI TAIGANG STAINLESS STEEL PRECISION STRIP CO LTD
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the production of ultra-thin and ultra-wide stainless steel precision strips is still the bottleneck of the precision stain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roll system preparation method and rolling method for rolling ultra-thin ultra-wide stainless steel products
  • Roll system preparation method and rolling method for rolling ultra-thin ultra-wide stainless steel products
  • Roll system preparation method and rolling method for rolling ultra-thin ultra-wide stainless steel products

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0051] Example one:

[0052] A stainless steel coil with a thickness of 0.08mm and a width of 650mm is selected as the raw material, and the thickness of the finished steel strip for rolling is 0.02mm.

[0053] First, a 20-high rolling mill with a thickness of 0.08mm as a raw material for cold-rolled coils is rolled. When rolling, the British BP rolling oil is used for lubrication and cooling. The temperature of the rolling oil is 39°C. After 8 passes, it is cold rolled to 0.02mm. The rolling speed of the first seven passes is 300m / min, the rolling speed of the finished product pass is 200m / min, the work roll diameter is 27mm, the rolling pressure during the whole process is 1100-1300KN, and the reduction rate of the pass is 10-30%.

[0054] The roll system configuration selects the designed roll system (that is, the roll system equipped in the above-mentioned roll system configuration method).

[0055] The main technical indicators of products produced by the above process can reach:...

Example Embodiment

[0059] Embodiment two:

[0060] A stainless steel coil with a thickness of 0.1mm and a width of 650mm is selected as the raw material, and the thickness of the finished steel strip for rolling is 0.03mm.

[0061] First, a 20-high rolling mill with a thickness of 0.1mm as a raw material for cold-rolled coils is rolled. During rolling, British BP rolling oil is used for lubrication and cooling. The temperature of the rolling oil is 40°C. After 8 passes, it is cold rolled to 0.03mm. The rolling speed of the first seven passes is 350m / min, the rolling speed of the finished product pass is 200m / min, the work roll diameter is 28mm, the rolling pressure during the whole process is 1000-1200KN, and the pass reduction rate is 10-30%.

[0062] The roll system configuration selects the designed roll system.

[0063] The main technical indicators of products produced by the above process can reach:

[0064] 1) Thickness deviation: 0.03±0.002mm;

[0065] 2) Hardness (HV): 560—590HV;

[0066] 3) Rough...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Unevennessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a roll system preparation method and rolling method for rolling ultra-thin ultra-wide stainless steel products. The roll system preparation method comprises the following stepsthat the diameter of a working roll is set to be 25-28 mm; and the cone ratio of intermediate rolls is set to be 0.25%; and the convexity curve of the second intermediate rolls is set to be a function curve between the cos of 30-90 degrees. The rolling method comprises the following steps of 1) selecting, specifically, a stainless steel coil raw material with the thickness of 0.08 to 0.1mm and the width of more than 600 mm is selected; and 2) rolling, specifically, cold rolling is carried out for eight times until the thickness is 0.03mm or below, and the pressing rate at the next time is 10%-30%. According to the roll system preparation method and the rolling method for rolling the ultra-thin ultra-wide stainless steel products, the convexity of the second intermediate roll, the taper ofthe intermediate roll and the diameter of the working roll are limited, during rolling, the thickness tolerance fluctuation of the product is small, the flatness of the plate type is good, the rolling process is stable, the yield of the steel coil is high, the product quality is remarkably improved, the method is suitable for industrial mass production, and the high-quality requirement of the high-end industry of the precision stainless steel extremely thin strip is met.

Description

technical field [0001] The invention relates to the technical field of steel strip processing, in particular to a method for arranging a roll system and a rolling method for rolling ultra-thin and ultra-wide stainless steel products. Background technique [0002] At present, stainless steel precision strips are gradually moving towards the high-end market, and precision stainless steel is a high-end variety of stainless steel with high technical content and complex processes. Precision stainless steel has strict requirements on product characteristics such as dimensional tolerances, plate shapes, and surfaces. Ultra-thin and ultra-wide stainless steel (width ≥ 600mm, thickness ≤ 0.05mm) is produced through the cold rolling characteristics of cold deformation strengthening. During the manufacturing process, there will be obvious changes or fluctuations in the shape control and surface control, and even cause the entire roll to be scrapped. [0003] At present, the productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B1/22B21B27/02
CPCB21B1/22B21B27/021B21B2027/022
Inventor 王天翔李华罗纪平段浩杰武显斌刘玉栋任岩廖席员超波张艳霞
Owner SHANXI TAIGANG STAINLESS STEEL PRECISION STRIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap