A kind of anti-tensile creep non-bromine flame-retardant expanded polystyrene material and preparation method

A technology of expanded polystyrene and polystyrene, applied in the field of building decoration materials, which can solve the problems of unfavorable outdoor use, poor tensile creep resistance and flame retardancy

Active Publication Date: 2022-02-22
HUANGSHAN MEISEN NEW MATERIAL TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the technical problem to be solved by the present invention is to provide a kind of expanded polystyrene composite material with excellent tensile creep resistance and bromine-free flame retardancy, so as to solve the problem of the foamed polystyrene composite material in the prior art due to its resistance to Poor tensile creep properties and flame retardant properties are not conducive to outdoor use;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-tensile creep non-bromine flame-retardant expanded polystyrene material and preparation method
  • A kind of anti-tensile creep non-bromine flame-retardant expanded polystyrene material and preparation method
  • A kind of anti-tensile creep non-bromine flame-retardant expanded polystyrene material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The expanded polystyrene composite material with excellent tensile creep resistance and bromine-free flame retardancy described in this example, based on the total amount of raw materials for the preparation of the composite material, includes the following raw material components in mass content:

[0039]

[0040]

[0041] The preparation method of the tensile creep-resistant bromine-free flame-retardant expanded polystyrene composite material described in this embodiment comprises the following steps:

[0042] (1) Dry the selected amount of polystyrene, phenolic resin, rock wool fiber, polyetherimide, polytetrafluoroethylene fiber, polypropylene mesh fiber and various auxiliary agents at 95 ° C. Mix evenly, and discharge to cold mixing, cool down to 80°C and discharge to obtain a special premix;

[0043] (2) adding the above-mentioned special premix into a parallel twin-screw extruder to extrude and granulate, controlling the barrel temperature of the parallel t...

Embodiment 2

[0047] The tensile creep-resistant bromine-free flame-retardant expanded polystyrene composite material described in this embodiment, the raw materials for its preparation include the following raw material components in parts by weight:

[0048]

[0049]

[0050] The preparation method of the tensile creep-resistant bromine-free flame-retardant expanded polystyrene composite material described in this embodiment comprises the following steps:

[0051] (1) Dry the selected amount of polystyrene, phenolic resin, rock wool fiber, polyetherimide, polytetrafluoroethylene fiber, polypropylene mesh fiber and various auxiliary agents at 120 ° C. Mix evenly, and discharge to cold mixing, cool down to 80°C and discharge to obtain a special premix;

[0052] (2) adding the above-mentioned special premix into a parallel twin-screw extruder to extrude and granulate, controlling the barrel temperature of the parallel twin-screw extruder to be 165° C., and the screw speed to be 80 rpm to...

Embodiment 3

[0056] The tensile creep-resistant bromine-free flame-retardant expanded polystyrene composite material described in this embodiment, its preparation raw materials include raw material components of the following quality:

[0057]

[0058]

[0059] The preparation method of the tensile creep-resistant bromine-free flame-retardant expanded polystyrene composite material described in this embodiment comprises the following steps:

[0060] (1) Dry the selected amount of polystyrene, phenolic resin, rock wool fiber, polyetherimide, polytetrafluoroethylene fiber, polypropylene mesh fiber and various auxiliary agents at 105 ° C. Mix evenly, and discharge to cold mixing, cool down to 80°C and discharge to obtain a special premix;

[0061] (2) adding the above-mentioned special premix into a parallel twin-screw extruder to extrude and granulate, controlling the barrel temperature of the parallel twin-screw extruder to be 150° C., and the screw speed to be 90 rpm to obtain pellet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building decoration materials, in particular to a foamed polystyrene composite material with excellent tensile creep resistance and bromine-free flame retardancy, and further discloses a preparation method thereof. The foamed polystyrene composite material of the present invention mainly uses general-purpose polystyrene, phenolic resin, polypropylene mesh fiber, rock wool fiber, polyetherimide, polytetrafluoroethylene fiber as raw material, and by adding phase Compatible agent, lubricant, coupling agent, foaming agent and ultraviolet light absorber are used as auxiliary agents to carry out extrusion granulation and molding. The expanded polystyrene composite material of the present invention greatly improves the tensile creep resistance and flame retardancy of the expanded polystyrene composite material under the coordinated action of various raw material components, and does not contain toxic bromine The flame retardant can be used in fields requiring high tensile creep resistance and flame retardancy of polystyrene foam composite materials, greatly expanding the application field of foam polystyrene composite materials.

Description

technical field [0001] The invention belongs to the technical field of building decoration materials, in particular to a foamed polystyrene composite material with excellent tensile creep resistance and bromine-free flame retardancy, and further discloses a preparation method thereof. Background technique [0002] All-plastic composite material is a kind of composite material made entirely of plastic, which does not use any wood components, and is prepared by micro-foaming, injection or extrusion molding and other processing techniques to obtain products that are similar in appearance to wood and have a density equivalent to that of wood. Expanded polystyrene composite material is one of the research directions. [0003] Compared with the first generation of wood-plastic composite materials, expanded polystyrene composite products have light weight, excellent water resistance, durability and decorative properties, and are widely used in the market. However, compared with th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L61/06C08L79/08C08L27/18C08L23/12C08L35/06C08K7/10C08K5/3475C08K5/132C08J9/10C08J9/08
CPCC08J9/105C08J9/08C08J2325/06C08J2461/06C08J2479/08C08J2427/18C08J2203/04C08J2203/02C08K7/10C08K5/3475C08K5/132
Inventor 盛岳金赵小亮
Owner HUANGSHAN MEISEN NEW MATERIAL TECH