Method for preparing fiber-grade polyester chip for textile processing

A technology of polyester chips and fiber grades, applied in textiles and papermaking, fiber chemical characteristics, single-component polyester artificial filaments, etc., can solve the problems of long-term storage, antibacterial and disinfection characteristics fade and disappear, and unfavorable users and other problems to achieve the effect of speeding up cooling and drying and reducing moisture

Inactive Publication Date: 2019-10-01
江苏鑫福纤维科技有限公司
View PDF16 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the textiles are generally soaked in the disinfectant and antibacterial agent after the textiles are made. Although this method can make the textiles have the characteristics of disinfection and antibacterial, the characteristics only exist on the surface of the textiles, resulting in many After the first use, the antibacterial and disinfection properties are easy to fade and disappear, and it cannot be stored for a long time, which is not conducive to the user's use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of method that the present invention is used for the fiber grade polyester chips of textile processing, described method for the fiber grade polyester chips of textile processing comprises the following steps:

[0023] S1, the preparation of antibacterial powder:

[0024] (7) React a certain amount of zeolite with 400ml of antibacterial metal ion solution at 40°C for 2 hours, the zeolite and antibacterial metal solution are equimolar, so that the zeolite can fully exchange reaction with the antibacterial metal ion solution, and precipitate all antibacterial Metal ion;

[0025] (8) After the reaction is completed, centrifuge the metal antibacterial ions at the place, and use deionized water to wash until no antibacterial ions are separated out in the lotion, that is, all the antibacterial metal ions are separated out;

[0026] (9) The obtained antibacterial ions are dried at 100°C for 1 hour, and then burned at 500°C for 3 hours to obtain antibacterial powder. Th...

Embodiment 2

[0032] A kind of method that the present invention is used for the fiber grade polyester chips of textile processing, described method for the fiber grade polyester chips of textile processing comprises the following steps:

[0033] S1, the preparation of antibacterial powder:

[0034] (10) React a certain amount of zeolite with 600ml of antibacterial metal ion solution at 40°C for 3 hours, the zeolite and antibacterial metal solution are equimolar, so that the zeolite can fully exchange reaction with the antibacterial metal ion solution, and precipitate all the antibacterial Metal ion;

[0035] (11) After the reaction is completed, centrifuge the metal antibacterial ions at the place, and use deionized water to wash until no antibacterial ions are separated out in the lotion, that is, all antibacterial metal ions are separated out;

[0036] (12) The obtained antibacterial ions are dried at 100°C for 1 hour, and then burned at 500°C for 3 hours to obtain antibacterial powder....

Embodiment 3

[0042] A kind of method that the present invention is used for the fiber grade polyester chips of textile processing, described method for the fiber grade polyester chips of textile processing comprises the following steps:

[0043] S1, the preparation of antibacterial powder:

[0044] (13) React a certain amount of zeolite with 800ml of antibacterial metal ion solution at 40°C for 4 hours, the zeolite and antibacterial metal solution are equimolar, so that the zeolite can fully exchange reaction with the antibacterial metal ion solution, and precipitate all antibacterial Metal ion;

[0045] (14) After the reaction is completed, centrifuge the metal antibacterial ions at the place, and use deionized water to wash until no antibacterial ions are separated out in the lotion, that is, all the antibacterial metal ions are separated out;

[0046](15) The obtained antibacterial ions are dried at 100°C for 1 hour, and then burned at 500°C for 3 hours to obtain antibacterial powder. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a fiber-grade polyester chip for textile processing, and the method comprises the following steps: S1, preparation of antibacterial powder, namely a certain amount of zeolite with 400-800 ml of an antibacterial metal ion solution are reacted at 40DEG C for 2-4 hours; after the reaction is completed, centrifugal separation is carried out, and deionizedwater is used for washing until no antibacterial ion is separated out from a washing liquid; the obtained antibacterial ions are dried at 100 DEG C for 1 hour and then burned at 500 DEG C for 3 hoursto obtain the antibacterial powder. In the invention, high-temperature activated carbon powder and the antibacterial powder containing the antibacterial metal ions are added into the traditional rawmaterials of the polyester chip, and the antibacterial powder and the activated carbon powder have antibacterial and disinfecting effects, and are fully mixed and reacted with the polyester raw materials, so that the formed new polyester also has antibacterial and disinfecting effects, and further a textile fabric made of the polyester chip also has antibacterial and disinfecting effects.

Description

technical field [0001] The invention relates to the technical field of polyester chips, in particular to a method for fiber-grade polyester chips used in textile processing. Background technique [0002] Polyester is a general term for polymers obtained by polycondensation of polyols and polybasic acids. Generally, dibasic acids, dibasic alcohols and additives are adjusted into slurry to make finished polyester through direct esterification. The finished polyester mainly refers to poly Ethylene phthalate, which also customarily includes linear thermoplastic resins such as polybutylene terephthalate and polytrimethylene terephthalate, is one of the earliest materials used as textile raw materials, and it is also the mainstay of synthetic fibers. Number one variety. Its biggest advantage is that it has good wrinkle resistance and shape retention, and has high strength. It is durable, wrinkle-resistant, non-ironing, and non-sticky. Polyester chips have many excellent textile ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/183C08G63/78C08K7/24C08K3/015C08K3/22D01F1/10D01F6/92
CPCC08G63/183C08G63/78C08K3/22C08K7/24C08K2003/2227C08K3/015D01F1/10D01F1/103D01F6/92
Inventor 李金光杨双会耿建波
Owner 江苏鑫福纤维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products