Low-temperature sintering method for enhancing strength of ceramic green body

A ceramic green body and low-temperature sintering technology, which is applied in the field of ceramic processing, can solve the problems of high sintering temperature, long sintering time, and large energy consumption, so as to reduce the sintering temperature, reduce the sintering temperature and sintering time, and prolong the service life Effect

Inactive Publication Date: 2019-10-18
阜阳创启工艺品有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing patent document CN109232001A discloses a firing method for improving the strength of the ceramic tableware body. After placing the ceramic green body in the kiln, it undergoes primary firing, spray treatment, secondary firing, tertiary fi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature sintering method for enhancing strength of ceramic green body

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] A low-temperature sintering method for enhancing the strength of a ceramic body includes the following steps:

[0022] (1) One-time drying: After the green body is prepared, perform microwave drying at a frequency of 760MHz, a power of 0.04kW, heating for 5s, stopping for 60s, and drying to a moisture content of 35-40%, uniformly and slowly removing part of the water in the green body , Reduce the gas and voids in the ceramic green body, make the particles in the green body closer, lower the sintering temperature of the green body, and dry the green body once;

[0023] (2) Spraying: spray the surface care agent uniformly on the surface of the once-dried green body, the spraying amount of the surface care agent is 0.5ml / dm each time 2 , Consists of the following parts by weight of raw materials: sodium selenite 14, nano silica 7, nano silver 6, borax 2, water 400, continuous spraying 2 times, the interval between the two is 3h, the surface care agent is made ...

Example Embodiment

[0029] Example 2

[0030] A low-temperature sintering method for enhancing the strength of a ceramic body includes the following steps:

[0031] (1) One-time drying: After the green body is prepared, perform microwave drying at a frequency of 780MHz, a power of 0.05kW, heating for 6s, stopping for 65s, and drying to a moisture content of 35-40%, uniformly and slowly removing part of the water in the green body , Reduce the gas and voids in the ceramic green body, make the particles in the green body closer, lower the sintering temperature of the green body, and dry the green body once;

[0032] (2) Spraying: spray the surface care agent uniformly on the surface of the once-dried green body, the spraying amount of the surface care agent is 0.6ml / dm each time 2 , Consists of the following parts by weight of raw materials: sodium selenite 15, nano silica 8, nano silver 7, borax 2.5, water 450, continuous spraying 2 times, the interval between the two is 3.5h, the surface care agent cons...

Example Embodiment

[0038] Example 3

[0039] A low-temperature sintering method for enhancing the strength of a ceramic body includes the following steps:

[0040] (1) One-time drying: After the green body is prepared, perform microwave drying, frequency of 800MHz, power of 0.06kW, heating for 7s, stop for 70s, and drying to a moisture content of 35-40%, uniformly and slowly remove part of the water in the green body , Reduce the gas and voids in the ceramic green body, make the particles in the green body closer, lower the sintering temperature of the green body, and dry the green body once;

[0041] (2) Spraying: spray the surface care agent uniformly on the surface of the once-dried green body, the spraying amount of the surface care agent is 0.7ml / dm each time 2 , Consists of the following parts by weight of raw materials: sodium selenite 16, nano-silica 9, nano-silver 8, borax 3, water 500, continuous spraying 2 times, the interval between the two is 4h, the surface care agent consists of a variet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention mainly relates to the technical field of ceramic processing, and discloses a low-temperature sintering method for enhancing the strength of a ceramic green body. The low-temperature sintering method comprises the steps of primary drying, spraying, secondary drying, primary sintering, secondary sintering and post-treatment; according to the low-temperature sintering method for enhancing the strength of the ceramic green body, a sintering temperature is low, the strength and wear resistance of the ceramic green body can be significantly improved, the surface is smooth, the practicability of ceramic is improved, and the service life of the ceramic is prolonged; firstly, a ceramic green is subjected to intermittent microwave drying, part of moisture in the green is uniformly andslowly removed, gas and voids in the ceramic green are reduced to enable particles in the green to be closer, and the sintering temperature of the green is reduced; and a surface care agent is uniformly sprayed on the surface of the green twice continuously after primary drying, the surface care agent is prepared from a variety of nano materials, and can form a uniform protective layer on the surface of the green, so that cracks of the green in the subsequent processing process are avoided, and the strength and wear resistance of the ceramic are improved.

Description

technical field [0001] The invention mainly relates to the technical field of ceramic processing, in particular to a low-temperature sintering method for enhancing the strength of a ceramic green body. Background technique [0002] With the gradual improvement of people's living standards and the change of aesthetic views, people are more and more fond of ceramic products, and the scope of use of ceramic products in daily life is also becoming wider and wider, such as tableware, floors, wall tiles, sanitary ware, etc., can be seen everywhere The use of ceramic products, ceramic products have high strength, but cracks or defects will appear after being subjected to sudden high temperature, low temperature, impact or bump, which will obviously affect the appearance and service life of ceramic products, and reduce the practicability of ceramic products. [0003] The preparation process of ceramic products includes the process of blank preparation, molding, drying, sintering, gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/64C04B41/85B28B11/24
CPCB28B11/243C04B35/64C04B41/5116C04B41/85C04B2235/6562C04B2235/6565C04B2235/6567C04B2235/661C04B41/5035C04B41/5006C04B41/5007C04B41/4578C04B41/4535
Inventor 余国海
Owner 阜阳创启工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap