A kind of preparation method of chitosan phosphorus removal material and chitosan phosphorus removal material

A technology of chitosan and metal salts, which is applied in chemical instruments and methods, water treatment parameter control, and other chemical processes, can solve the problems of large consumption of acid and alkali solutions, cumbersome preparation process, etc., and achieve uniform load, rich sources, The effect of non-pyrogenic reaction

Active Publication Date: 2022-07-19
OCHEMATE MATERIAL TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The phosphorus removal adsorbent can be regenerated and reused, has a large adsorption capacity (above 27mg / g), and has good industrial practical value, but the preparation process is cumbersome, and the consumption of acid and alkali solution is large during the process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of chitosan phosphorus removal material and chitosan phosphorus removal material
  • A kind of preparation method of chitosan phosphorus removal material and chitosan phosphorus removal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Take 50g of chitosan with a particle size of 1mm, a degree of deacetylation of 90%, and a viscosity-average molecular weight of 100,000, add it to a 10L aqueous solution, stir at a speed of 60 rpm to make it form a suspension, add 41g Fe(NO) 3 ) 3 , 26g MnSO 4 , 94g Al(NO 3 ) 3 , After stirring evenly, use spray drying technology to dry the adsorption and phosphorus removal material. The spray drying conditions are: inlet air temperature 150 °C, outlet air temperature 80 °C, drying time 1.5S, maximum water evaporation 8Kg / h, peristaltic pump feeding 2L / h, dry air flow 1.5m 3 / min, spray gas flow 0.5m 3 / h, the nozzle diameter is 2mm, and the dry powder recovery rate is 95%.

Embodiment 2

[0049] Weigh 41g Fe(NO 3 ) 3 , 26g MnSO 4 , 94g Al(NO 3 ) 3 , add it into 16L of water, stir at a speed of 50 rpm to dissolve it, add 50g of chitosan with a particle size of 1 mm, a degree of deacetylation of 90%, and a viscosity average molecular weight of 300,000, stir and mix evenly, and then use spray drying The adsorption and dephosphorization material is obtained by technical drying. The spray drying conditions are as follows: the inlet air temperature is 200°C, the outlet air temperature is 100°C, the drying time is 1.5S, the maximum water evaporation is 8Kg / h, the peristaltic pump feed is 2L / h, and the drying air flow rate is 1.5m. 3 / min, spray gas flow 0.5m 3 / h, the nozzle diameter is 2mm, and the dry powder recovery rate is 95%.

Embodiment 3

[0051] Take 30g of chitosan with a particle size of 3mm, a degree of deacetylation of 80%, and a viscosity-average molecular weight of 250,000, add it to an 8L aqueous solution, stir at a speed of 30 rpm to form a suspension, and add 54g of FeCl 3 , 59.4g MnCl 2 , 51.3g Al 2 (SO 4 ) 3 , After stirring evenly, the adsorption and dephosphorization material is obtained by drying by spray drying technology. The spray drying conditions are: inlet air temperature 100°C, outlet air temperature 50°C, drying time 1S, maximum water evaporation 10Kg / h, peristaltic pump feeding 2L / h h, dry air flow 1m 3 / min, spray gas flow 0.2m 3 / h, the nozzle diameter is 3mm, and the dry powder recovery rate is 95%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The present invention provides a method for preparing chitosan phosphorus removal material by spray drying method. The preparation method comprises the following steps: adding chitosan and metal salt into water respectively to make them uniformly dispersed to form a mixed solution; The chitosan phosphorus removal material was prepared by spray drying. The present invention also provides a chitosan phosphorus removal material prepared by the above preparation method. The preparation method of the invention is simple, the process conditions are mild, and the prepared phosphorus removal adsorption material has a large adsorption capacity.

Description

technical field [0001] The invention relates to a preparation method of chitosan phosphorus removal material, chitosan phosphorus removal material and application. Background technique [0002] With the rapid development of industry, the development and utilization of environmental resources by human beings are becoming more and more frequent, resulting in a large amount of sewage and wastewater containing nutrients such as nitrogen and phosphorus. The global natural water pollution situation is not optimistic, and water eutrophication has become an important problem to be solved urgently. Nitrogen and phosphorus are the main causes of water eutrophication, and phosphorus is often regarded as one of the main inducing factors of water eutrophication. Therefore, phosphorus removal from water is of great significance for controlling eutrophication. [0003] At present, various technologies have been used for phosphorus removal in water, such as chemical method, biological met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/24B01J20/30C02F1/28
CPCB01J20/24B01J20/08B01J20/06C02F1/286C02F2101/105C02F2209/18
Inventor 唐利锋袁新兵方佩晖王晓明卢明凤
Owner OCHEMATE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap