Manufacture method for manufacturing straws through natural material

A technology of natural materials and manufacturing methods, applied in the direction of manufacturing tools, wood treatment, impregnated wood, etc., can solve problems such as waste of resources, environmental pollution, etc., and achieve the effects of resource conservation, good flexibility, and environmental protection

Inactive Publication Date: 2019-11-22
张其浩
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the current straws are plastic products. When these straws ar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for manufacturing straws from natural materials, comprising the following steps:

[0025] 1) Select annual reeds, remove the reed leaves on the reed stalks and cut off the reed stalks whose root diameter exceeds 15mm and the upper end is lower than 6mm;

[0026] 2) Cut the cut reed stalks into 25cm segments, use a drill with a diameter of 10mm to get through the middle of the reeds with a minimum diameter of less than 12mm, and use a drill with a diameter of 15mm to cut them into segments and The middle of the reed rod with a minimum diameter greater than 12mm can also be pierced through with 6-point iron wire;

[0027] 3) using a film blade to cut one end of the reed rod obtained in step 2) at a 30° bevel;

[0028] 4) The outer wall is polished with sandpaper to make the outer wall smooth, and the powder that falls off is washed with clean water;

[0029] 5) Use a 360-mesh sandpaper drill on the outer wall to penetrate into the inside of the opened reed rod ...

Embodiment 2

[0039] A method for manufacturing straws from natural materials, comprising the following steps:

[0040] 1) Select annual reeds, remove the reed leaves on the reed stalks and cut off the reed stalks whose root diameter exceeds 15mm and the upper end is lower than 6mm;

[0041] 2) Cut the cut reed stalks into 5-25cm segments, use a drill with a diameter of 5mm to open through the middle of the cut reeds with a minimum diameter of less than 12mm, and use a drill with a diameter of 11.5mm to cut into Segmental reeds with a minimum diameter greater than 12mm can be pierced through the middle, or can be pierced with 6-point iron wire;

[0042] 3) using a film blade to cut one end of the reed rod obtained in step 2) at a 60° bevel;

[0043] 4) The outer wall is polished with sandpaper to make the outer wall smooth, and the powder that falls off is washed with clean water;

[0044] 5) Use a 400-mesh sandpaper drill on the outer wall to penetrate into the inside of the opened reed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a manufacture method for manufacturing straws through a natural material. The manufacture method includes the following steps that firstly, annual reed is selected and used, reed leaves on a reed rod are removed, and the root, with the diameter exceeding 15 mm, and the upper end, with the diameter smaller than 6 mm, of the reed rod are sheared off and removed; secondly, thesheared reed rod is cut off into sections of 5-25 cm; thirdly, one end of each reed rod manufactured in the second step is cut to form an oblique angle of 10-89 degrees through a membrane blade; fourthly, the outer walls are polished through abrasive paper so that the outer walls can be polished smooth; fifthly, abrasive paper of 360 mesh to 600 mesh is used for the outer walls and drills and stretches into the through reed rods to conduct polishing; and sixthly, high-temperature saline water disinfection or high-temperature blow-in disinfection is conducted for 5 minutes, and drying in the sun is conducted. The raw material yield of the straws manufactured through the natural material is large, the manufacture method is easy in manufacture and safe and reliable in usability, the straws can be used in cooperation with stainless steel straws, the reed straws which are abandoned after being used up can be recycled and used for making paper, resources can be saved, and environment protection can be achieved.

Description

technical field [0001] The invention relates to straws, in particular to a method for manufacturing straws with a natural material. Background technique [0002] Suction straw or claims drinking straw, is a cylindrical, hollow plastic product, and its main function is to be used for drinking beverage in the cup, also has the bone marrow that is used to suck the good animal long bone of some cooking. Generally, the diameter is about 0.5cm, but when used to suck drinks such as yogurt and pearl milk tea, thicker straws are used, and some have a diameter of 1.5cm. Some less common, extremely small diameter straws are used for drinking hot beverages. [0003] However, most of the present straws are plastic products. When these straws are used, they are all disposable, which wastes resources and pollutes the environment. Contents of the invention [0004] In order to solve the problems raised in the above-mentioned background technology, the object of the present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27J1/00B27M1/08B27M3/24B24B5/04B27K3/02B27K5/00
CPCB24B5/04B27J1/00B27K3/02B27K5/0085B27M1/08B27M3/24
Inventor 张其浩
Owner 张其浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap