026Cr18Ni12Mo2N stainless steel forging for nuclear power station and manufacturing method thereof

A technology of 026cr18ni12mo2n and a manufacturing method, which is applied in the field of stainless steel forging, can solve the problem that the strength requirements cannot meet the requirements of forgings, etc., and achieve the effect of effectively refining grains and increasing the strength of materials

Active Publication Date: 2019-12-10
无锡市法兰锻造有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength requirements of the existing 026Cr18Ni12Mo2N stainless steel cannot meet the requirements of forgings for nuclear power plants, so it is necessary to develop a high-strength 026Cr18Ni12Mo2N stainless steel forgings to meet the requirements of nuclear power plants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0031] The chemical composition of stainless steel forgings is: C is 0.021%, Si is 0.48%, Mn is 1.82%, P is 0.018%, S is 0.008%, Cr is 17.53%, Ni is 11.82%, Mo is 2.53%, N is 0.07 %, Cu is 0.8%, and the rest is pig iron.

[0032] The stainless steel forging is produced by the manufacturing method of the present invention: the raw material is refined into a stainless steel ingot containing the chemical composition in this embodiment by using an AOD furnace. The obtained stainless steel ingots are made into stainless steel forgings with a hydraulic press. The forging is formed through 3 fire times, the forging ratios of the 3 fire times are 2, 2, 1 respectively, and the heating temperatures of the 3 fire times are 1200°C, 1000°C, 800°C respectively. The riser end of the stainless steel ingot is removed by 18%, and the nozzle end of the stainless steel ingot is removed by 7%. The forged stainless steel forging is heated to 1090°C and held for 3.5 hours, and water is cooled by r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a 026Cr18Ni12Mo2N stainless steel forging for a nuclear power station. The 026Cr18Ni12Mo2N stainless steel forging for nuclear power station comprises the following chemical components: 0.015-0.035% of C, not greater than 1%of Si, not greater than 2% of Mn, not greater than 0.03% of P, not greater than 0.015% of S, 2-18.2% of Cr, 11.6-12.5% of Ni, 2.25-2.75% of Mo, 0.05-0.08% of N, not greater than 1% of Cu, and the balance pig iron. The invention also discloses method of manufacture. The method comprises the steps of refining raw materials; forging: forging the obtained stainless steel ingot into a stainless steel forging, wherein the stainless steel forging is subjected to main deformation at the temperature of 1000 + / -20 DEG C; and heat treatment, namely, heatingthe forged stainless steel forging to 1050-1120 DEG C, preserving heat, and then cooling with water; and detecting. According to the method adopting the abovementioned mode, the content of C and N isincreased in chemical components, the content of Cr and Ni is adjusted, and the strength of the forging is increased in material components. In the aspect of the manufacturing method, the internal stress generated in the finish forging process can also generate static recrystallization in the heat treatment process, so that the material grains are effectively refined, and the refined grains can increase the material strength.

Description

technical field [0001] The invention relates to the technical field of stainless steel forging, in particular to a 026Cr18Ni12Mo2N stainless steel forging for nuclear power plants and a manufacturing method thereof. Background technique [0002] Austenitic stainless steel refers to stainless steel with austenitic structure at room temperature, and 026Cr18Ni12Mo2N stainless steel is one of austenitic stainless steels. When the steel contains about 18% of Cr and 8% to 25% of Ni, it has a stable austenite structure. Austenitic stainless steel is non-magnetic and has high toughness and plasticity, good machinability, but low strength. [0003] The forgings used in nuclear power plants have high requirements on the strength of 026Cr18Ni12Mo2N stainless steel, which needs to have a certain high strength. The strength requirements of the existing 026Cr18Ni12Mo2N stainless steel cannot meet the requirements of forgings used in nuclear power plants, so it is necessary to develop a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/58C22C38/44C22C38/42C21D8/00
CPCC21D8/005C22C38/001C22C38/02C22C38/04C22C38/42C22C38/44C22C38/58
Inventor 李刚亮吴金波石宏亮邹琪邓东袁超
Owner 无锡市法兰锻造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com