Single-coating water-based UV pearlescent silver powder paint and preparation method thereof

A technology of silver powder paint and pearl powder, which is applied in the direction of coating, device for coating liquid on the surface, pretreatment of surface, etc., can solve the problems of complicated and inconvenient spraying process or processing steps, and long processing time, etc. The effect of solving the harm to human health, shortening the baking time and simplifying the construction process

Inactive Publication Date: 2019-12-13
广东涂乐师新材料科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the process of spraying the plastic workpiece with the spray agent obtained by combining the water-based pearlescent silver powder primer and the water-based UV topcoat, it needs to be sprayed at least twice and baked at least twice to achieve the curing effect. The spraying process or processing steps have the disadvantages of being cumbersome and inconvenient, and the time required for processing is long.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-coating water-based UV pearlescent silver powder paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] A single coating water-based UV pearlescent silver paint and a preparation method thereof, a single coating water-based UV pearlescent silver paint and a preparation method thereof, comprising the following components by weight ratio:

[0034] Styrene-acrylic emulsion 60-80%,

[0035] Propylene Glycol 1-5%,

[0036] Hyperbranched polyol 1-5%,

[0037] Water-soluble highly active monomer 4-10%,

[0038] Water-based pearl powder 2-5%,

[0039] Photoinitiator A 1-5%,

[0040] Photoinitiator B 1-5%,

[0041] Leveling agent 0.1-0.5%,

[0042] Defoamer 0.1-0.5%,

[0043] Deionized water 8-12%,

[0044] Water-based anti-silver additive 0.5-2%,

[0045] Water-based thickener 0.1-0.5%.

[0046] In one embodiment, the photoinitiator A is German BASF photoinitiator Irgacure500, and the photoinitiator B is German BASF photoinitiator IRGACURE 2959.

[0047] In one of the embodiments, the leveling agent is BYK-347 leveling agent from Germany.

[0048] In one embodiment, th...

Embodiment 1

[0053] A kind of single coating waterborne UV pearl luster silver powder paint, it comprises following composition by weight ratio:

[0054] Styrene-acrylic emulsion 70%,

[0055] Propylene Glycol 2%,

[0056] hyperbranched polyol 3%,

[0057] Water-soluble highly active monomer 5%,

[0058] Water-based pearl powder (silver) 3%,

[0059] Photoinitiator A 2%,

[0060] Photoinitiator B 4%,

[0061] Leveling agent 0.3%,

[0062] Defoamer 0.4%,

[0063] Deionized water 9%,

[0064] Water-based anti-silver additive 1%,

[0065] Water-based thickener 0.3%.

[0066] In one embodiment, the photoinitiator A is German BASF photoinitiator Irgacure500, and the photoinitiator B is German BASF photoinitiator IRGACURE 2959.

[0067] In one of the embodiments, the leveling agent is BYK-347 leveling agent from Germany.

[0068] In one embodiment, the defoamer is BASF Dehydran 1620 defoamer.

[0069] In one of the embodiments, the water-based anti-sliver additive of Tego AddBOND 1270 ...

Embodiment 2

[0075] A kind of single coating waterborne UV pearl luster silver powder paint, it comprises following composition by weight ratio:

[0076] Styrene-acrylic emulsion 70%,

[0077] Propylene Glycol 3%,

[0078] hyperbranched polyol 3%,

[0079] Water-soluble highly active monomer 7%,

[0080] Water-based pearl powder 4%,

[0081] Photoinitiator A 4%,

[0082] Photoinitiator B 2%,

[0083] Leveling agent 0.4%,

[0084] Defoamer 0.2%,

[0085] Deionized water 11%,

[0086] Water-based anti-silver additive 1.5%,

[0087] Water-based thickener 0.4%.

[0088] In one embodiment, the photoinitiator A is German BASF photoinitiator Irgacure500, and the photoinitiator B is German BASF photoinitiator IRGACURE 2959.

[0089] In one of the embodiments, the leveling agent is BYK-347 leveling agent from Germany.

[0090] In one embodiment, the defoamer is BASF Dehydran 1620 defoamer.

[0091] In one of the embodiments, the water-based anti-sliver additive of Tego AddBOND 1270 is u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to single-coating water-based UV pearlescent silver powder paint and a preparation method thereof. The single-coating water-based UV pearlescent silver powder paint produced by adopting a formula, a weight ratio and the preparation method disclosed by the invention has the advantages that in the construction process of a workpiece, only one-time spraying and one-time baking are needed; the defect that a traditional process of mixing water-based pearlescent silver powder primer with water-based UV finish paint, and construction on workpieces, at least two times of sprayingcoating and at least two times of baking are needed is avoided; the baking time can be shortened to 8-15 minutes, the construction procedure can be simplified, the baking time can be shortened, and the construction efficiency can be improved; in addition, deionized water can be used as a diluent instead of an organic solvent, so that the use amount of the diluent can be greatly reduced, the problem that the use of the organic solvent is harmful to human health is effectively solved, using is more convenient, and the environment protection performance is better.

Description

technical field [0001] The invention relates to a single-coating water-based UV pearlescent silver powder paint and a preparation method thereof. Background technique [0002] Currently used in Huawei, Gionee, VIVO and other brands of electronic product casings and product frames are processed through the combination of water-based pearlescent silver powder primer and water-based UV topcoat. Because the water-based pearlescent silver powder primer has good decoration And protection, so that it can make pure metal effect and metal effect with various colors, so that its market prospect is very broad. [0003] However, as the environmental protection situation becomes increasingly severe, the environmental protection requirements for coatings will also expand. The use of water-based pearlescent silver powder primers and water-based UV topcoats on the market both emit a large amount of VOC, and the current water-based pearlescent paints on the market The combined use of silver...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D5/36C09D7/20C09D7/40C09D7/43B05D1/02B05D3/02B05D3/06B05D7/24B05D3/10
CPCB05D1/02B05D3/0254B05D3/067B05D3/10B05D3/101B05D7/24C09D4/06C09D5/36C09D7/20C09D7/40C09D7/43
Inventor 陈建平刘妍霞朱金辉
Owner 广东涂乐师新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap