High-elongation automobile axle housing steel for cold stamping, and production method thereof

A high-elongation, cold-stamping technology, applied in the metal field, can solve problems such as non-compliant and difficult-to-form auto parts, and achieve cost-saving effects

Inactive Publication Date: 2020-01-10
ANGANG STEEL CO LTD
View PDF13 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The Chinese patent application with the publication number CN 106480367A discloses a production method of high-strength cold-formed automobile axle housing steel, which is designed by adding a certain amount of niobium, vanadium and titanium through the carbon and manganese elements of the common C-M

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-elongation automobile axle housing steel for cold stamping, and production method thereof
  • High-elongation automobile axle housing steel for cold stamping, and production method thereof
  • High-elongation automobile axle housing steel for cold stamping, and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] Below by embodiment the present invention will be further described.

[0032] In the embodiment of the present invention, smelting, continuous casting, reheating, rolling, cooling, and crimping are carried out according to the component ratio of the technical solution. The composition of the steel of the embodiment of the present invention is shown in Table 1. The technical parameters of the rolling temperature of the steel of the embodiment of the present invention are shown in Table 2. See Table 3 for the rolling schedule of each pass of steel rolling in the embodiment of the present invention. The mechanical properties of the steel of the embodiment of the present invention are shown in Table 4. The steel microstructure of the embodiment of the present invention is shown in Table 5.

[0033] Table 1 Composition (wt %) of the embodiment steel of the present invention

[0034] Example C Si mn P S Al V Cr 1 0.14 0.054 1.45 0.007 0.003 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides high-elongation automobile axle housing steel for cold stamping, and a production method thereof. The automobile axle housing steel comprises the following components in percentage by weight: 0.14%-0.17% of C, 0.020%-0.080% of Si, 1.25%-1.65% of Mn, 0.010%-0.065% of Al, 0.025%-0.065% of V, 0.15%-0.25% of Cr, not greater than 0.020% of P, not greater than 0.006% of S, and thebalance Fe and inevitable impurities. The production method comprises the steps of smelting, continuous casting, heating, rolling, cooling and coiling. The steel has high elongation under the tensilestrength of 470MPa, and the elongation A is not less than 40%; and integral forming of stamping can be realized by applying the steel plate, no welding is achieved, and the cost is saved.

Description

technical field [0001] The invention belongs to the field of metals, in particular to a high-elongation automobile axle housing steel for cold stamping and a production method thereof. Background technique [0002] The automobile axle housing is one of the main components of the automobile driving system. It supports the weight of the frame and the rear parts of the frame, and at the same time it protects the components in the transmission system. In the manufacturing field of the axle housing industry, there are two completely different product manufacturing methods: stamping and welding axle housings and casting axle housings. With the development of axle housing manufacturing technology and the need for automobile weight reduction and energy saving, especially for truck driven axle housings, hot-rolled steel plates with a thickness of 12 to 16 mm have been used to make stamped and welded axle housings, replacing the complex manufacturing process and production Inefficien...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/24C22C38/38C21D8/02
CPCC21D8/0226C21D2211/005C21D2211/009C22C38/02C22C38/04C22C38/06C22C38/24C22C38/38
Inventor 孙成钱董毅时晓光刘仁东张宇徐荣杰王俊雄韩楚菲王进臣
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap