A color-changing enamel processing method applied to metal surfaces

A processing method and metal surface technology, applied in the field of color-changing enamel processing, can solve problems such as surface bursting, and achieve the effect of improving the yield rate

Active Publication Date: 2022-02-11
SHENZHEN BAOFU JEWELRY CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is that, aiming at the defects of the prior art, the present invention provides a color-changing enamel processing method applied to the metal surface, by increasing the adhesion between the enamel glaze and the metal surface, and performing multiple filling and baking Make the enamel gradually shape and release the internal stress, aiming to solve the problem of surface cracking when the enamel pigment in the prior art is directly applied to different metals, so as to improve the yield rate of the color-changing enamel in the mass production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A color-changing enamel processing method applied to metal surfaces
  • A color-changing enamel processing method applied to metal surfaces

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] In order to make the objects, technical solutions and advantages of the present invention, the present invention will be described in detail below with reference to the accompanying drawings. It is to be understood that the specific embodiments described herein are intended to explain the present invention and is not intended to limit the invention.

[0034] like figure 1 , figure 2 As shown, a variable coloration process for applying to metal surfaces, including the steps:

[0035] Step S100, pattern grooves of the surface of the metal embryo body are produced.

[0036] DETAILED DESCRIPTION OF THE INVENTION During the metal surface, the glaze is carried out, and it is necessary to make the corresponding groove in the surface of the metal embryo body, and the groove is attached to the enamel glaze. The metal in this embodiment is precious metal, especially gold and silver platinum, etc.

[0037] The step S100 specifically includes the following steps:

[0038] Step S110, pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Mohs hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a color-changing enamel processing method applied to a metal surface. The steps include: making a pattern groove on the surface of a metal body; 10‑14wt%, phosphorus 8‑12wt%, organic pigment 20‑30wt%, binder 20‑30wt% mixed to make enamel glaze powder; add thermosensitive coloring material and color filler required by the product into the enamel glaze powder and adjust Forming enamel paste; the metal embryo body pattern grooves are filled with enamel paste many times and baked for many times until the enamel completely fills the precious gold embryo body grooves. The invention promotes the release of the concentrated internal stress of the enamel glaze during the molding process through multiple fillings and baking and cooling, and realizes a simple production process through the step-by-step attachment of the enamel, so that the enamel glaze is not easy to appear after cooling Detachment due to cracks or production sandwiched layers.

Description

Technical field [0001] The present invention relates to the field of 珐 handicrafts, and more particularly to a discoloration processing method applied to a metal surface. Background technique [0002] The existing enamel products are used in glass products, ceramic products, and enamel will be pulverized to ground glaze, apply to glass products after processes, after the surface of ceramics, dry, burna, etc. The resulting composite handicraft. [0003] The composition of the glaze mainly includes raw materials such as quartz, pulp, boron sand, fluorine, etc., and is added to a powder shape, and then bold into a mixture of silicic acid compounds. [0004] The difference between the metal color material and the quartz high melting point of silica as the main ingredient, the difference in expansion coefficients between the ceramic articles, can be completely attached to the glass, the ceramic product surface after direct firing, showing a bright color However, when the conventional ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23D5/06C23D5/02C23D7/00C03C8/00
CPCC23D5/06C23D5/02C23D7/00C03C8/00C03C2207/10
Inventor 薛焜
Owner SHENZHEN BAOFU JEWELRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products