A kind of preparation technology of non-dyeing regenerated polyester staple fiber

A preparation process, technology of recycled polyester, applied in the direction of fiber treatment, fiber type, fiber chemical characteristics, etc., can solve the problems of poor dyeing effect, uneven dispersion, agglomeration and other problems of colored polyester fiber, achieve good dyeing effect, uniform dispersion, prevent The effect of mutual reunion

Active Publication Date: 2022-05-03
HANGZHOU BENMA CHEMFIBER & SPINNING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to improper selection of existing pigments and dispersants, the pigments will be agglomerated and unevenly dispersed when they are dissolved in molten polyester in a molten state, resulting in poor dyeing effect of colored polyester fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of non-dyeing regenerated polyester staple fiber
  • A kind of preparation technology of non-dyeing regenerated polyester staple fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] refer to figure 1 , a preparation process of non-dyed regenerated polyester staple fiber, the bottle flakes are subjected to the following steps:

[0041] S1: Raw material preparation. The bottle flakes of the recovered mineral water bottles are repeatedly cleaned, sterilized, and then cut and crushed.

[0042] S2: pre-processing. Sorting the materials after S1 treatment, and then put the materials into the rotary drum vacuum dryer. After the feeding is completed, start to heat up in the drum at a rate of 1.5°C / min, and heat up to 60°C for heat preservation. After that, heat transfer oil is introduced and the drum is started at the same time. At the same time, start the vacuum pump to evacuate the drum, and keep the vacuum at 70Pa, the drying time is 10h, and the moisture content of the bottle flakes is controlled below 0.01%.

[0043] S3: heating and melting.

[0044] First prepare the masterbatch. Put the raw materials of the masterbatch into the slurry tank in no...

Embodiment 24

[0071] Embodiment 24: The difference from Example 1 is that in the step of S6 oiling, the chemical composition of the oil agent is 33 parts by weight of stearylamine polyoxyethylene ether, 32 parts of lauryl alcohol and aminopropanol kojic acid phosphoric acid 51 parts of ester.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the manufacturing field of regenerated chemical fibers, and discloses a preparation process of non-dyed regenerated polyester staple fibers. The bottle flakes are subjected to the following steps: S1: raw material preparation; S2: pretreatment; S3: heating and melting; after S2 The treated material is mixed with the color masterbatch, and then heated and melted together; the raw materials of the color masterbatch include in parts by weight: 70-90 parts of dimethyl terephthalate, 20-40 parts of propylene glycol, 120-150 parts of pigment part and 110-130 parts of dispersant; said dispersant includes polyethylene wax and cetyltrimethylammonium bromide, and the mass ratio of the two is 4:1; S4: spinning; S5: cooling molding; S6: oiling; S7: winding and bundling; S8: crimping and cutting; non-dyed and regenerated polyester staple fibers are obtained after the above steps. It can prevent the agglomeration of the pigment when it is dissolved in the molten polyester in the molten state, so that the pigment can be dispersed evenly, and finally the dyed colored polyester has a better dyeing effect.

Description

technical field [0001] The invention relates to the field of manufacturing regenerated chemical fibers, more specifically, it relates to a preparation process of non-dyed regenerated polyester staple fibers. Background technique [0002] Regenerated polyester staple fiber refers to the use of polyester cloth, waste polyester bottle flakes, spinning waste, foam material, pulp, etc. as raw materials. The waste and old bottle flakes are crushed, cleaned, mixed with various materials, and then dried. Melt extrusion, spinning, winding, bundling, drawing, crimping, relaxation heat setting, and cutting to form polyester staple fibers of different lengths. The use of recycled polyester can improve the current shortage of textile raw materials in my country, and the processing method of waste utilization is in line with the concept of environmental protection. [0003] At present, there are two main types of dyeing methods for polyester fiber textiles. One is to weave polyester fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/04D01F1/10D01F11/08C08G63/183D06M15/53D06M13/144D06M13/453D06M13/463D06M15/643D06M101/32
CPCD01F6/92D01F1/04D01F1/10D01F11/08C08G63/183D06M15/53D06M13/144D06M13/453D06M13/463D06M15/643D06M2101/32
Inventor 许国良
Owner HANGZHOU BENMA CHEMFIBER & SPINNING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap