A kind of thermosetting phenolic resin cutting wheel and preparation method thereof

A technology for cutting grinding wheels and phenolic resin, which is applied in the direction of bonding grinding wheels, manufacturing tools, and metal processing equipment. The effect of sharpness

Active Publication Date: 2021-04-13
郑州九天工贸有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the process of cutting metal by the grinding wheel, in order to increase the abrasion and lubrication of the grinding wheel and reduce the wear of the grinding wheel, pyrite is generally added to the raw material of the grinding wheel. The main component of pyrite is iron disulfide, adding disulfide Although iron can reduce the wear of the grinding wheel, iron disulfide is easily oxidized by oxygen in the air to produce sulfur dioxide and ferric oxide. Sulfur dioxide meets water to form sulfurous acid. Burrs and other phenomena appear on the section, and at the same time, the ferric oxide is separated from the grinding wheel and falls down, making the grinding wheel form pores and reducing the sharpness of the grinding wheel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thermosetting phenolic resin cutting wheel and preparation method thereof
  • A kind of thermosetting phenolic resin cutting wheel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A thermosetting phenolic resin cutting wheel, its raw material ratio is shown in Table 1.

[0046] S1. Raw material A ingredients

[0047] Under the condition of constant stirring, mix microcrystalline corundum and brown corundum evenly, then add cryolite, manganese aluminum spinel, boron carbide, silicon dioxide superfine powder, alumina superfine powder, gypsum, mix well, and then Add a wetting agent and mix evenly to obtain raw material A;

[0048] Among them, Al in microcrystalline corundum 2 o 3 The weight content of the microcrystalline corundum is 95.5%, and the gradation of microcrystalline corundum is: 15-10mm 4kg, 10-8mm 9kg, 8-5mm 5kg; Al in brown corundum 2 o 3 The weight content of brown corundum is 95%, and the gradation of brown corundum is: 10-8mm 8kg, 8-5mm 16kg, 5-3mm 22kg, 3mm-0mm 9kg; Na in cryolite 3 AlF 6 The weight content is 97%, the particle size is less than or equal to 0.074mm; MnAl in manganese aluminum spinel 2 o 4 The weight content...

Embodiment 2

[0056] A thermosetting phenolic resin cutting wheel, its raw material ratio is shown in Table 1.

[0057] S1. Raw material A ingredients

[0058] Under the condition of constant stirring, mix microcrystalline corundum and brown corundum evenly, then add cryolite, manganese aluminum spinel, boron carbide, silicon dioxide superfine powder, alumina superfine powder, gypsum, mix well, and then Add a wetting agent and mix evenly to obtain raw material A;

[0059] Among them, Al in microcrystalline corundum 2 o 3 The weight content of the microcrystalline corundum is 95.5%, and the gradation of microcrystalline corundum is: 15-10mm 5kg, 10-8mm 13kg, 8-5mm 7kg; Al in brown corundum 2 o 3 The weight content of brown corundum is 95%, and the gradation of brown corundum is: 10-8mm 6kg, 8-5mm 14kg, 5-3mm 18kg, 3mm-0mm 7kg; Na in cryolite 3 AlF 6 The weight content is 97%, the particle size is less than or equal to 0.074mm; MnAl in manganese aluminum spinel 2 o 4 The weight conten...

Embodiment 3

[0068] A thermosetting phenolic resin cutting wheel, its raw material ratio is shown in Table 1.

[0069] S1. Raw material A ingredients

[0070] Under the condition of constant stirring, mix microcrystalline corundum and brown corundum evenly, then add cryolite, manganese aluminum spinel, boron carbide, silicon dioxide superfine powder, alumina superfine powder, gypsum, mix well, and then Add a wetting agent and mix evenly to obtain raw material A;

[0071] Among them, Al in microcrystalline corundum 2 o 3 The weight content of the microcrystalline corundum is 95.5%, and the gradation of microcrystalline corundum is: 15-10mm 4kg, 10-8mm 10kg, 8-5mm 6kg; Al in brown corundum 2 o 3 The weight content of brown corundum is 95%, and the gradation of brown corundum is: 10-8mm 8kg, 8-5mm 16kg, 5-3mm 21kg, 3mm-0mm 8kg; Na in cryolite 3 AlF 6 The weight content is 97%, the particle size is less than or equal to 0.074mm; MnAl in manganese aluminum spinel 2 o 4 The weight conten...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a thermosetting phenolic resin cutting grinding wheel and a preparation method thereof, belonging to the technical field of cutting grinding wheel production. The cutting grinding wheel includes a grinding body and a reinforcing mesh embedded in the grinding body. In terms of weight percentage, the raw materials of the grinding body include Raw material A, raw material B; raw material A includes microcrystalline corundum, brown corundum, cryolite, manganese aluminum spinel, boron carbide, ultrafine powder, gypsum, wetting agent; raw material B is thermosetting phenolic resin powder, thermosetting phenolic resin powder The addition amount is 20-30% of raw material A gross weight. The cutting grinding wheel, through the synergy between the raw materials, enables the cutting grinding wheel to have higher sharpness and grinding efficiency, and also has higher gyration strength, which improves the service life of the cutting grinding wheel. The preparation method of the cutting grinding wheel not only makes the preparation of the cutting grinding wheel stable, but also increases the bonding strength between raw materials and improves the use effect of the cutting grinding wheel.

Description

technical field [0001] The invention relates to the technical field of cutting grinding wheel production, more specifically, it relates to a thermosetting phenolic resin cutting grinding wheel and a preparation method thereof. Background technique [0002] Grinding wheel is the main tool for grinding. It is a porous substance composed of abrasives, fillers, and binders. It is widely used in metallurgy, construction, railways and other fields. It is mainly used for cutting and grinding steel pipes, shaped pipes, and steel bars. At present, in the process of cutting metal with the grinding wheel, in order to increase the abrasion and lubrication of the grinding wheel and reduce the wear of the grinding wheel, pyrite is generally added to the raw material of the grinding wheel. The main component of pyrite is iron disulfide, adding disulfide Although iron can reduce the wear of grinding wheels, iron disulfide is easily oxidized by oxygen in the air to produce sulfur dioxide and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D5/12B24D5/10B24D3/28B24D3/34B24D18/00
CPCB24D3/285B24D3/344B24D5/10B24D5/12B24D18/0009
Inventor 李蒙
Owner 郑州九天工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More