Polypropylene composite material with obvious pearlescent effect and its preparation method and application

A composite material, pearlescent effect technology, applied in the field of polypropylene modification, to achieve the effect of large aspect ratio, improved scratch resistance, improved rigidity and hardness

Active Publication Date: 2022-03-11
WANHUA CHEMICAL (NINGBO) CO LTD +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide a high-hardness and low-shrinkage polypropylene composite material with obvious pearlescent effect that can replace ABS and its preparation method, so as to solve the bottleneck of the application of existing polypropylene materials in replacing spray-free ABS materials, and can On the existing ABS mold, the polypropylene material with high hardness, low shrinkage and obvious pearlescent effect can be realized, which can be applied to many fields such as small household appliances, electronic and electrical shells, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composite material with obvious pearlescent effect and its preparation method and application
  • Polypropylene composite material with obvious pearlescent effect and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] (1) Preparation of glass fiber-based pearlescent pigments: put 100kg of chopped glass fibers into the first high-temperature furnace at 1250°C for melting, set a 14um aperture spinneret tray at the bottom of the melting furnace, open the spinneret tray, and melt the glass The fiber filaments are sprayed out and passed through the second high-temperature melting furnace at 650°C under the traction of the wire rack in the horizontal direction. A stirring paddle is set at the bottom of the high-temperature furnace, and 2.3kg of titanium dioxide and 0.25kg of pure zinc are melted and dispersed, and the titanium dioxide and metallic zinc are uniform It is dip-coated on the smooth glass fiber surface, and cut into 3-5mm fiber segments by a shredder under the traction of the wire separator, and finally obtains a glass fiber-based pearlescent pigment with a coating rate of 70%.

[0042] (2) Preparation of polypropylene composite material: Weigh 7.2kg of high stiffness copolymer ...

Embodiment 2

[0044] (1) Preparation of glass fiber-based pearlescent pigments: put 100kg of chopped glass fibers into the first high-temperature furnace at 1250°C for melting, set a 14um aperture spinneret tray at the bottom of the melting furnace, open the spinneret tray, and melt the glass The fiber filaments are sprayed out and passed through the second high-temperature melting furnace at 700°C under the traction of the wire rack in the horizontal direction. Stirring paddles are installed at the bottom of the high-temperature furnace to melt and disperse 3.3kg of titanium dioxide and 1.7kg of pure zinc, and the titanium dioxide and metal zinc are uniform It is dip-coated on the smooth glass fiber surface, and cut into 3-5mm fiber segments by a shredder under the traction of the wire separator, and finally obtains a glass fiber-based pearlescent pigment with a coating rate of 85%.

[0045] (2) Preparation of polypropylene composite material: Weigh 7.0kg homopolypropylene PPH-PP6012, 0.45k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
melt flow indexaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypropylene composite material with obvious pearlescent effect, its preparation method and application. The polypropylene composite material includes the following components: polypropylene, glass fiber-based pearlescent pigment, compatibilizer, dispersant, and antioxidant. The low-shrinkage polypropylene material with pearlescent effect in the present invention can obtain a low-shrinkage polypropylene material with obvious pearlescent effect, Rockwell hardness above 105, and shrinkage rate below 0.5% by adding a certain proportion of glass fiber-based pearlescent pigments. On the existing ABS mold, it directly replaces the ABS material with spray-free pearlescent effect, and is widely used in automobiles, small household appliances, toys and other industries.

Description

technical field [0001] The invention relates to a polypropylene composite material, in particular to a high-hardness and low-shrinkage polypropylene composite material with obvious pearlescent effect that can replace ABS, a preparation method and application thereof, and belongs to the technical field of polypropylene modification. Background technique [0002] As a general-purpose plastic, polypropylene has the advantages of low price and good weather resistance, and is widely used in automobiles, home appliances, office supplies and various electronic appliances. With the demand of downstream customers for PP to replace ABS materials, especially in some downstream applications that require pearlescent effect, such as small household appliance casings, electronic appliance casings and other products, higher requirements are put forward for PP materials, such as high hardness, durability Scratch free, low shrinkage and has a clear pearlescent effect. PP materials have probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08L23/12C08L51/06C08K9/10C08K7/14
CPCC08L23/14C08L23/12C08L51/06C08K9/10C08K7/14
Inventor 顾永江付懿东李旭陆佳伟
Owner WANHUA CHEMICAL (NINGBO) CO LTD