Production process of double-layer knitted fabric with comfortable stretch yarn self-fuzzing effect

A knitted fabric and production process technology, applied in knitting, weft knitting, warp knitting and other directions, can solve the problems of damaged fiber state, fiber susceptibility to damage, increased processes, etc., to avoid fiber damage and to achieve dense fleece effect. Overall, the effect of low production cost

Active Publication Date: 2020-04-17
GUANGDONG SMART TEAM TEXTILES TECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Shu elastic silk fabric belongs to elastic fabric, in the process of preparation of Shu elastic silk fabric, needs to carry out a layer of fluff through fleece processing, although the fleece processing technology of this fleece processing in the prior art can achieve the fluffing effect, there is The process increases, and the fibers are easily damaged, which affects the strength of the fabric.
[0003] Moreover, this fleece process of the prior art, because the claws of the fleece machine are used to snatch the fibers and raise the fleece, it will damage the original state of the fibers, and it is easy to damage the yarn during the fleece process. The thread will be fatally damaged, causing holes in the fabric, and the fleece effect is not dense enough, and it is easy to shed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A production process of a double-layer knitted fabric with a self-raising effect of elastic silk, which comprises the following steps:

[0025] Step 1, fiber selection: select cotton fiber, nylon filament and sorona fiber as raw materials;

[0026] Step 2, spinning: the yarn spun from cotton fiber is used as the upper thread, the yarn spun from nylon filament is used as the middle construction thread, and the yarn spun from sorona fiber is used as the bottom thread;

[0027] Step 3. Weaving: Weave the upper thread, middle construction thread and bottom thread obtained in step 2 by placing an order, placing an order, and using filaments in the middle to weave through a double-layer cloth weaving method to obtain a fabric; among them, the weaving needle row The method is double-sided needle;

[0028] Step 4, Determining the Embryo: Determining the fabric obtained in Step 3 at 195°C;

[0029] Step 5. Dyeing: Using an air-flow dyeing machine, first dye the sorona fiber of...

Embodiment 2

[0033] A production process of a double-layer knitted fabric with a self-raising effect of elastic silk, which comprises the following steps:

[0034] Step 1, fiber selection: select cotton fiber, nylon filament and sorona fiber as raw materials;

[0035] Step 2, spinning: the yarn spun from cotton fiber is used as the upper thread, the yarn spun from nylon filament is used as the middle construction thread, and the yarn spun from sorona fiber is used as the bottom thread;

[0036] Step 3. Weaving: Weave the upper thread, middle construction thread and bottom thread obtained in step 2 by placing an order, placing an order, and using filaments in the middle to weave through a double-layer cloth weaving method to obtain a fabric; among them, the weaving needle row The method is double-sided needle;

[0037] Step 4, Determining the Embryo: Determining the fabric obtained in Step 3 at 190°C;

[0038] Step 5. Dyeing: Using an air-flow dyeing machine, first dye the sorona fiber of...

Embodiment 3

[0042] A production process of a double-layer knitted fabric with a self-raising effect of elastic silk, which comprises the following steps:

[0043] Step 1, fiber selection: select cotton fiber, nylon filament and sorona fiber as raw materials;

[0044] Step 2, spinning: the yarn spun from cotton fiber is used as the upper thread, the yarn spun from nylon filament is used as the middle construction thread, and the yarn spun from sorona fiber is used as the bottom thread;

[0045] Step 3. Weaving: Weave the upper thread, middle construction thread and bottom thread obtained in step 2 by placing an order, placing an order, and using filaments in the middle to weave through a double-layer cloth weaving method to obtain a fabric; among them, the weaving needle row The method is double-sided needle;

[0046] Step 4, Determining the Embryo: Determining the fabric obtained in Step 3 at 200°C;

[0047] Step 5. Dyeing: Using an air-flow dyeing machine, first dye the sorona fiber of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of textiles, in particular to a production process of a double-layer knitted fabric with a comfortable stretch yarn self-fuzzing effect. According to the production process of the double-layer knitted fabric with the comfortable stretch yarn self-fuzzing effect, the sorona fiber spun yarns are used as the bottom surface of the base yarn woven fabric, dyeing is performed under the action of temperature and disperse dye in the dyeing process, the sorona fibers emerge from the bottom surface, a layer of fluff is formed on the surface of the fabric, andthe effect of fuzzing process is achieved without the fleece treatment so that one more processing procedure is avoided, one time of damage to the fibers is avoided, the strength of the fabric is notdamaged, and the fleece effect is more compact and neater than the fleece effect of the fleece process in the prior art and fluff is not liable to fall off. In addition, the phenomena in the prior art tta the fibers are damaged by the fleece process and holes are formed in the fabric can be avoided by using the sorona fiber fleece effect.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a production process of a double-layer knitted fabric with a self-fluffing effect of elastic silk. Background technique [0002] Shu elastic silk fabric belongs to elastic fabric, in the process of preparation of Shu elastic silk fabric, needs to carry out a layer of fluff through fleece processing, although the fleece processing technology of this fleece processing in the prior art can achieve the fluffing effect, there is The process increases, and the fibers are easily damaged, which affects the strength of the fabric. [0003] Moreover, this fleece process of the prior art, because the claws of the fleece machine are used to snatch the fibers and raise the fleece, it will damage the original state of the fibers, and it is easy to damage the yarn during the fleece process. The thread is fatally damaged, causing holes in the fabric, and the fleece effect is not dense enough, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04B1/14D04B1/16D04B21/00D06P3/82D06P1/16D06C7/02D06C13/00
CPCD04B1/14D04B1/16D04B21/00D06C7/02D06C13/00D06P1/16D06P3/8204
Inventor 奚斌刘小华
Owner GUANGDONG SMART TEAM TEXTILES TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com