Machining technology for fusing wood into resin

Abstract

The invention discloses a machining technology for fusing wood into resin. In order to overcome the defects in the prior art, the machining technology for fusing the wood into the resin is provided. The machining technology includes the following steps that S1, production equipment and raw materials are prepared; S2, the resin and a curing agent are poured into a container according to the proportion of 3:1, a glass bar is used for stirring the mixture, the mixture is poured into a designated container or die in a non-drawing shape, the mixture is solidified into a solid (solid or liquid pigments, gold powder, silver powder, luminous powder, pearl powder, rosewood flour, cracked cobblestones and the like can be added according to needs) after drying is conducted by 48 h, after solidification is conducted for a certain time period, an oil painting brush, an egg beater and the like can be used for making different fine art pictures; and S3, after the second step is completed, the formedsolid material is taken out from the die for surface cleaning, and the cleaning manner includes the first cleaning manner that die forming is directly conducted, only surface layer treatment, polishing, waxing or direct oily material (wax oil) spraying or oil paint spraying are needed, and the effect of the smooth surface is achieved.

Description

technical field [0001] The invention relates to the technical field of resin-melted wood processing, in particular to a resin-melted wood processing technology. Background technique [0002] Resin usually refers to a softening or melting range after being heated. When softening, it has a tendency to flow under the action of an external force. It is solid, semi-solid, and sometimes liquid organic polymers at room temperature. It is broadly defined and can be used as raw materials for plastic products. Any high molecular compound is called resin, its relative molecular weight is uncertain but usually high, it is solid, medium solid, pseudo solid at room temperature, sometimes it can be liquid organic substance, it has a softening or melting temperature range, and it is under the action of external force It has a tendency to flow and is often shell-shaped when broken. In a broad sense, it refers to polymers or prepolymers used as plastic substrates. They are generally insoluble...

AI Technical Summary

Problems solved by technology

[0003] Although resins in the prior art are widely used, their development in terms of creativity is not perfect enough. The main reason is that the additives are difficult to control and the process is relatively complicated.