Antibacterial thermal fabric and preparation method thereof

A technology for fabrics and fabrics, applied in the field of textile threads, can solve the problems of easy pilling, insufficient dyeing, and increased end breakage rate of fabrics, achieve high-strength antibacterial and thermal properties, speed up the penetration time of fabrics, good air permeability and comfort sexual effect

Active Publication Date: 2020-05-05
YANCHENG SILIDE COCOON SILK
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of exhaust dyeing, in order to ensure that the dyestuffs fully enter the fabric fibers, a long soaking time is required, and the dyeing efficiency is low. The existing method of stirring, pounding or shaking the fabrics is often used to promote the dyeing efficiency, which is easy to cause damage to the fabric fibers. damage, increase the rate of broken ends, and cause the fabric to be prone to pilling; dyeing the fabric by dip-dyeing may also cause poor dyeing uniformity of the fabric, and for large-scale fabric dyeing, it is necessary to dye the fabric section by section. There may be insufficient dyeing or color difference at the junction of the dyeing area, which will affect the dyeing effect; in addition, during the dyeing process of the fabric, the dye particles are easy to precipitate, which may cause uneven dyeing of the fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial thermal fabric and preparation method thereof
  • Antibacterial thermal fabric and preparation method thereof
  • Antibacterial thermal fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] An antibacterial and warm-keeping fabric, comprising the following components in parts by weight: 30 parts of bamboo fiber, 20 parts of Kapron copper ion fiber, 30 parts of cotton fiber, 30 parts of kapok fiber, 15 parts of silk goose down, and 15 parts of heating fiber;

[0051] Said heating fiber adopts salam.

[0052] The preparation method of above-mentioned antibacterial warm fabric comprises the steps:

[0053] (i) Preparation of fabric 1: Spin silk thread after cotton fiber and silk goose down fiber are evenly mixed to obtain silk thread A, get 20 parts of bamboo fiber and all kapok fibers and mix evenly and spin into silk thread to obtain silk thread B; After the silk thread A and the silk thread B are sterilized, the silk thread A is used as the core, and the silk thread B is spirally wound on the silk thread A to obtain a primary functional silk thread, and the primary functional silk thread is woven into a fabric to obtain a fabric 1;

[0054] (ii) preparati...

Embodiment 2

[0066] An antibacterial and warm-keeping fabric, comprising the following components in parts by weight: 33 parts of bamboo fiber, 17 parts of Kapron copper ion fiber, 34 parts of cotton fiber, 28 parts of kapok fiber, 14 parts of silk goose down, and 14 parts of heating fiber;

[0067] The above-mentioned heating fiber adopts Meiyabi.

[0068] The preparation method of above-mentioned antibacterial warm fabric comprises the steps:

[0069] (i) Preparation of fabric 1: Spin silk thread after cotton fiber and silk goose down fiber are evenly mixed to obtain silk thread A, get 22 parts of bamboo fiber and all kapok fibers and mix evenly and spin into silk thread to obtain silk thread B; After the silk thread A and the silk thread B are sterilized, the silk thread A is used as the core, and the silk thread B is spirally wound on the silk thread A to obtain a primary functional silk thread, and the primary functional silk thread is woven into a fabric to obtain a fabric 1;

[007...

Embodiment 3

[0076] An antibacterial and warm-keeping fabric, comprising the following components in parts by weight: 36 parts of bamboo fiber, 15 parts of Kapron copper ion fiber, 37 parts of cotton fiber, 25 parts of kapok fiber, 13 parts of silk goose down, and 13 parts of heating fiber;

[0077] Said heating fiber adopts salam.

[0078] The preparation method of above-mentioned antibacterial warm fabric comprises the steps:

[0079] (i) Preparation of fabric 1: Spin silk thread after cotton fiber and silk goose down fiber are evenly mixed to obtain silk thread A, get 24 parts of bamboo fiber and all kapok fibers and mix uniformly and spin into silk thread to obtain silk thread B; After the silk thread A and the silk thread B are sterilized, the silk thread A is used as the core, and the silk thread B is spirally wound on the silk thread A to obtain a primary functional silk thread, and the primary functional silk thread is woven into a fabric to obtain a fabric 1;

[0080] (ii) prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antibacterial thermal fabric and a preparation method thereof, and belongs to the technical field of textile silk yarns. The fabric comprises the following components (by weight): 30 to 45 parts of bamboo fiber, 10 to 20 parts of Coppron copper ion fibers, 30 to 45 parts of cotton fibers, 20 to 30 parts of kapok fibers, 10 to 15 parts of filament goose down, and 10 to 15parts of thermal fibers. The preparation method comprises the following steps: firstly, blending the cotton fibers and the filament goose down fibers into silk yarns A; blending kapok fibers and partof bamboo fibers into silk yarns B; twisting the two kinds of silk yarn together to be woven into a first fabric, then blending the Coppron copper ion fibers and the remaining bamboo fibers into silkyarns C, weaving the silk yarns C and the thermal fibers into a second fabric, then bonding the two kinds of fabric together to obtain a gray fabric, and then dyeing the gray fabric and shaping. Theantibacterial thermal fabric prepared according to the preparation method provided by the invention has efficient antibacterial thermal performance, and is relatively good in air permeability and comfort.

Description

technical field [0001] The invention relates to the technical field of textile threads, in particular to an antibacterial and warm-keeping fabric and a preparation method thereof. Background technique [0002] Today's textile fabrics have highly embodied the characteristics of novelty, compounding, diversification, and functionalization of products, and there is a huge demand for high-performance, high-value-added, and special-function clothing, apparel, and home textile fabrics. In recent years, functional textile products have developed rapidly internationally. In addition to common functional products such as waterproof, oil-proof, anti-fouling, and flame-retardant, functional products such as anti-ultraviolet, far-infrared warmth, antibacterial, and negative ions have also come out one after another. People enrich the textile market, more to meet people's different uses and special consumption needs. Generally, if the textiles are made of pure wool, most of them are ver...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/02B32B9/04B32B9/00B32B27/02B32B27/12B32B27/30B32B37/02D06B3/10D06B3/32D06B15/00D06B23/04D06B23/20
CPCB32B5/024B32B5/08B32B5/26B32B37/02B32B2262/0223B32B2262/062B32B2262/065B32B2262/08B32B2262/14B32B2307/304B32B2307/7145B32B2307/724D06B3/10D06B3/32D06B15/00D06B15/005D06B23/04D06B23/20
Inventor 苏少林钱飞苏志龙
Owner YANCHENG SILIDE COCOON SILK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap