Anti-static dust-sticking pad and preparation method thereof

An anti-static and dust mat technology, which is applied in the field of sticky mats, can solve the problems of reducing the effect of sticking dust, achieve the effects of reducing firmness, improving the effect of sticking dust, and low production cost

Inactive Publication Date: 2020-05-08
东莞市尼的科技股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing sticky mats are multi-layer PE rubber-coated mats. For general dust, the dust sticking effect is better, but for dust with static electricity, it firmly adheres to the sole / wheel, and the dust sticking effect is greatly reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static dust-sticking pad and preparation method thereof
  • Anti-static dust-sticking pad and preparation method thereof
  • Anti-static dust-sticking pad and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] An antistatic sticky dust mat, comprising a sticky dust mat body, the surface of the sticky dust mat body is distributed with several nano-scale suction holes; the anti-static sticky dust mat is prepared from component A and nano-scale suction hole generating liquid As, the component A includes the following raw materials in parts by weight:

[0039]

[0040] The organic silica gel is methyl vinyl silicone rubber; the hydrogen-containing silicone oil is hydrogen-containing silicone oil with hydrogen-carrying side chains.

[0041] The cross-linking agent is formed by mixing ethyl orthosilicate and dicumyl peroxide at a weight ratio of 5:1; the cross-linking accelerator is dibutyltin dilaurate.

[0042] The nano-material powder is nano-alumina powder; the particle size of the nano-material powder is 10nm.

[0043] The specific surface area of ​​the white carbon black is 200m 2 / g; the white carbon black is a modified white carbon black that has been soaked in a coupl...

Embodiment 2

[0055] An antistatic sticky dust mat, comprising a sticky dust mat body, the surface of the sticky dust mat body is distributed with several nano-scale suction holes; the anti-static sticky dust mat is prepared from component A and nano-scale suction hole generating liquid As, the component A includes the following raw materials in parts by weight:

[0056]

[0057] The organic silica gel is methyl vinyl silicone rubber; the hydrogen-containing silicone oil is a hydrogen-containing silicone oil with methyl-terminated side chains carrying hydrogen.

[0058] The crosslinking agent is ethyl orthosilicate; the crosslinking accelerator is dibutoxydibutylstannane.

[0059] The nano-material powder is a mixture of nano-calcium carbonate powder and nano-magnesia powder in a weight ratio of 3:1; the particle size of the nano-material powder is 0.1 nm.

[0060] The specific surface area of ​​the white carbon black is 100m 2 / g; the white carbon black is a modified white carbon blac...

Embodiment 3

[0071] An antistatic sticky dust mat, comprising a sticky dust mat body, the surface of the sticky dust mat body is distributed with several nano-scale suction holes; the anti-static sticky dust mat is prepared from component A and nano-scale suction hole generating liquid As, the component A includes the following raw materials in parts by weight:

[0072]

[0073] The organic silica gel is methyl vinyl silicone rubber; the hydrogen-containing silicone oil is hydrogen-containing silicone oil with hydrogen-carrying side chains.

[0074] The crosslinking agent is benzoyl peroxide; the crosslinking accelerator is dibutyldiphenoxytin and dibutylbis(2-phenylphenoxy)tin mixed in a weight ratio of 1:1. become.

[0075] The nano-material powder is formed by mixing nano-alumina powder and nano-zinc oxide powder at a weight ratio of 1:1; the particle size of the nano-material powder is 100 nm.

[0076] The specific surface area of ​​the white carbon black is 300m 2 / g; the white ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of dust-sticking pads, in particular to an anti-static dust-sticking pad and a preparation method thereof. The anti-static dust-sticking pad comprises a dust-sticking pad body, a plurality of nanoscale suction holes are distributed in the surface of the dust-sticking pad body, the anti-static dust-sticking pad is prepared from a component A and a nanoscale suction hole generating liquid, and the component A is prepared from the following raw materials: organic silica gel, hydrogen-containing silicone oil, white carbon black, nano material powder, inorganic conductive powder, an antistatic agent, a dispersing agent, a cross-linking agent, a cross-linking accelerant and color masterbatch. According to the anti-static dust-sticking pad, the plurality of nanoscale suction holes are distributed in the surface of the dust-sticking pad body, the anti-static dust-sticking pad can easily stick dust on the contact surface so that dust-sticking effectsare obtained, the anti-static dust-sticking pad can be washed with water to remove dust on the surface of the dust-sticking pad body, the dust-sticking effect can be recovered after the anti-static dust-sticking pad is dried, the anti-static dust-sticking pad can be recycled so that the service life of the anti-static dust-sticking pad is prolonged, and compared with an existing multi-layer PE gluing pad, the anti-static dust-sticking pad is more environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of sticky mats, in particular to an antistatic sticky mat and a preparation method thereof. Background technique [0002] Sticky mat, also known as sticky floor glue, is mainly suitable for sticking at the entrance of the clean space and between the buffer zones. It can effectively stick the dust on the soles and wheels, and minimize the impact of dust on the quality of the clean environment. In this way, the effect of simple dust removal is achieved, and the problem that the dust removal of other floor mats is not thorough and cannot ensure that the dust does not spread is solved. [0003] Most of the existing sticky mats are multi-layer PE rubber-coated mats. For general dust, the dust-sticking effect is better, but for dust with static electricity, it adheres firmly to the sole / wheel, and the dust-sticking effect is greatly reduced. Contents of the invention [0004] In order to overcome the shortcomin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L83/05C08L33/02C08K13/06C08K9/06C08K7/26C08K5/14C08K5/57C08K3/22C08K3/34C08K3/04C08J7/14
CPCC08J7/14C08J2383/04C08K2003/222C08K2003/2227C08K2201/001C08K2201/011C08L83/04C08L2201/04C08L2205/025C08L2205/03C08L33/02C08K13/06C08K9/06C08K7/26C08K5/14C08K5/57C08K3/22C08K3/34C08K3/04
Inventor 刘敏
Owner 东莞市尼的科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap