Ceramic tile adhesive

A technology of tile adhesive and mass percentage, applied in the field of tile adhesive, can solve the problems of low bonding strength and high cost

Inactive Publication Date: 2020-05-29
VASA MORTAR CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the embodiment of the present invention provides a tile adhesive, the main purpose is to solve the problems of high cost and low bonding strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic tile adhesive
  • Ceramic tile adhesive
  • Ceramic tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prepare the raw materials according to the following formula, and then mix and stir evenly to obtain the tile adhesive;

[0025] The specific weight (KG) ratio of each component is as follows:

[0026]

Embodiment 2

[0028] Prepare the raw materials according to the following formula, and then mix and stir evenly to obtain the tile adhesive;

[0029] The specific weight (KG) ratio of each component is as follows:

[0030]

Embodiment 3

[0032] Prepare the raw materials according to the following formula, and then mix and stir evenly to obtain the tile adhesive;

[0033] The specific weight (KG) ratio of each component is as follows:

[0034]

[0035]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ceramic tile adhesive, and relates to the technical field of adhesives. The ceramic tile adhesive is composed of the following components in percentage by mass: 35.0 percentto 45.0 percent of ordinary Portland cement, 50.0 percent to 65.0 percent of an aggregate, 0.3 percent to 0.5 percent of cellulose ethers, 1.5 percent to 2.5 percent of an adhesive and 0.05 percent to0.50 percent of a modifier. According to the invention, a powdery coupling agent is added into the raw materials of the ceramic tile adhesive, so that the synergistic effect between redispersible adhesive powder and an inorganic material is enhanced, the utilization efficiency of the redispersible adhesive powder is improved, the cost is reduced, and the water resistance, temperature resistance and freeze-thaw resistance of the ceramic tile adhesive are improved.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a tile adhesive. Background technique [0002] Ceramic tiles have become one of the most commonly used finishing materials in the field of market construction. However, various hollowing phenomena often occur in the pasting of ceramic tiles due to various reasons. In order to solve this problem, through the polymer modification of cement mortar, the adhesion of some material tiles has been significantly improved, and the ceramic tiles rarely appear empty under the correct construction method. [0003] For the pasting of high-quality ceramic tiles, the traditional method is to add a large amount of redispersible rubber powder to the tile adhesive to achieve a firm effect of ceramic tile bonding. For example, by increasing the amount of rubber powder in large quantities, better flexibility can be achieved, which is satisfied with large deformation of gypsum boards and wood. Cera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00637C04B2201/50C04B14/06C04B24/383C04B24/26C04B24/20C04B24/42
Inventor 韩朝辉
Owner VASA MORTAR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap