High-temperature multi-color-change irreversible temperature-indicating coating for petrochemical equipment and preparation method thereof

A temperature-indicating coating and equipment technology, applied in the field of coatings, to achieve the effects of wide source of raw materials, simple preparation process, and high temperature-indicating precision

Active Publication Date: 2020-06-09
江苏纽克莱涂料有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there is no temperature-indicating paint specially developed for high-temperature equipment in the petrochemical industry in the industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature multi-color-change irreversible temperature-indicating coating for petrochemical equipment and preparation method thereof
  • High-temperature multi-color-change irreversible temperature-indicating coating for petrochemical equipment and preparation method thereof
  • High-temperature multi-color-change irreversible temperature-indicating coating for petrochemical equipment and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] This example relates to the preparation of a high-temperature multi-color irreversible temperature-indicating coating for petrochemical equipment.

[0061] The experimental process of this embodiment is as follows:

[0062] (1) In 8 parts by weight of xylene, mix 14 parts by weight of ultramarine blue, 0.8 parts by weight of bentonite, 1 part by weight of fumed silica, 2 parts by weight of titanium dioxide and 2.2 parts by weight of precipitated barium sulfate, and disperse to a particle size of less than or equal to 30 microns to obtain a first mixture; and

[0063] (2) In 10 parts by weight of xylene, mix the first mixture and 62 parts by weight of silicone resin, and disperse until the particle size is less than or equal to 20 microns, to obtain the high-temperature multi-color irreversible temperature-indicating coating for petrochemical equipment according to Example 1 .

[0064] The solid content of the temperature-indicating paint according to Example 1 is 40%,...

Embodiment 2-5

[0084] According to the method similar to Example 1, the high-temperature multi-color irreversible temperature-indicating coating for petrochemical equipment according to Examples 2-5 was prepared, and its temperature-indicating performance was tested under the same conditions as Example 1. In Example 5 using butyl ester as the organic solvent, the step of adding xylene in the preparation process of Example 1 was replaced by the step of adding butyl ester. Table 1 shows the temperature-indicating paint formulations of Examples 2-5.

[0085] The temperature-indicating paint formula of table 1 embodiment 2-5 (based on weight percentage)

[0086] raw material Example 2 Example 3 Example 4 Example 5 1503 silicone resin 55 60 70 75 ultramarine 8 20 15 8 Bentonite 2 0.8 1 0.8 fumed silica 1.5 0.5 1 0.5 Titanium dioxide 2.5 1.5 1.5 2.5 Precipitated Barium Sulfate 11 4 5.5 5.2 Xylene 20 19.2 6 0 Buty...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature multi-color-change irreversible temperature-indicating coating for petrochemical equipment. The high-temperature multi-color-change irreversible temperature-indicating coating is characterized by being prepared from the following raw materials in percentage by weight: 55 to 75% of organic silicon resin, 8 to 20% of ultramarine, 0.8 to 2% of a thickeningagent, 6 to 15% of a filler and 6 to 20% of an organic solvent. The invention further relates to a preparation method of the high-temperature multi-color-change irreversible temperature-indicating coating for the petrochemical equipment. The high-temperature multi-color-change irreversible temperature-indicating coating for the petrochemical equipment is high in temperature indicating precision, wide in raw material source and simple in preparation process, and can be used for over-temperature early warning of petrochemical equipment within a temperature range of 250-450 DEG C.

Description

technical field [0001] The application relates to the technical field of coatings, in particular to a high-temperature multi-color-changing irreversible temperature-indicating coating for petrochemical equipment and a preparation method thereof. Background technique [0002] Temperature-indicating paint is a special paint that uses color changes to indicate the surface temperature and temperature distribution of objects. It is also commonly called color-changing paint or heat-sensitive paint. [0003] According to the color stability of the temperature-indicating paint after it changes color, the temperature-indicating paint can be divided into reversible temperature-indicating paint and irreversible temperature-indicating paint. When heated to a predetermined temperature, the color of the coating changes, showing a new color different from the original color of the coating at room temperature, and when it is cooled to room temperature again, the coating returns to the origi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/26C09D5/29C09D7/61
CPCC08K2003/2241C08K2003/3045C09D5/26C09D5/29C09D183/04C09D7/61C08K3/00C08K3/34C08K3/346C08K3/36C08K3/22C08K3/30
Inventor 阎九林解军