Preparation method of self-winding polyester FDY fiber and prepared polyester FDY fiber
A self-curling, polyester technology, applied in the field of polyester FDY fiber, can solve the problems of poor suspension and inconspicuous nodes, and achieve the effects of increasing drape, good moisture absorption and perspiration and ventilation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0025] A kind of preparation method of self crimping polyester FDY fiber, comprises the following steps:
[0026] A. After crystallizing, drying and extruding the low-shrinkage polyester chips, they are spun through an "8"-shaped spinneret to obtain low-shrinkage polyester spinning; among them, the low-shrinkage polyester chips are those with a shrinkage rate of <20%. polyester chips;
[0027] B. Mix the high-shrinkage polyester chip and the polyester chip C evenly to form a mixture; wherein, the high-shrinkage polyester chip is a polyester chip with a shrinkage rate ≥ 20%, and the polyester chip C is polyethylene terephthalate Alcohol ester polyester chips;
[0028] C, the mixture is thickened by a thickening device to form a composite chip; wherein, the viscosity of the composite chip is greater than the viscosity of the low-shrinkage polyester chip;
[0029] D. After the composite chip is dried and extruded, it is spun through an "8"-shaped spinneret to obtain composite s...
Embodiment
[0053] Embodiment group 1-a kind of preparation method of self-curling polyester FDY fiber, comprises the following steps:
[0054] A. Crystallize, dry and extrude low-shrinkage polyester chips with a viscosity of 0.4dl / g, and spin through an "8"-shaped spinneret to obtain low-shrinkage polyester spinning; among them, low-shrinkage polyester chips The shrinkage rate is 10%;
[0055] B, the high-shrinkage polyester chips and the polyester chips C of the following table 1 formulation amount are mixed uniformly to form a mixture; wherein, the shrinkage rate of the high-shrinkage polyester chips is 45%;
[0056] C. Viscosifying the mixture to 0.9dl / g through a viscosifying device to form a composite chip;
[0057] D. After the composite chips are dried and extruded, they are spun through an "8"-shaped spinneret to obtain composite spinning;
[0058] E. According to the formulation amount in the following table 2, after combining the low-shrinkage polyester spinning obtained in s...
PUM
Property | Measurement | Unit |
---|---|---|
Melting point | aaaaa | aaaaa |
Melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap