Data line coating material and preparation method thereof

A technology of coating material and data line, applied in the field of data transmission line, to achieve the effect of increasing surface hardness, increasing metallic luster and good appearance effect

Inactive Publication Date: 2020-06-19
东莞线宝电子科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the development of the electronic accessories industry, the requirements for environmental protection are becoming more and more stringent, and the requirements for data lines are also getting higher and higher. Only wear-resistant and not easy to break can no longer meet the demand. Not easy to break, and environmental protection, metallic luster data line coating material and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The data line coating material of this embodiment includes, by weight, 85 parts of TPU, 0.5 part of phthalocyanine green, 0.5 part of reinforcing agent, 0.6 part of compatibilizer, and 5 parts of metal powder. In this embodiment, the reinforcing agent is white carbon black, and the compatibilizer is a maleic anhydride grafted compatibilizer.

[0021] The preparation method of the data line coating material in this embodiment includes the following steps:

[0022] (1) Knead TPU, add phthalocyanine green, reinforcing agent, compatibilizer and metal powder in proportion and mix at 20°C to obtain a mixture;

[0023] (2) After mixing the mixture evenly, add it to a twin-screw extruder, and carry out extrusion molding at 150°C.

[0024] Before the mixture is extruded, the molten mixture is molded with the data line and the charging line to obtain the mobile phone data line for performance testing.

Embodiment 2

[0026] The data line coating material of this embodiment includes, by weight, 90 parts of TPV, 0.7 parts of phthalocyanine blue, 0.3 parts of reinforcing agent, 0.3 parts of flame retardant, 0.7 parts of compatibilizer, and 7 parts of metal powder. In this embodiment, the reinforcing agent is carbon black, the flame retardant is toluene-diphenyl phosphate, and the compatibilizer is maleic anhydride grafted compatibilizer.

[0027] The preparation method of the data line coating material in this embodiment includes the following steps:

[0028] (1) Mix TPV, add phthalocyanine blue, reinforcing agent, flame retardant, compatibilizer, metal powder in proportion and mix at 18°C ​​to obtain a mixture;

[0029] (2) After mixing the mixture evenly, add it to a twin-screw extruder, and carry out extrusion molding at 200°C.

[0030] Before the mixture is extruded, the molten mixture is molded with the data line and the charging line to obtain the mobile phone data line for performance...

Embodiment 3

[0032] The data line coating material of this embodiment includes, by weight, 93 parts of PVC, 0.6 parts of permanent violet, 0.7 parts of reinforcing agent, 0.7 parts of compatibilizer, and 9 parts of metal powder. In this embodiment, the reinforcing agent is carbon black, and the compatibilizer is a maleic anhydride grafted compatibilizer.

[0033] The preparation method of the data line coating material in this embodiment includes the following steps:

[0034] (1) Mix PVC, add permanent violet, reinforcing agent, compatibilizer and metal powder in proportion and mix at 20°C to obtain a mixture;

[0035] (2) After mixing the mixture evenly, add it to a twin-screw extruder, and carry out extrusion molding at 250°C.

[0036] Before the mixture is extruded, the molten mixture is molded with the data line and the charging line to obtain the mobile phone data line for performance testing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a data line coating material and a preparation method thereof. The data line coating material comprises the following components in parts by weight: 85-98 parts of a carrier, 0.5-1 part of color masterbatch, 0.5-1 part of a compounding agent, 0.5-1 part of a compatilizer and 1-10 parts of metal powder. The preparation method of the data line coating material comprises the following steps: (1) mixing the carrier, adding the color master batch, the compounding agent, the compatilizer and the metal powder in proportion, and carrying out mixing to obtain a mixture; and (2) uniformly mixing the mixture, adding the mixture into a double-screw extruder, and carrying out extrusion molding. The data line coating material has metal luster and a good appearance effect; and through the addition of metal powder, the use of the color masterbatch is reduced, the surface hardness of the coating material is increased, and the data line is prevented from being scratched in the useprocess.

Description

technical field [0001] The invention relates to the technical field of data transmission lines, in particular to a data line coating material with metallic luster and a preparation method thereof. Background technique [0002] The main function of the data line is data transmission and charging, and there are core wires for data transmission and charging. These core wires cannot be directly exposed, otherwise it will be extremely unsafe when used. In order to ensure that users can use the data cable safely, and to ensure that the data cable is not easy to be broken when it is wound, it is necessary to use a coating to protect the core wire. At present, the data cables on the market are mostly made of three materials: TPE, PVC, and braided wire. The price of PVC is relatively economical, and the touch is good, but after a long time of use, it is prone to cracking and breaking. Compared with PVC, TPE is better in terms of thermoplasticity, flexibility and elasticity, and it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/04C08L101/00C08L27/06C08L83/04C08L51/00C08K13/04C08K3/08C08K13/02
CPCC08L27/06C08L75/04C08L83/04C08L101/00C08L2203/202C08L2207/04C08L51/00C08K13/04C08K3/08C08K13/02
Inventor 毛中平
Owner 东莞线宝电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com