Prefabricated part water washing surface coating agent

A technology of prefabricated components and water-washing surfaces, applied in manufacturing tools, ceramic molding machines, etc., can solve the problems of poor coating effect, poor coating effect, poor viscosity control, etc., and achieves convenient preparation, low cost, good effect

Inactive Publication Date: 2020-07-03
YUANJIAN INDZED HOUSING INTEGRATED TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a prefabricated component water-washing surface coating agent, which has the advantages of simple preparation process, low cost, good effect, and easy combination with cast-in-place concrete, and solves the problems of high preparation cost and poor viscosity. , leading to poor effect of the paint, and secondly, the preparation steps are cumbersome, and the viscosity is not well controlled, which leads to the problem that the effect of the paint is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A water-washing surface coating agent for prefabricated components. The mass ratio of the water-washing surface coating agent for prefabricated components is: water: glucose: thickener = 2:1:0.05.

[0020] The making of a kind of prefabricated part washing surface coating agent comprises the following steps:

[0021] S1. Take water with a mass of 2 units, place it on a heating furnace and heat it until the water boils;

[0022] S2. Add glucose with a mass of 0.5 units into the heating furnace, and continue heating until boiling;

[0023] S3. Add glucose with a mass of 0.5 units to the boiling solution in the heating furnace in S2, and continue heating until boiling;

[0024] S4, adding a thickening agent with a mass of 0.05 units to the boiling solution in the heating furnace in S3;

[0025] S5. Pour the solution in the heating furnace in S4 into the reaction kettle, start the stirring motor to fully stir, and ensure uniform stirring;

[0026] S6. Pour the uniformly ...

Embodiment 2

[0030] A water-washing surface coating agent for prefabricated components. The mass ratio of the water-washing surface coating agent for prefabricated components is: water: glucose: thickener=2.1:1.1:0.06.

[0031] The making of a kind of prefabricated part washing surface coating agent comprises the following steps:

[0032] S1. Take water with a mass of 2.1 units and place it on a heating furnace for heating until the water boils;

[0033] S2. Add glucose with a mass of 0.5 units into the heating furnace, and continue heating until boiling;

[0034] S3. Add glucose with a mass of 0.6 units to the boiling solution in the heating furnace in S2, and continue heating until boiling;

[0035] S4, adding a thickening agent with a mass of 0.06 units to the boiling solution in the heating furnace in S3;

[0036] S5. Pour the solution in the heating furnace in S4 into the reaction kettle, start the stirring motor to fully stir, and ensure uniform stirring;

[0037] S6. Pour the uni...

Embodiment 3

[0041] A water-washing surface coating agent for prefabricated components. The mass ratio of the water-washing surface coating agent for prefabricated components is: water: glucose: thickener=1.9:0.9:0.04.

[0042] The making of a kind of prefabricated part washing surface coating agent comprises the following steps:

[0043] S1. Take water with a mass of 1.9 units and place it on a heating furnace for heating until the water boils;

[0044] S2. Add glucose with a mass of 0.4 units into the heating furnace, and continue heating until boiling;

[0045] S3. Add glucose with a mass of 0.5 units to the boiling solution in the heating furnace in S2, and continue heating until boiling;

[0046] S4, adding a thickening agent with a mass of 0.04 units to the boiling solution in the heating furnace in S3;

[0047] S5. Pour the solution in the heating furnace in S4 into the reaction kettle, start the stirring motor to fully stir, and ensure uniform stirring;

[0048] S6. Pour the uni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of prefabricated part water washing surface coating agents, and discloses a prefabricated part water washing surface coating agent. The prefabricated partwater washing surface coating agent is characterized in that the mass ratio of water to glucose to a thickening agent is 1.7-2.3 to 0.7-1.3 to 0.02-0.08. When a prefabricated part is made, the coatingagent coats a formwork in advance for form erecting and pouring, after the strength of the concrete meets the hoisting requirement, form removal is performed, then a high pressure water gun is used for flushing to flush away concrete mortar on a contact surface of the coating agent, then stone aggregate is exposed outside to be conveniently combined with cast-in-place concrete, through the arrangement of components of the coating agent, the viscosity of the coating agent can be improved, meanwhile, the application performance of the coating agent also can be improved, the preparation processis simple, the cost is low, the effect is good, the proper viscosity can be conveniently adjusted, the thickening agent is arranged, so that residual monomers of the prefabricated part water washing surface coating agent are few, self-thickening property is achieved, the thickening agent color paste modulation is convenient, the stability is good, crusts are not formed on the surface, and the compatibility with a coating is good.

Description

technical field [0001] The invention relates to the technical field of prefabricated component water-washing surface coating agent, in particular to a prefabricated component water-washing surface coating agent. Background technique [0002] Prefabricated components refer to steel, wood or concrete components prefabricated in factories or on site according to design specifications. There are many kinds of prefabricated component molds, common ones are concrete component molds, component molds, hexagonal reservoir slope protection molds, bridge cover molds, urban Road side stones, cement component molds, cement product component molds, concrete product molds, canal cover molds, hollow hexagonal slope protection brick molds, road and bridge cover molds, cable trench cover molds, roadbed cover molds, electric power cover molds, water conservancy Irrigation molds, plastic manhole cover molds, water conservancy cover molds, ditch cover molds, tunnel cover molds, trench cover mold...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B28B7/38
CPCB28B7/384B28B7/388
Inventor 王春力李天祥田骉
Owner YUANJIAN INDZED HOUSING INTEGRATED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com