A technology for preventing partitions and wall panels, applied in the field of building materials, can solve problems such as being unsuitable for mechanism production, and achieve high-strength effects.

Inactive Publication Date: 2003-07-16
田欣
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using glass fiber cloth as a reinforced structure has good strength, but it is not suitable for machine-made production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0006] When the present invention is actually implemented, the weight percentages of each raw material component of the base material can adopt the following proportioning, which can make the partition wall board have excellent comprehensive performance:

[0007] Bentonite 15%;

[0008] Fly ash 30%;

[0009] Herbal powder 25%;

[0010] Magnesium oxide (more than 87% of purity) 20%;

[0011] Magnesium Chloride 9.5%; and

[0012] Acid, potassium permanganate, sodium hexametaphosphate and ferrous sulfate are used in a total amount of 0.5%.

[0013] For the partition wall panel with a general specification of 90×600, 9 to 11 composite nylon ropes of φ4 to φ6 are used as reinforcements for the matrix. The composite nylon ropes are made of nylon and hemp in a ratio of 3:1. In practice, the use of pure nylon rope as a reinforcement has poor adhesion, and the use of pure hemp rope as a reinforcement is easy to rot. The composite nylon rope can eliminate the respective disadvantage...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A fire-resistance light partition for building is made up of bentonite, fly ash and herbaceous and ligreous fibres as raw materials, and the glass fibre or nylon ropes are used as its reinforcement. Its advantages include light weight, high surface density (50 kg / sq.m) and low cost (23 yuan / m2) with 100X600 partition as example.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a novel lightweight five-proof partition board. Background technique [0002] In order to ensure the use performance, the partition board needs to have a certain strength performance. On this basis, the higher the hollow rate of the partition board, the better the use effect. Chinese patent application No. 93115234.8 (publication number is CN1101092A) discloses a magnesium-silicon fiber-planted composite lightweight hollow wallboard, the center of which is provided with a plurality of through holes, reinforced by glass fiber or glass fiber cloth. Using glass fiber cloth as a reinforced structure has good strength, but it is not suitable for machine-made production. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a new type of partition wall board which is suitable for machine-made production and has suffic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More