Woven bag coating, preparation method, coating method and woven bag

A woven bag and coating technology, which is applied in textiles and papermaking, textile/flexible product manufacturing, final product manufacturing, etc., can solve the problems of moisture, perforation, dust leakage, etc., and achieve dust reduction, strength retention, and tensile strength The effect of zero loss

Active Publication Date: 2020-07-31
宜良县日发塑业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The object of the present invention is to provide a kind of woven bag paint and preparation method, coating method and woven bag, to solve the problem that the plastic woven bag after being coated with the coating film needs to be prepared when the cement-coated plastic woven bag is prepared in the prior art. The problem of exhaust is solved by punching holes on the cloth, but there are technical problems such as running, popping, and ash leakage during filling, and easy to be damp in the later stage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Woven bag coating, preparation method, coating method and woven bag
  • Woven bag coating, preparation method, coating method and woven bag
  • Woven bag coating, preparation method, coating method and woven bag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] 1.1 Preparation of woven bag coating:

[0065] A woven bag coating provided by the present invention, its raw materials include: low-density polyethylene 7.5%; special-grade polypropylene 47%; first-grade polypropylene 38%; whitening agent: 0.4%; masterbatch: 6% ; Antireflection Masterbatch: 0.35%; Degradant: 0.08%; Paraffin: 0.67%.

[0066] 1.2 Preparation method:

[0067] (1) prepare each raw material by proportioning;

[0068] ① Preparation of super polypropylene;

[0069] The preparation method of the super-grade polypropylene is: mixing the drawing-grade polypropylene particles and the first-grade recycled polypropylene particles in a weight ratio of 2:8; then granulating the finished product, the ash content of which is 5%;

[0070] ② Preparation of primary polypropylene;

[0071] The preparation method of the primary polypropylene is: mixing the primary recycled polypropylene particles and the secondary recycled polypropylene particles in a weight ratio of 5:...

Embodiment 2

[0077] To prepare woven bag coating:

[0078] A woven bag paint provided by the present invention, its raw materials include: low-density polyethylene 15%; special-grade polypropylene 40%; first-grade polypropylene 31.2%; whitening agent: 0.3%; masterbatch: 10% ; Anti-reflection masterbatch: 2%; Cooling masterbatch: 0.5%; Paraffin wax: 1%.

[0079] Preparation:

[0080] (1) prepare each raw material by proportioning;

[0081] ① Preparation of super polypropylene;

[0082] The preparation method of the super-grade polypropylene is: mixing the drawing-grade polypropylene particles and the first-grade recycled polypropylene particles in a weight ratio of 1.5:8.5; then granulating the finished product, the ash content of which is 6%;

[0083] ② Preparation of primary polypropylene;

[0084] The preparation method of the primary polypropylene is: mixing the primary recycled polypropylene particles and the secondary recycled polypropylene particles in a weight ratio of 4:6; then...

Embodiment 3

[0090] To prepare woven bag coating:

[0091] A woven bag coating provided by the present invention, its raw materials include: 2% low-density polyethylene; 55.25% special-grade polypropylene; 30% first-grade polypropylene; whitening agent: 0.5%; masterbatch: 2% ; Anti-reflection masterbatch: 10%; Cooling masterbatch: 0.2%; Paraffin wax: 0.05%.

[0092] Preparation:

[0093] (1) prepare each raw material by proportioning;

[0094] ① Preparation of super polypropylene;

[0095] The preparation method of the super-grade polypropylene is: mixing the drawing-grade polypropylene particles and the first-grade recycled polypropylene particles in a weight ratio of 2.5:7.5; then granulating the finished product, the ash content of which is 4%;

[0096] ② Preparation of primary polypropylene;

[0097] The preparation method of the primary polypropylene is: mixing the primary recycled polypropylene particles and the secondary recycled polypropylene particles in a weight ratio of 6:4;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a woven bag coating, a preparation method, a coating method and a woven bag, and solves the problems that in the prior art, when the cement laminating plastic woven bag is prepared, the problem of air exhaust needs to be solved by punching on plastic woven cloth coated with a coating film, but the phenomena of running, overflowing and ash leakage exist during filling when punching is carried out, and damping is prone to being caused in the later period. The woven bag coating is prepared from the following raw materials including, by weight, 2%-15% of low-density polyethylene, 40%-70% of special grade polypropylene, 30%-60% of first-grade polypropylene, 0.3%-0.5% of a whitening agent, 2%-10% of a master batch, 0.2%-0.5% of an anti-reflection master batch, 0.05%-0.1% of a cooling master batch and 0.5%-1% of paraffin, wherein the sum of the weight percentages of the raw materials is 100%. The preparation method is used for preparing the cement woven bag, and the woven bag is good in exhaust effect, high in tensile strength and good in moisture resistance.

Description

technical field [0001] The invention relates to a coating, in particular to a woven bag coating, a preparation method, a coating method and a woven bag. Background technique [0002] Coating is a term in the process of making woven bags. Its principle is to apply resin to plastic woven cloth in a molten state. Only apply the molten resin to the plastic woven cloth and cool it immediately to obtain a two-in-one woven cloth, which is a laminated plastic woven bag. However, coating a layer of plastic film on the plastic woven cloth will cause airtightness and greatly reduce the exhaust performance. [0003] In the process of using the compound film plastic woven bag, the existing cement enterprises generally use the rotary air pressure packaging machine to put the cement tank into the compound film plastic woven bag through the air pressure. The bag output of the domestic cement factory after filling will basically reach 60-120 tons / hour. Under this premise, the cement packa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/04
CPCD06N3/0002D06N3/0088D06N3/045D06N2211/20Y02P70/62
Inventor 陈崇武章显帅计丕坤袁庆祝
Owner 宜良县日发塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap