Forming preparation method of degradable nitrile rubber gloves

A technology of nitrile rubber and nitrile latex, which is applied in the direction of gloves, clothing, applications, etc., can solve the problems of low utilization value, limited scope of application, violation, etc., to improve strength and mechanical properties, improve rheological properties, and improve processing performance effect

Inactive Publication Date: 2020-08-04
安徽攀望科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the introduction of collagen, protein, etc. will increase the threat of allergic reactions, which violates the original intention of using nitrile gloves. The reason why people widely use nitrile gloves is that they do not contain latex protein and will not cause allergic reactions.
Moreover, the use of natural degradable materials such as cellulose and starch is carefully blended, and the chemical corrosion resistance and physical properties of the gloves drop sharply, which does not meet the performance level of ordinary non-degradable gloves. Low
Chinese patent CN2018106797858 discloses degradable gloves and its preparation method, which are not easy to tear, and have excellent degradable properties, suitable for use in various environments, and the scope of application in various environments is greatly limited
At present, there are few corresponding products and technologies for degradable nitrile rubber gloves in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming preparation method of degradable nitrile rubber gloves

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The first step, prepare cyanoacrylate mixed and liquid impregnation latex: by weight, first according to the composition of nitrile latex: 76 parts of carboxylated nitrile latex, 0.2 part of potassium hydroxide, 15 parts of modified geopolymer 0.1 part, 0.1 part of initiator azobisisobutylamidine hydrochloride, beating and mixing evenly to obtain impregnated emulsion, and then according to the composition of cyanoacrylate mixed solution: 33 parts of hexyl cyanoacrylate, 0.3 parts of buffer copper acetate 34 parts of liquid nitrile rubber, 5 parts of thickener PF, 0.1 part of stabilizer propane sultone, 5 parts of softener dipropylene phthalate, 2 parts of accelerator zinc dimethyl dithiocarbamate, Mix evenly to obtain a mixed liquid of hexyl cyanoacrylate, which is dipped into latex liquid and sent into the latex dipping tank, and the mixed liquid of hexyl cyanoacrylate is sent into the polyethylene pre-soaking tank; the second step, the dipping molding of gloves: use S...

Embodiment 2

[0031] (1) Preparation of dipping latex and cyanoacrylate mixed solution: in parts by weight, first according to the composition of nitrile latex: initiator cumene hydroperoxide 0.02 parts, modified geopolymer 13 parts, carboxyl 64 parts of nitrile latex, 0.1 part of potassium hydroxide, beating and mixing evenly to obtain impregnated latex liquid, and then according to the composition of cyanoacrylate mixed liquid: stabilizer 2,6-di-tert-butyl-4-methylphenol 0.05 0.01 part of buffering agent citric acid, 3 parts of softener tricresyl phosphate, 0.1 part of accelerator CA, 25 parts of heptyl cyanoacrylate, 31 parts of liquid nitrile rubber, 5 parts of thickener zinc methacrylate , mixed evenly to obtain a mixed solution of heptyl cyanoacrylate, which was impregnated with latex and sent into a latex dipping tank, and the mixed solution of heptyl cyanoacrylate was sent into a polyethylene pre-preg tank; (2) Glove dip molding: use Spray the hand mold with hot water at 75°C, clean...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of high polymer materials. The invention relates to gloves, in particular to degradable nitrile rubber gloves forming preparation method. The invention discloses a forming preparation method of degradable nitrile rubber gloves. The preparation method is simple, convenient and easy to implement, and the prepared gloves have the characteristics of acid and alkali resistance, oil stain resistance, permeation resistance, bacteria resistance, no latex allergy and convenience in use, are lighter, thinner and softer in touch feeling, excellent in elasticity, excellent in physical property and chemical property, free of any natural latex component, free of allergy risk, good in degradability and wide in application prospect.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, in particular to a molding preparation method of degradable nitrile rubber gloves. Background technique [0002] Nitrile gloves refer to gloves made or painted, with oil-proof effect, mainly used in factories, oil fields, repair shops, etc. Nitrile gloves do not contain latex protein, so they will not cause allergic reactions. At the same time, they are antistatic, resistant Aging and oil resistance, the shape of the glove is designed according to the shape of the human hand, with great sensitivity, excellent tensile properties and puncture resistance, high tensile strength and excellent wear resistance. However, nitrile latex has the characteristics of low wet gel strength, large shrinkage, poor film-forming performance, and low vulcanized film strength, so it is difficult to make dipped products. Especially for the production of thin gloves, it has been a difficult problem for glove ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A41D19/00C08F279/02C08F220/50
CPCA41D19/0055C08F279/02C08F220/50
Inventor 田雪伟
Owner 安徽攀望科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap