Porcelain antique brick with golden glitter effect and preparation method thereof

An antique brick and golden technology, which is applied in the field of porcelain antique brick and its preparation, can solve the problems of non-transparent polished glaze and flash gold materials that are fired and completely fused at one time, without three-dimensional effect, and not durable, etc., to achieve Rich texture expressiveness, transparent three-dimensional effect, and strong three-dimensional effect

Active Publication Date: 2021-03-19
广西蒙娜丽莎新材料有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many kinds of ceramic tile products developed on the market, such as the patent named "a ceramic glazed tile with gold metal effect and its preparation method" with the application number CN 101880178A, which discloses a method using What is more special is that the combination of copper-aluminum alloy powder and ceramics produces a glaze effect of golden metallic luster, but it does not have the characteristics of transparent polished glaze and flash gold materials that can be fired and completely fused at a high temperature, so the glaze produced by it The metallic luster produced by the face brick is only on the surface of the brick, and the product has no three-dimensional effect, and is not wear-resistant and durable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porcelain antique brick with golden glitter effect and preparation method thereof
  • Porcelain antique brick with golden glitter effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Example 1 (taking the production of 600*600mm products as an example)

[0042] A porcelain antique brick with golden glitter effect, the golden glitter glaze used in the porcelain antique brick with golden glitter effect is composed of the following raw materials in parts by weight: 880 ink: 45 parts, glitter material A: 40 parts, And flashing material B: 8 parts; the flow rate of the 880 ink is 18 seconds; the 880 ink is composed of the following raw materials in parts by weight: 83 parts of water; 5.0 parts of sodium carboxymethyl cellulose; ethylene glycol: 5 parts; acrylic acid Copolymer: 0.5 parts; Polyurethane: 1 part; Isothiazolinone: 1 part; Sodium polycarboxylate: 2 parts;

[0043] The flashing material A is used to adjust the flashing effect of the golden flashing glaze; the flashing material A includes the following chemical components by weight percentage: loss on ignition: 1.00%; SiO 2 : 0.2%; Al 2 o 3 : 0.01%; CaO: 0.01%; P 2 o 5 : 0.2%; SO 3 : 0.2%;...

Embodiment 2

[0050] Example 2 (taking the production of 600*600mm products as an example)

[0051] A porcelain antique brick with golden glitter effect, the golden glitter glaze used in the porcelain antique brick with golden glitter effect is composed of the following raw materials in parts by weight: 880 ink: 50 parts, glitter material A: 45 parts, And flashing material B: 15 parts; the flow rate of the 880 printing ink is 25 seconds; the 880 printing ink is composed of the following raw materials in parts by weight: 86 parts of water; 8.0 parts of sodium carboxymethyl cellulose; 8 parts of ethylene glycol; acrylic acid Copolymer: 1.5 parts; Polyurethane: 2 parts; Isothiazolinone: 2 parts; Sodium polycarboxylate: 3 parts;

[0052] The flashing material A is used to adjust the flashing effect of the golden flashing glaze; the flashing material A includes the following chemical components by weight percentage: loss on ignition: 1.00%; SiO 2 : 0.2%; Al 2 o 3 : 0.01%; CaO: 0.01%; P 2 o ...

Embodiment 3

[0059] Example 3 (taking 600*600mm product production as an example)

[0060] A porcelain antique brick with golden glitter effect, the golden glitter glaze used in the porcelain antique brick with golden glitter effect is composed of the following raw materials in parts by weight: 880 ink: 47 parts, glitter material A: 42 parts, And flashing material B: 10 parts; the flow rate of the 880 ink is 22 seconds; the 880 ink is composed of the following raw materials in parts by weight: 84 parts of water; 6.0 parts of sodium carboxymethyl cellulose; ethylene glycol: 6 parts; acrylic acid Copolymer: 0.8 parts; Polyurethane: 1.2 parts; Isothiazolinone: 1.5 parts; Sodium polycarboxylate: 2.5 parts;

[0061] The flashing material A is used to adjust the flashing effect of the golden flashing glaze; the flashing material A includes the following chemical components by weight percentage: loss on ignition: 1.00%; SiO 2 : 0.15%; Al 2 o 3 : 0.01%; CaO: 0.01%; P 2 o 5 : 0.2%; SO 3 : 0.2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a porcelain archaized brick with golden glittering effect and a preparation method of the porcelain archaized brick, 880 stamp-pad ink accounting for a large proportion in thegolden glittering glaze can provide a good printing effect, agglomeration of a glittering material is reduced, glaze defects are reduced, the antifouling property is improved, and the glaze melting effect is enhanced; a flashing material A can adjust the flashing effect of the composite glaze; a glittering material B is mainly used for adjusting the high-temperature firing temperature of the composite glaze besides adjusting the glittering effect of the composite glaze, so that complete fusion of the golden glittering glaze and the transparent polished glaze is guaranteed, the smoothness of aglaze surface is kept, and a prepared porcelain archaized brick finished product has antifouling, wear-resisting and durable properties; the porcelain archaized brick has the following characteristics that the printing glittering golden color is combined with the product color and texture, the product has more impact force in level and vision, the pattern level is richer, the texture is more natural, the stereoscopic impression is stronger, and a newly fused glazed product has more transparent three-dimensional stereoscopic impression.

Description

technical field [0001] The invention relates to the technical field of architectural ceramic antique bricks, in particular to a porcelain antique brick with golden glitter effect and a preparation method thereof. Background technique [0002] With the needs of people and the development of the market, there are more and more types of building decoration materials, and the requirements are becoming more and more high-end and novel. No matter it is the design color and color of brick materials and patterns, higher requirements are put forward. [0003] At present, there are many kinds of ceramic tile products developed on the market, such as the patent named "a ceramic glazed tile with gold metal effect and its preparation method" with the application number CN 101880178A, which discloses a method using What is more special is that the combination of copper-aluminum alloy powder and ceramics produces a glaze effect of golden metallic luster, but it does not have the characteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/89C04B35/622
CPCC03C8/00C04B35/622C04B41/52C04B41/89C04B2235/96C04B2235/9646C04B41/4543C04B41/5022
Inventor 萧志强赵勇刘荣勇赵一波曹普银汪小刚邱玉鹏
Owner 广西蒙娜丽莎新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com