Thick-specification pipeline steel and low-compression-ratio production process thereof

A technology with low compression ratio and production process, which is applied in the field of low-carbon micro-alloy steel materials, can solve the problems that the drop hammer toughness is difficult to meet the standard requirements, segregation and porosity in the core of continuous casting slabs, and easy coarse grains, etc.

Active Publication Date: 2020-10-09
武汉钢铁有限公司
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main purpose of the present invention is to aim at the low compression ratio production process of the existing ultra-thick wall pipeline steel, which easily leads to coarse grains, segregation and looseness in the core of the continuous casting slab, low strength and toughness, especially the drop hammer toughness (DWTT) is difficult to meet Insufficient standard requirements, etc., provide a low compression ratio production method for thick gauge pipelines, the obtained pipeline steel meets the service technical requirements of pipeline steel such as extra thick wall, high strength and toughness, and the production process involved is simple, easy to operate, suitable for popularization and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thick-specification pipeline steel and low-compression-ratio production process thereof
  • Thick-specification pipeline steel and low-compression-ratio production process thereof
  • Thick-specification pipeline steel and low-compression-ratio production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～4

[0052] 150mm billet is used to roll 25mm thickness X70 grade seabed acid-resistant pipeline steel. The specific implementation steps are as follows:

[0053] 1) Carry out smelting according to the composition requirements stated in Table 1, and control the content of molten steel as follows: N≤0.0050%, H≤0.0002%, O≤0.0025%, P≤0.015%, S≤0.0030%; molten steel composition After qualified, the molten steel is treated with Mg, the Mg in the molten steel is controlled at 0.0002-0.0022%, and the casting temperature is controlled at 1533-1548°C. At the same time, electromagnetic stirring and light reduction technology are used during the continuous casting solidification process to reduce the composition and Organization macro segregation;

[0054] 2) After casting a slab with a thickness of 150mm, install a heating furnace to heat and keep it warm; the heating temperature is 1160-1200°C; according to different furnace loading temperatures, the time in the furnace is 130-230min, and t...

Embodiment 5～9

[0066] Using 230mm billet to roll 40mm-41mmX70 grade pipeline steel, the specific implementation steps are as follows:

[0067] 1) Carry out smelting according to the composition requirements stated in Table 4, and control the content of molten steel as follows: N≤0.0050%, H≤0.0002%, O≤0.0025%, P≤0.015%, S≤0.0030%; molten steel composition After the molten steel composition is qualified, the molten steel is treated with Mg, the Mg in the molten steel is controlled at 0.0002-0.0022%, and the temperature is controlled at 1533-1548°C during casting. Reduce the composition and macro-segregation of the slab;

[0068] 2) After casting into a slab with a thickness of 230mm, install a heating furnace to heat and keep it warm; the heating temperature is 1160-1200°C; according to different furnace loading temperatures, the time in the furnace is 160-260min, and the holding time at a high temperature of 1160-1200°C is 60-100min;

[0069] 3) Three-stage hot rolling; in the first stage, o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses low-compression-ratio thick-specification pipeline steel which consists of the following chemical components in percentage by mass: 0.03-0.07% of C, 0.10-0.30% of Si, 1.1-1.6%of Mn, 0.1-0.3% of Cr, 0.1-0.4% of Ni, 0.10-0.25% of Mo, 0.04-0.07% of Nb, less than or equal to 0.03% of V, 0.01-0.025% of Ti, 0.01-0.045% of Al, and 0.002-0.0022% of Mg. The thick-specification pipeline steel is prepared from clean steel smelting, continuous casting, casting blank heating, three-stage controlled-rolling, and a super-quick cooling process. A matrix structure of an obtained steelplate is granular bainite and acicular ferrite, has better strength toughness matching and a low yield ratio, is excellent in HIC and SSCC acidic corrosion resistance, and can meet service technical requirements of pipeline steel with thickness specification yield strength greater than or equal to 485 MPa, and an anti-acid pipeline.

Description

technical field [0001] The invention belongs to the technical field of low-carbon micro-alloy steel materials, and in particular relates to a thick-gauge pipeline steel and a production process thereof with a low compression ratio. Background technique [0002] China is a country that consumes a lot of energy. For the sake of high-efficiency energy transmission and safety considerations, high-grade steel, large-diameter, large-wall thickness, and high-pressure transmission have become important development directions for pipeline construction. The country urgently needs to develop high-grade steel pipes such as X70-X80 Pipeline steel with wall thickness. [0003] Compared with conventional thin-gauge pipeline steel, the production of high-grade large-wall-thickness pipeline steel often adopts the method of grain refinement to ensure strength and toughness. By applying a large amount of compression to thick-gauge continuous casting slabs, grain refinement and The purpose of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/58C22C38/44C22C38/48C22C38/46C22C38/50C22C38/06C21D8/02
CPCC22C38/02C22C38/04C22C38/58C22C38/44C22C38/48C22C38/46C22C38/50C22C38/06C21D8/0226C21D2211/002C21D2211/005
Inventor 岳江波李利巍俆进桥邹航梅荣利邓伟张鹏武汪波聂顺刘静
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com