Low-carbon martensitic steel, myriameter drilling machine hanging ring and preparation method of myriameter drilling machine hanging ring

A martensitic steel and lifting ring technology, which is applied to drilling equipment, drill pipes, drill pipes, etc., can solve problems such as failure to meet the use requirements, reduce the formation of inclusions and harmful tissues, improve hardenability, and ensure high strength The effect of toughness

Active Publication Date: 2020-12-04
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For 12000m and above ultra-deep well drilling rigs with a section diameter of 180mm or even larger diameter suspension ring products, the current materials can no longer meet the use requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-carbon martensitic steel, myriameter drilling machine hanging ring and preparation method of myriameter drilling machine hanging ring
  • Low-carbon martensitic steel, myriameter drilling machine hanging ring and preparation method of myriameter drilling machine hanging ring
  • Low-carbon martensitic steel, myriameter drilling machine hanging ring and preparation method of myriameter drilling machine hanging ring

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation method of suspension ring of the present invention specifically comprises the following steps:

[0035] (1) Refined into billet according to the following composition, its composition is calculated by mass percentage, including the following components:

[0036] C: 0.17% to 0.19%; Si: 0.20% to 0.25%; Mn: 0.6% to 0.7%; Cr: 1.5% to 1.6%; Mo: 0.7% to 0.8%; Ni: 4.1% to 4.3%; V: 0.13%~0.15%; S≤0.005% and P≤0.01%, the rest is iron and unavoidable impurities.

[0037](2) Electroslag remelting is performed on the steel billet to obtain an ingot with a diameter of not less than 690mm, the ingot is heated evenly, the heating temperature is controlled at 1180±10°C, and forging is carried out, and the termination temperature of forging is controlled above 860°C to obtain Round steel with a diameter of 350mm to 380mm shall be annealed at no lower than 400°C after forging to eliminate forging defects and residual stress;

[0038] (3) Heat the round steel to 1180±10°...

Embodiment 1

[0042] The invention discloses a preparation method of a suspension ring, which specifically comprises the following steps:

[0043] (1) as shown in table 1, carry out refining into billet according to following composition, and its composition is calculated by mass percentage, comprises following component:

[0044] C: 0.17%; Si: 0.20%; Mn: 0.6%; Cr: 1.5%; Mo: 0.7%; Ni: 4.1%; Avoid impurities.

[0045] (2) Electroslag remelting is performed on the steel billet to obtain an ingot with a diameter of 690mm. The ingot is heated evenly to 1170°C for forging. The forging temperature is controlled at 860°C to 1170°C to obtain a circle with a diameter of 350mm to 360mm. For steel, after forging, the surface temperature is lowered to 400°C and annealed in the furnace;

[0046] (4) The round steel is reheated to 1170°C for forging, the forging temperature is controlled at 860°C to 1170°C, and a suspension ring sample with a diameter of 160mm is obtained by forging;

[0047] (5) Heat...

Embodiment 2

[0050] The invention discloses a preparation method of a suspension ring, which specifically comprises the following steps:

[0051] (1) as shown in table 1, carry out refining into billet according to following composition, and its composition is calculated by mass percentage, comprises following component:

[0052] C: 0.19%; Si: 0.25%; Mn: 0.7%; Cr: 1.6%; Mo: 0.8%; Ni: 4.3%; V: 0.15%; Avoid impurities.

[0053] (2) Electroslag remelting is performed on the steel billet to obtain an ingot with a diameter of 870mm, and the ingot is heated evenly to 1190°C for forging at a forging temperature of 860°C to 1170°C to obtain round steel with a diameter of 360mm to 380mm. After forging, the surface temperature is lowered to 450°C and annealed in the furnace;

[0054] (4) Reheat the round steel to 1190°C for forging, the forging start temperature is controlled at 860°C to 1170°C, and a ring sample with a diameter of 170mm is obtained by forging;

[0055] (5) Heat the suspension ri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
impact energyaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of petroleum equipment manufacturing, and particularly discloses low-carbon martensitic steel. The low-carbon martensitic steel comprises the following components inpercentage by mass: 0.17-0.19% of C, 0.20-0.25% of Si, 0.6-0.7% of Mn, 1.5-1.6% of Cr, 0.7-0.8% of Mo, 4.1-4.3% of Ni, 0.13-0.15% of V, smaller than or equal to 0.005% of S, smaller than or equal to0.01% of P, and the balance iron and inevitable impurities. The invention further discloses a myriameter drilling machine hanging ring prepared from the low-carbon martensitic steel, the diameter canreach 180 mm, and the use requirement of the myriameter drilling machine hanging ring is met. The invention further discloses a preparation method of the myriameter drilling machine hanging ring, thecost is low, and the manufacturing period is short.

Description

technical field [0001] The invention belongs to the field of petroleum equipment manufacturing, and in particular relates to a low-carbon martensitic steel, a 10,000-meter drilling rig suspension ring and a preparation method thereof. Background technique [0002] The lifting ring is an important lifting component of the oil drilling rig. It is a solid bar forging and mainly bears tensile load and fatigue load. With the development of ultra-deep oil and gas drilling and the application of 10,000-meter drilling rigs, the requirements for the lifting capacity of the lifting ring are getting higher and higher, and the diameter of the lifting ring is getting larger and larger. In order to ensure the overall service safety of the lifting ring, it is required that its entire section have consistent mechanical properties. Especially the material at the center has high strength and toughness, which requires the steel for the ring to have sufficient hardenability and toughness. At p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/46C21D1/18C21D1/26C21D6/00C21D8/06C21D9/40C21D9/52E21B19/02
CPCC22C38/02C22C38/04C22C38/44C22C38/46C22C38/002C21D1/26C21D6/004C21D6/005C21D6/008C21D8/065C21D9/525C21D9/40C21D1/18E21B19/02C21D2211/008
Inventor 李方坡
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com