Preparation method and application of viscose-based zinc ion antibacterial fibers

An antibacterial fiber and zinc ion technology, applied in the field of fabric fiber preparation, can solve the problem that the antibacterial effect is difficult to last, and achieve the effects of widening the market, obvious antibacterial effect, and saving production costs.

Pending Publication Date: 2020-10-16
SHANGHAI SHUIXING HOME TEXTILE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention patent application with the application number 201710845409.7 discloses a Raschel composite carpet, which is prepared by a dry spinning process, and a small amount of zinc ion antibacterial agent is added to its components. Due to the limitation of the process method, such The antibacterial effect of the product is difficult to last

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] A kind of preparation method of viscose base zinc ion antibacterial fiber of the present invention comprises the following steps:

[0015] (1) Weigh 5~10g of dispersant with a concentration of 10g / L and add it to 18~21g of ZnSO 4 ·7H 2 O, 200~220g of Na 2 SO 4 and 110~120g of concentrated H 2 SO 4 The volume of the mixed composition is 1~2L in an acid bath, stir evenly to obtain a mixed spinning solution; the dispersant is mixed in HB-sy100, BYK-171, TiO 2 , SHMP, or spin-653 in any one.

[0016] (2) Oxidation-reduction reaction in coagulation bath: add 18-21g of ZnSO after 2-3 hours of reaction 4 ·7H 2 O. When the as-spun yarn starts to be stretched, raise the temperature of the coagulation bath to 60-65°C, then add a rotating rod to stir at 120-150r / min to accelerate the reaction, and gradually obtain the antibacterial finished fiber.

[0017] The combination of zinc ions and viscose fibers is mainly completed in the solution, and its essence is an oxidation-r...

Embodiment 1

[0022] The preparation method of the present embodiment viscose-based zinc ion antibacterial fiber, comprises the steps:

[0023] (1) Weigh 5g of dispersant with a concentration of 10g / L and add it to 18g of ZnSO 4 ·7H 2 O, 200g of Na 2 SO 4 and 110 g of concentrated H 2 SO 4 The volume of the mixed composition is 1L in an acid bath, and stirred evenly to obtain a mixed spinning solution; the dispersant is HB-sy100.

[0024] (2) Redox reaction in coagulation bath: add 18g of ZnSO after 2h of reaction 4 ·7H 2 O. When the as-spun yarn starts to be stretched, raise the temperature of the coagulation bath to 60°C, then add a rotating bar to stir and accelerate the reaction at 120r / min, and gradually obtain the antibacterial finished fiber.

[0025] Prepare the antibacterial quilt with the antibacterial finished fiber obtained in step (2): According to the mass ratio, 30% of the antibacterial finished fiber and 70% of the polyester fiber are opened and mixed, and passed thro...

Embodiment 2

[0028] (1) Weigh 6g of dispersant with a concentration of 10g / L and add it to 19g of ZnSO 4 ·7H 2 O, 200~220g of Na 2 SO 4 and 115 g of concentrated H 2 SO 4 The volume of the mixed composition is in an acid bath of 1.5L, and stirred evenly to obtain a mixed spinning solution; the dispersant is TiO 2 .

[0029] (2) Redox reaction in coagulation bath: add 19g of ZnSO after 2.5h of reaction 4 ·7H 2 O. When the as-spun yarn starts to be stretched, increase the temperature of the coagulation bath to 63°C, and then add a rotating rod at 140r / min for stirring to accelerate the reaction, and gradually obtain the antibacterial finished fiber.

[0030] Prepare the antibacterial quilt with the antibacterial finished fiber obtained in step (2): According to the mass ratio, 35% of the antibacterial finished fiber and 65% of the polyester fiber are opened and mixed, and passed through the nozzle at the entrance before heat setting, with 5Kg / cm 2 Spray the white latex glue with a so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method and application of viscose-based zinc ion antibacterial fibers. The preparation method disclosed by the invention comprises the following steps of: (1) weighing 5-10 g of a dispersing agent with the concentration of 10 g / L, adding the dispersing agent into an acid bath with the volume of 1-2 L, which is formed by mixing 18-21 g of ZnSO4.7H2O, 200-220 gof Na2SO4 and 110-120 g of concentrated H2SO4, and uniformly stirring to obtain a mixed spinning solution; and (2) carrying out oxidation-reduction reaction in a coagulating bath, namely adding 18-21g of ZnSO4.7H2O again after the reaction is carried out for 2-3 hours, heating the coagulating bath to 60-65 DEG C when the nascent filament starts to be stretched, adding a rotating rod, and carryingout stirring acceleration reaction at 120-150r / min to gradually obtain the antibacterial finished fibers.

Description

technical field [0001] The invention relates to a preparation method of fabric fibers, in particular discloses a preparation method of viscose-based zinc ion antibacterial fibers. Background technique [0002] Nowadays, people's education level is generally high, and they have extensive and unique cognition and requirements for various products. Home textiles occupy a large area of ​​textiles. Products, etc. are essential elements to create a warm home style. Not only do they have practical value, but products with multiple functions will have broad development space and will better meet the needs of consumers. At present, antibacterial, deodorant, and aromatic home textiles have been continuously appearing in home textile expos and home textile markets of different brands, and are gradually integrated into consumers' consumption concepts. [0003] Viscose fiber is now widely used regenerated cellulose fiber, mainly by extracting pure fiber from cellulose raw materials that...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08D04H1/655D04H1/587D04H1/4382D02G3/44D03D15/00D03D13/00
CPCD01F2/08D04H1/655D04H1/587D04H1/4382D02G3/449D03D15/00D03D13/008D10B2201/24D10B2401/13D10B2503/06
Inventor 陈秀苗武亚琼
Owner SHANGHAI SHUIXING HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com