A kind of graphene/alkane composite coating for aluminum alloy strip and preparation method thereof

A technology of aluminum alloy strip and composite coating, applied in coating, anti-corrosion coating, device for coating liquid on the surface, etc., can solve the problems of poor corrosion resistance and environmental protection of conversion coating, and achieve high coating The effect of binding force, high hydrophobicity, high abrasion resistance

Active Publication Date: 2021-11-05
CHINALCO RUIMIN +1
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional chemical conversion of hexavalent chromium is not environmentally friendly and basically cannot be used; phosphating treatment requires a large amount of raw materials such as acid and alkali, and there are problems in the treatment and discharge of waste liquid phosphorus, and the corrosion resistance of the conversion coating is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene/alkane composite coating for aluminum alloy strip and preparation method thereof
  • A kind of graphene/alkane composite coating for aluminum alloy strip and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of preparation method of graphene / alkane composite coating for aluminum alloy strip comprises the following steps:

[0037] (1) Surface pretreatment: The aluminum alloy plate with a width of 50 cm is subjected to alkali washing, degreasing, and hot air drying.

[0038] (2) Coating preparation: add graphene with a surface oxygen / carbon ratio of 1:30 to n-dodecane and n-tridecane (mass ratio 2:1), stir mechanically for 30 minutes, and then place it under low-temperature circulating water conditions for ultrasonication Disperse for 30 minutes, keep the temperature of the coating at 35°C to 45°C, prepare graphene dispersion A; add N-β-(aminoethyl)-γaminopropyltrimethoxysilane coupling agent to graphene dispersion under stirring In liquid A, continue mechanical stirring and aging for 12 hours to prepare graphene dispersion B; add graphene dispersion B to n-dodecane and n-tridecane, and mechanically stir for 30 minutes to prepare a coating. Graphene accounts for 0.01%...

Embodiment 2～5

[0041] Examples 2-5: Different from Example 1, the surface oxygen / carbon ratios of graphene (according to the examples) are 1:15, 1:10, 1:5, 1:1.

Embodiment 6-8

[0042] Embodiment 6-8: Different from Embodiment 1, the coupling agent (according to the embodiment) is γ-aminopropylmethyldiethoxysilane, anilinomethyltriethoxysilane, diethylamino Substituted methyltriethoxysilane and aminopropyltriethoxysilane, the mass ratio is 1:2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of coating materials for aluminum alloy plates, and in particular relates to a graphene / alkane composite coating for aluminum alloy plates and strips. The coating of the coating contains at least alkane or cycloalkane, graphene and its derivatives, and a silane coupling agent; the coating of the present invention has technological characteristics such as environmental protection, low cost, simple process, and continuous production, and has high corrosion resistance Excellent properties such as high wear resistance, hydrophobicity, high coating adhesion, low surface resistivity, long service life, etc., suitable for surface treatment of aluminum alloys to meet the storage process of aluminum alloy materials, subsequent welding, coating, etc. need.

Description

technical field [0001] The invention belongs to the technical field of coating materials for aluminum alloy plates, and in particular relates to a graphene / alkane composite coating for aluminum alloy plates and strips. Background technique [0002] Aluminum alloy has the advantages of good mechanical properties, light weight, and corrosion resistance, and has been widely used in various industries, especially in aerospace, marine ships, new energy vehicles, and high-end sports cars that require high lightweight. Aluminum alloys will inevitably corrode during storage and use, and aluminum alloy sheets need to be bonded, painted and other processing procedures during the application process. Therefore, the surface treatment technology of aluminum alloys is one of the important factors affecting their use. [0003] Aluminum alloys are generally surface treated by chemical conversion, anodic oxidation, coating and other methods, and as a primer, chemical conversion is preferred,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D5/08C09D7/63B05D7/16B05D3/02
CPCB05D3/0209B05D3/0254B05D7/16C09D1/00C09D5/08C09D7/63
Inventor 黄瑞银张易宁林俊鸿陈素晶吴建新林梅钦
Owner CHINALCO RUIMIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com