Titanium fiber toughening cold heading die and preparation method thereof

A titanium fiber and cold heading technology is applied in the field of titanium fiber toughening cold heading mold and its preparation, which can solve the problem of high cost, improve the bonding force and interface structure, easily meet the process conditions, and achieve the effects of high production efficiency.

Active Publication Date: 2020-11-06
XIAN UNIV OF TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] An object of the present invention is to provide a titanium fiber toughened cold heading die, which solves the problem that the existing cold heading die needs to use rare metals and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium fiber toughening cold heading die and preparation method thereof
  • Titanium fiber toughening cold heading die and preparation method thereof
  • Titanium fiber toughening cold heading die and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] A kind of preparation method of titanium fiber toughening cold heading die of the present invention comprises the following steps:

[0035] Step 1, weigh the following components according to mass percentage, WC powder 70%-85%, Fe powder 5%-15%, Ti fiber 10%-20% and graphite powder 1%-3%, the above components The sum of the mass percentages is 100%; the particle size of the WC powder is 3 μm-10 μm, the particle size of the Fe powder is 8 μm-12 μm, and the diameter of the Ti fiber is 200 μm-1000 μm.

[0036]In step 2, use a ball mill to uniformly mix the WC powder, Fe powder and graphite powder weighed in step 1 to form a mixed powder. During the mixing process, the speed of the ball mill is 80-120r / min, and the ball milling time is 2h-10h. Add the mixed powder and binder into the kneader, the speed of the kneader is 30-50r / min, heat the solid mixed powder in the kneader, the heating temperature is 130°C-150°C, and the binder Wet the powder after heating and melting, an...

Embodiment 1

[0042] Prepare a kind of WC volume fraction and be the titanium fiber toughened cold heading die of 45%, comprise the following steps:

[0043] Step 1, weigh the following components according to mass percentage, WC powder 70.9%, Fe powder 7.9%, Ti fiber 19.3% and graphite powder 1.9%, the sum of the mass percentages of the above components is 100%; wherein, WC powder The particle size of Fe powder is about 8 μm, and the particle size of Fe powder is about 10 μm.

[0044] Step 2, use a ball mill to mix the WC powder, Fe powder and graphite powder weighed in step 1 evenly to form a mixed powder. During the mixing process, the ratio of grinding balls to powder is 2:1, and the ball mill speed is 120r / min. The time is 6h.

[0045] Add the mixed powder and binder into the kneader, start the kneader at a speed of 50r / min, heat the solid mixed powder in the kneader at a heating temperature of 140°C, and wait until the binder is heated Wet the powder after melting and fully wrap it ...

Embodiment 2

[0052] Prepare a kind of WC volume fraction and be that the titanium fiber toughening cold heading die of 47%, comprises the following steps:

[0053] Step 1, take the following components according to mass percentage, WC powder 72.2%, Fe powder 8.4%, Ti fiber 17.5% and graphite powder 1.9%, the sum of the mass percentages of the above components is 100%; wherein, WC powder The particle size of Fe powder is about 8 μm, and the particle size of Fe powder is about 10 μm.

[0054] Step 2, use a ball mill to mix the WC powder, Fe powder and graphite powder weighed in step 1 evenly to form a mixed powder. During the mixing process, the ratio of grinding balls to powder is 2:1, and the ball mill speed is 80r / min. The time is 4h.

[0055] Add the mixed powder and binder into the kneader, start the kneader at a speed of 40r / min, heat the solid mixed powder in the kneader at a heating temperature of 140°C, and wait until the binder is heated Wet the powder after melting and fully wra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a titanium fiber toughening cold heading die. The cold heading die internally comprises a Ti fiber net-shaped framework, wherein Ti fibers forming the Ti fiber net-shaped framework are covered with a TiC layer; the TiC layer is formed by stacking submicron-order TiC particles; micron-order WC particles and Fe binding phases are dispersed and distributed between the Ti fibernet-shaped framework; and the Ti fiber net-shaped framework is formed by connecting a plurality of transverse Ti fibers and longitudinal Ti fibers, the transverse Ti fibers are spiral fibers, and thetransverse Ti fibers are connected with the longitudinal Ti fibers from inside to outside. The invention further discloses a preparation method of the titanium fiber toughening cold heading die. Thetitanium fiber toughening cold heading die prepared through the method does not contain rare metal, and is low in manufacturing cost, high in toughness and wide in application range.

Description

technical field [0001] The invention belongs to the technical field of cold heading dies, and relates to a titanium fiber toughened cold heading die and a preparation method thereof. Background technique [0002] As an important part of the cold heading machine, the cold heading die is often used for cold heading, cold punching and upsetting of metal materials. During the cold heading deformation process, it must bear a large unit pressure and severe impact load. The cold heading mold is required to be both It has good impact toughness and certain wear resistance. [0003] Cemented carbide has the characteristics of high hardness and high strength. It is an ideal material for cold heading dies and is widely used. At present, in order to improve the toughness of cold heading dies, high-cobalt (Co%≈20%) cemented carbides are generally used. However, its inherent low bending strength, poor toughness and other problems lead to a decline in performance. On the one hand, the co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C49/02C22C49/14C22C47/12C22C47/06B22F5/00B22F3/22B22F3/10B21J13/02C22C111/02
CPCB21J13/02B22F3/1007B22F3/1021B22F3/1039B22F3/225B22F5/007C22C47/06C22C47/12C22C49/02C22C49/14
Inventor 钟黎声崔鹏杰卢正欣梁淑华邹军涛朱建雷白海强
Owner XIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com