A kind of preparation method of high-purity manganese sulfate

A manganese sulfate, high-purity technology, applied in the direction of manganese sulfate, etc., can solve problems such as complex process flow, high production cost of high-purity manganese sulfate, and affecting the stability of lithium batteries

Active Publication Date: 2021-06-29
TSINGHUA UNIV
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of these processes is that it is difficult to meet the requirements for manganese fluoride to remove calcium and magnesium, and the introduction of fluoride ions
Because the existence of fluoride ions will affect the stability of lithium batteries, it is necessary to use activated alumina to absorb and remove fluorine before evaporation and concentration, the process is complicated and the operating cost is increased.
Various unfavorable factors lead to the high production cost of high-purity manganese sulfate at present, and the preparation process is relatively complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high-purity manganese sulfate
  • A kind of preparation method of high-purity manganese sulfate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] The invention provides a kind of preparation method of high-purity manganese sulfate, comprises the following steps:

[0020] (1) removing heavy metal ions in the thick manganese salt solution to obtain a liquid phase product;

[0021] (2) Mix the liquid-phase product and bicarbonate to carry out precipitation of calcium, magnesium and manganese ions, and carry out solid-liquid separation after the concentration of manganese ions in the system≤0.2g / L to obtain crude manganese carbonate solid; the calcium, magnesium and manganese ions The pH value of the system during the precipitation process is ≤8.6;

[0022] (3) After the thick manganese carbonate solid is dispersed in water, carbon dioxide is introduced into the dispersion, and the refined manganese carbonate solid is obtained after solid-liquid separation;

[0023] (4) Wash the refined manganese carbonate solid and dissolve it in dilute sulfuric acid, then concentrate and crystallize to obtain high-purity manganese...

Embodiment 1

[0037] With feed grade manganese sulfate (Ca, Mg concentration is respectively 135ppm and 406ppm) as raw material, the concentration of each impurity in feed grade manganese sulfate is shown in Table 1.

[0038] Table 1. Concentration of each impurity element in feed grade manganese sulfate

[0039] Impurity elements calcium magnesium cobalt chromium copper iron Potassium sodium nickel lead silicon cadmium zinc Concentration (ppm) 1337 4058 326 32 0.0 269 8 585 617 43 155 3 2569

[0040] Dissolve 5 kg of feed grade manganese sulfate in 10 L of water, add solid sodium bicarbonate to adjust the pH of the solution to 5, and let it stand for 24 hours. Then restart stirring, add 100 grams of formane, stir for 2h, then filter. The filtrate is transferred to another 20L plastic barrel, and a sufficient amount of sodium bicarbonate solid (total amount is 2.8kg) is added under constant stirring condition, and the pH value of the...

Embodiment 2

[0046] Take 5L of manganese sulfate feed solution from Guizhou Neng Mine (see Table 3 for the concentration of impurity elements, and the concentration of manganese sulfate is 368g / L), add solid sodium bicarbonate under constant stirring, adjust the pH value of the solution to 7, let stand for 24h, filter . The filtrate was transferred to another 10L container, and 120g of sodium forma solid was added under continuous stirring, and after stirring for 2 hours, it was left to stand for 24 hours and filtered. Under constant stirring condition, add sodium bicarbonate solid (total addition is 1450g) in filtrate, the pH value of solution is controlled to below 8.6 with the mode of the sodium hydroxide solution of 100g / L. Wait for the manganese ion concentration in the solution to be less than 0.2g / L, leave standstill, treat that after most of the manganese carbonate precipitation settles to the bottom of the container, dump and discard the last clear liquid, filter, and collect the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of positive electrode materials for lithium batteries, and provides a method for preparing high-purity manganese sulfate. Firstly, heavy metal ions in a crude manganese salt solution are removed, and then the obtained liquid phase product is mixed with bicarbonate for calcium, magnesium, and manganese ionization. Precipitate to obtain crude manganese carbonate solid; then disperse the crude manganese carbonate solid in water and pass carbon dioxide into the dispersion to obtain refined manganese carbonate solid; dissolve the refined manganese carbonate solid in dilute sulfuric acid and concentrate and crystallize to obtain high-purity sulfuric acid manganese. The present invention converts the manganese salt into manganese carbonate by controlling the reaction conditions, and converts the calcium carbonate and magnesium carbonate accompanied by manganese carbonate precipitation into soluble bicarbonate by introducing carbon dioxide, thereby realizing the removal of calcium and magnesium ions, and then returning Dissolution and crystallization can easily obtain high-purity manganese sulfate. The method provided by the invention has simple steps and low cost, and the content of impurity ions in the obtained high-purity manganese sulfate is extremely low.

Description

technical field [0001] The invention relates to the technical field of lithium battery cathode materials, in particular to a preparation method of high-purity manganese sulfate. Background technique [0002] High-purity manganese sulfate, also known as battery-grade manganese sulfate, is one of the raw materials required for the production of ternary lithium batteries. In order to ensure the quality of lithium batteries, the purity requirements for manganese sulfate are very high. For example, the requirements for calcium and magnesium are not more than 50ppm, the concentration of other impurity metals (iron, lead, zinc, copper, etc.) shall not exceed 10ppm. The existing production process of high-purity manganese sulfate generally uses manganese fluoride to remove calcium and magnesium, sodium sulfide or sodium thiomer to remove heavy metals, and then evaporates and concentrates to obtain high-purity manganese sulfate products. The disadvantage of these processes is that i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G45/10
CPCC01G45/10
Inventor 王毅李亚贾美然王邦达
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com