Production process of asphalt waste plastic synthetic floor tiles

A production process and plastic technology, applied in plastic recycling, household components, applications, etc., can solve the problems of difficult decomposition of plastic waste, large production and use, affecting the ecological environment, etc., achieve fast production speed, solve difficult processing, improve water permeability effect

Inactive Publication Date: 2020-12-01
刘云山
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing floor tiles are made of clay, which consumes a lot of clay. Extensive mining of clay will cause great damage to cultivated land and forest land, and affect the ecological environment.
Moreover, the existing floor tiles have poor water permeability, and it is difficult for rainwater to quickly flow into the ground. When used on sidewalks, floor tiles with permeable holes need to be specially laid.
[0003] At present, the production and use of plastic products in my country is large, and a large amount of plastic waste is produced every day, and plastic waste is difficult to decompose, and pollutes the environment after being discarded.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of production technology of asphalt waste plastic synthetic floor tile, comprises the following steps:

[0022] a. Collect the waste plastics and classify them according to the color, and then put the plastics of different colors into the shredder and crush them into renewable plastic particles for later use. The diameter of the crushed plastic particles is 5mm;

[0023] b. In parts by volume, add 20 parts of asphalt and 80 parts of plastic granules in proportion to a mixer with a heating device. The heating temperature is 180°C. During the stirring process, it is heated to make it evenly mixed, and the stirring time is 30-50 minutes;

[0024] c. Inject the mixed solution obtained in step b into a molding die to form a blank;

[0025] d. After the blank is cooled to room temperature, the corners and the surface are polished, and the burr is removed to obtain the finished floor tile.

[0026] Further, in the step b, 0.5%-2% anti-aging agent is added to the raw ma...

Embodiment 2

[0029] A kind of production technology of asphalt waste plastic synthetic floor tile, comprises the following steps:

[0030] a. Collect the waste plastics and classify them according to the color, and then put the plastics of different colors into the shredder and crush them into renewable plastic particles for later use. The diameter of the crushed plastic particles is 3mm;

[0031] b. In parts by volume, add 10 parts of asphalt and 90 parts of plastic granules in proportion to a mixer with a heating device. The heating temperature is 160 ° C. During the stirring process, it is heated to make it evenly mixed, and the stirring time is 30-50 minutes;

[0032] c. Inject the mixed solution obtained in step b into a molding die to form a blank;

[0033] d. After the blank is cooled to room temperature, the corners and the surface are polished, and the burr is removed to obtain the finished floor tile.

[0034] Further, in the step b, 0.5%-2% anti-aging agent is added to the raw ...

Embodiment 3

[0037] A kind of production technology of asphalt waste plastic synthetic floor tile, comprises the following steps:

[0038] a. Collect the waste plastics and classify them according to the color, and then put the plastics of different colors into the shredder and crush them into renewable plastic particles for later use. The diameter of the crushed plastic particles is 5mm;

[0039] b. In parts by volume, add 15 parts of asphalt and 85 parts of plastic granules in proportion to a mixer with a heating device. The heating temperature is 170 ° C. During the stirring process, it is heated to make it evenly mixed, and the stirring time is 30-50 minutes;

[0040] c. Inject the mixed solution obtained in step b into a molding die to form a blank;

[0041] d. After the billet is cooled to room temperature, the corners and the surface are polished, and the burr is removed to obtain the finished floor tile.

[0042] Further, in the step b, 0.5%-2% anti-aging agent is added to the raw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a production process of asphalt waste plastic synthetic floor tiles. The production process comprises the steps of: 1, collecting waste plastics, classifying the waste plasticsaccording to colors, putting the plastics with different colors into a crusher, and crushing into renewable plastic particles for later use; 2, adding asphalt and the plastic particles into a stirrerwith a heating device in proportion, heating in the stirring process to uniformly mix the asphalt and the plastic particles, and stirring for not less than 30 minutes; 3, injecting a mixed solution obtained in the step 2 into forming molds for forming to obtain blanks; and 4, cooling the blanks to a room temperature, polishing edges and corners and surfaces, and removing burrs to obtain finishedfloor tiles. The production process of the asphalt waste plastic synthetic floor tiles has the beneficial effects that waste plastic can be reused, and the problem that plastic garbage is difficult totreat is solved; plastic and asphalt are mixed, the weight is light, the strength is high, the asphalt permeability is good, and the permeability of the bricks is improved; and the production processis low in cost, simple and convenient in manufacturing process, low in energy consumption, high in production speed, and high in yield.

Description

technical field [0001] The invention relates to the technical field of brick making, in particular to a production process of asphalt waste plastic synthetic floor bricks. Background technique [0002] In the infrastructure construction of urban residential quarters, a large number of outdoor floor tiles are required. Outdoor floor tiles have the outstanding characteristics of large quantities and wide application ranges. However, most of the existing floor tiles are made of clay, which needs to consume a large amount of clay, and a large amount of mining of the clay will cause great damage to cultivated land and woodland, and affect the ecological environment. Moreover, the existing floor tiles have poor water permeability, and it is difficult for rainwater to quickly flow into the ground. When used on sidewalks, floor tiles with permeable holes need to be specially laid. [0003] At present, the production and use of plastic products in my country is large, and a large am...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C45/00B29B17/02B29K95/00B29L31/10
CPCB29B17/02B29B2017/0203B29C45/0001B29K2095/00B29L2031/102Y02W30/62
Inventor 刘云山
Owner 刘云山
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products