A kind of toughening agent, PVC pipe material and preparation method thereof

A PVC pipe and toughening agent technology, applied in the field of toughening agent, PVC pipe material and its preparation, can solve the problems of brittle cracking, poor low-temperature impact resistance, etc.

Active Publication Date: 2022-04-26
HEFEI GENIUS NEW MATERIALS
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the present invention provides a toughening agent, which is formed by uniformly mixing low-density polyethylene 70%-80% and nitrile rubber 20%-30%, which is applied in PVC pipe materials, It can significantly improve the low-temperature impact resistance of PVC pipe materials, and solve the problems that the existing PVC pipes are easy to be brittle in winter and have poor low-temperature impact resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of toughening agent, PVC pipe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] According to parts by weight, 100 parts of polyvinyl chloride, 10 parts of acrylonitrile-butadiene-styrene copolymer, 5 parts of maleic anhydride grafted polyethylene, toughening agent (mass ratio is 3:1 low density polyethylene and nitrile rubber) 10 parts, 1 part of chlorinated polyethylene, 0.5 part of antioxidant 1098, 0.5 part of antioxidant 168, 1 part of zinc stearate was placed in the mixer at room temperature and mixed for 1 minute, and the mixing speed was 150 rpm / minute. Add the mixed raw materials into a twin-screw extruder, melt and extrude and granulate to obtain a PVC pipe material, wherein the temperature of the first zone of the twin-screw extruder is 160°C, and the temperature of the second zone is 170°C , the temperature of the third zone is 180°C, the temperature of the fourth zone is 210°C, the temperature of the fifth zone is 210°C, the temperature of the sixth zone is 210°C, and the speed is 300rpm.

Embodiment 2

[0029] According to parts by weight, 100 parts of polyvinyl chloride, 20 parts of acrylonitrile-butadiene-styrene copolymer, 6 parts of maleic anhydride grafted polyethylene, toughening agent (mass ratio is 3:1 low density polyethylene and nitrile rubber) 12 parts, 5 parts of chlorinated polyethylene, 2 parts of antioxidant 1098, 2 parts of antioxidant 168, 5 parts of zinc stearate were placed in mixer and mixed at room temperature for 2 minutes, mixing speed 180 rpm minute. Add the mixed raw materials into the twin-screw extruder, melt and extrude and granulate to obtain PVC pipe material, wherein the temperature of the first zone of the twin-screw extruder is 170°C, and the temperature of the second zone is 180°C , the temperature of the third zone is 200°C, the temperature of the fourth zone is 220°C, the temperature of the fifth zone is 220°C, the temperature of the sixth zone is 220°C, and the speed is 500rpm.

Embodiment 3

[0031] 100 parts by weight of polyvinyl chloride, 12 parts of acrylonitrile-butadiene-styrene copolymer, 8 parts of maleic anhydride grafted polyethylene, toughening agent (mass ratio is 3:1 low density polyethylene and 14 parts of nitrile rubber), 3 parts of chlorinated polyethylene, 1 part of antioxidant 1098, 2 parts of antioxidant 168, and 3 parts of zinc stearate were placed in a mixer at room temperature and mixed for 2 minutes at a mixing speed of 170 rpm . Add the mixed raw materials into a twin-screw extruder, melt and extrude and granulate to obtain PVC pipe material, wherein the temperature of the first zone of the twin-screw extruder is 170°C, and the temperature of the second zone is 190°C , the temperature of the third zone is 180°C, the temperature of the fourth zone is 210°C, the temperature of the fifth zone is 220°C, the temperature of the sixth zone is 220°C, and the speed is 500rpm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a toughening agent, a PVC pipe material and a preparation method thereof, which are prepared by uniformly mixing the following components in mass ratio: 70%-80% of low-density polyethylene, 20%-30% of nitrile rubber . In the present invention, by compounding low-density polyethylene and nitrile rubber and optimizing the mixing ratio, a toughening agent with excellent performance is obtained, which is very suitable for PVC pipe materials and can significantly improve the low-temperature impact resistance of PVC pipe materials .

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a toughening agent, a PVC pipe material and a preparation method thereof. Background technique [0002] Polyvinyl chloride plastic is polymerized from vinyl chloride monomer and is one of the most commonly used thermoplastics. Its trade name is called "chlorine plastic" for short, and its English abbreviation is PVC. Pure polyvinyl chloride resin is a hard thermoplastic substance, its decomposition temperature is very close to the plasticizing temperature, and its mechanical strength is poor. Therefore, polyvinyl chloride resin cannot be used to mold products, and plasticizers, stabilizers, fillers, etc. must be added to improve performance to make polyvinyl chloride plastics, and then processed into various products. Polyvinyl chloride can be divided into rigid polyvinyl chloride and soft polyvinyl chloride according to the amount of plasticizer added. [0003] PV...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L9/02C08L27/06C08L55/02C08L51/06C08L23/28C08K5/20C08K5/526C08K5/098
CPCC08L23/06C08L27/06C08L2205/035C08L2205/02C08L2203/18C08L9/02C08L55/02C08L51/06C08L23/286C08K5/20C08K5/526C08K5/098
Inventor 杨桂生方永炜梁娜邵灵芝王华宋伟华
Owner HEFEI GENIUS NEW MATERIALS